The low efficiency of oxygen evolution reaction(OER) is regarded as one of the major roadblocks for metal-air batteries and water electrolysis.Herein,a high-performance OER catalyst of NiFe_(0.2)(oxy)hydroxide(NiFe_(0...The low efficiency of oxygen evolution reaction(OER) is regarded as one of the major roadblocks for metal-air batteries and water electrolysis.Herein,a high-performance OER catalyst of NiFe_(0.2)(oxy)hydroxide(NiFe_(0.2)-O_(x)H_(y)) was developed through topotactic transformation of a Prussian blue analogue in an alkaline solution,which exhibits a low overpotential of only 263 mV to reach a current density of 10 mA cm^(-2) and a small Tafel slope of 35 mV dec-1.Ex-situ/operando Raman spectroscopy results indicated that the phase structure of NiFe_(0.2)-O_(x)H_(y) was irreversibly transformed from the type of α-Ni(OH)_(2) to γ-NiOOH with applying an anodic potential,while ex-situ/operando 57Fe Mossbauer spectroscopic studies evidenced the in-situ production of abundant high-valent iron species under OER conditions,which effectively promoted the OER catalysis.Our work elucidates that the amount of high-valent iron species in-situ produced in the NiFe(oxy)hydroxide has a positive correlation with its water oxidation reaction performance,which further deepens the understanding of the mechanism of NiFe-based electrocatalysts.展开更多
基金financially supported by the National Natural Science Foundation of China(21476232,21961142006)the International Partnership Program of Chinese Academy of Sciences(121421KYSB20170020)the State Key Laboratory of Catalysis in Dalian Institute of Chemical Physics(N-16-07)。
文摘The low efficiency of oxygen evolution reaction(OER) is regarded as one of the major roadblocks for metal-air batteries and water electrolysis.Herein,a high-performance OER catalyst of NiFe_(0.2)(oxy)hydroxide(NiFe_(0.2)-O_(x)H_(y)) was developed through topotactic transformation of a Prussian blue analogue in an alkaline solution,which exhibits a low overpotential of only 263 mV to reach a current density of 10 mA cm^(-2) and a small Tafel slope of 35 mV dec-1.Ex-situ/operando Raman spectroscopy results indicated that the phase structure of NiFe_(0.2)-O_(x)H_(y) was irreversibly transformed from the type of α-Ni(OH)_(2) to γ-NiOOH with applying an anodic potential,while ex-situ/operando 57Fe Mossbauer spectroscopic studies evidenced the in-situ production of abundant high-valent iron species under OER conditions,which effectively promoted the OER catalysis.Our work elucidates that the amount of high-valent iron species in-situ produced in the NiFe(oxy)hydroxide has a positive correlation with its water oxidation reaction performance,which further deepens the understanding of the mechanism of NiFe-based electrocatalysts.