Recycled ceramic mixed sand(RCMS) was obtained by partially replacing ultra-fine sand with recycled ceramic coarse sand(RCCS). The effects of RCCS replacement rate on the apparent density, workability, compressive...Recycled ceramic mixed sand(RCMS) was obtained by partially replacing ultra-fine sand with recycled ceramic coarse sand(RCCS). The effects of RCCS replacement rate on the apparent density, workability, compressive strength and splitting tensile strength of recycled ceramic concrete(RCC) were investigated. In addition, the relationship between the water-cement ratio and compressive strength of RCC was also studied. The experimental results indicate that the reusing of recycled ceramic aggregate can improve the cohesiveness and water retentiveness of fresh concrete and benefit the mechanical properties development. When the RCCS replacement rate is not less than 40%, the mechanical properties of RCC are superior to those of the reference concrete. Moreover, when recycled ceramic medium sand was completely used as fine aggregate, the maximum increase in both compressive strength and splitting tensile strength were obtained, comparing with those of reference concrete, the increment ratio was 19.85% and 32.73%, respectively. The microscopic analysis shows that the using of recycled ceramic aggregate can meliorate distinctly the structure of the interfacial transition zone(ITZ) and increase the compaction degree of cement paste. Furthermore, an expression of the compressive strength of RCC and the cement-water ratio is regressed and gains a good linear relativity. It is an effective way to recycle waste ceramic, and the consumption of recycled ceramic aggregate could reach from 26.9% to 47.6% of the total weight of aggregate in producing concrete.展开更多
The influence of silica fume, slag and fly ash on alkali-silica reaction under the condition of 70 ℃ is studied. The results show that silica, slag and fly ash may inhibit alkali-silica reaction only under suitable c...The influence of silica fume, slag and fly ash on alkali-silica reaction under the condition of 70 ℃ is studied. The results show that silica, slag and fly ash may inhibit alkali-silica reaction only under suitable content. When the content is less than 10%, silica fume does not markedly influence the expansion of alkali- silica reaction. When the content is 15%-20%, silica fume only may delay the expansion of alkali-silica reaction. When the content is 30%-70%, slag may only delay the expansion of alkali-silica reaction, but cannot inhibit the expansion of alkali-silica reaction. When the content is 10%, fly ash does not markedly influence the expansion of alkali-silica reaction. When the content is 20%-30%, fly ash may only delay the expansion of alkali-silica reaction, but cannot inhibit the expansion of alkali-silica reaction. When the content is over 50%, it is possible that fly ash can inhibit effectively alkali-silica reaction.展开更多
On the base of the influence rule of silica fume, slag and fly ash on alkali-silica reaction under the condition of 70 ℃, the mechanism of the effect of mineral admixtures on alkali-silica reaction is studied further...On the base of the influence rule of silica fume, slag and fly ash on alkali-silica reaction under the condition of 70 ℃, the mechanism of the effect of mineral admixtures on alkali-silica reaction is studied further in the paper. The results show that the effects of mineral admixtures on alkali-silica reaction are mainly chemistry effect and surface physichemistry effect. Under suitable condition, the chemistry effect may make alkali-silica reaction to be inhibited effectively, but the physichemistry effect only make alkali-silica reaction to be delayed. The chemistry effect and the physichemistry effect of minerals admixture are relative to the content of Ca(OH)2 in system. Under the condition that there is a large quantity of Ca(OH)2, mineral admixture cannot inhibit alkali-silica reaction effectively. Only when Ca(OH)2 in the system is very less, it is possible that mineral admixture inhibits alkali-silica reaction effectively.展开更多
基金Funded by the National Natural Science Foundation of China(No.50902107)the Fundamental Research Funds for the Central Universities(No.2013-YB-25)
文摘Recycled ceramic mixed sand(RCMS) was obtained by partially replacing ultra-fine sand with recycled ceramic coarse sand(RCCS). The effects of RCCS replacement rate on the apparent density, workability, compressive strength and splitting tensile strength of recycled ceramic concrete(RCC) were investigated. In addition, the relationship between the water-cement ratio and compressive strength of RCC was also studied. The experimental results indicate that the reusing of recycled ceramic aggregate can improve the cohesiveness and water retentiveness of fresh concrete and benefit the mechanical properties development. When the RCCS replacement rate is not less than 40%, the mechanical properties of RCC are superior to those of the reference concrete. Moreover, when recycled ceramic medium sand was completely used as fine aggregate, the maximum increase in both compressive strength and splitting tensile strength were obtained, comparing with those of reference concrete, the increment ratio was 19.85% and 32.73%, respectively. The microscopic analysis shows that the using of recycled ceramic aggregate can meliorate distinctly the structure of the interfacial transition zone(ITZ) and increase the compaction degree of cement paste. Furthermore, an expression of the compressive strength of RCC and the cement-water ratio is regressed and gains a good linear relativity. It is an effective way to recycle waste ceramic, and the consumption of recycled ceramic aggregate could reach from 26.9% to 47.6% of the total weight of aggregate in producing concrete.
文摘The influence of silica fume, slag and fly ash on alkali-silica reaction under the condition of 70 ℃ is studied. The results show that silica, slag and fly ash may inhibit alkali-silica reaction only under suitable content. When the content is less than 10%, silica fume does not markedly influence the expansion of alkali- silica reaction. When the content is 15%-20%, silica fume only may delay the expansion of alkali-silica reaction. When the content is 30%-70%, slag may only delay the expansion of alkali-silica reaction, but cannot inhibit the expansion of alkali-silica reaction. When the content is 10%, fly ash does not markedly influence the expansion of alkali-silica reaction. When the content is 20%-30%, fly ash may only delay the expansion of alkali-silica reaction, but cannot inhibit the expansion of alkali-silica reaction. When the content is over 50%, it is possible that fly ash can inhibit effectively alkali-silica reaction.
文摘On the base of the influence rule of silica fume, slag and fly ash on alkali-silica reaction under the condition of 70 ℃, the mechanism of the effect of mineral admixtures on alkali-silica reaction is studied further in the paper. The results show that the effects of mineral admixtures on alkali-silica reaction are mainly chemistry effect and surface physichemistry effect. Under suitable condition, the chemistry effect may make alkali-silica reaction to be inhibited effectively, but the physichemistry effect only make alkali-silica reaction to be delayed. The chemistry effect and the physichemistry effect of minerals admixture are relative to the content of Ca(OH)2 in system. Under the condition that there is a large quantity of Ca(OH)2, mineral admixture cannot inhibit alkali-silica reaction effectively. Only when Ca(OH)2 in the system is very less, it is possible that mineral admixture inhibits alkali-silica reaction effectively.