The phase composition, magnetic properties i.e. coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67CosNd3Y6B19 all...The phase composition, magnetic properties i.e. coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67CosNd3Y6B19 alloy, inhomogeneous in the as-quenched state, crystallized after annealing at 948 K for 0.5 h and consisted of Nd2Fe14B-type, Fe2B and paramagnetic phases. The rapidly solidified Fe64Co5Nd6Y6B19 alloy contained the Nd2Fel4B-type and paramagnetic phases. The annealing of the bulk Fe67CosNd3Y6B19 alloy at 948 K for 0.5 h led to hard magnetic properties. However, the bulk Fe64Co5Nd6Y6B19 alloy exhibited good hard magnetic properties directly after preparation.展开更多
The design and measuring potential of the latest generation of the magnetic scanner called Magscanner-Maglab System (MMS) was presented. It enabled the fast acquisition of 3D signals from magnetic sensors and their ...The design and measuring potential of the latest generation of the magnetic scanner called Magscanner-Maglab System (MMS) was presented. It enabled the fast acquisition of 3D signals from magnetic sensors and their visualization as digitalized mag- netic images. This system was used for monitoring of a thermal demagnetization process of permanent magnets. The original method and measurement devices were capable for examination of magnetic, mechanical and thermal defects in cylindrical rods made of NdFeB and non-rare earth components. Effectiveness of the method and device was tested for the reference demagnetized magnet dedicated for magnetostrictive actuators.展开更多
基金supported by the grants PBZ-MEiN/01/2006/09 (M. Hasiak)PBZ-KBN-115/T08/04 (J. Kaleta)
文摘The phase composition, magnetic properties i.e. coercivity and the magnetic polarization at room temperature for the bulk Fe67Co5Nd3Y6B19 and Fe64Co5Nd6Y6B19 alloys were studied. The bulk amorphous Fe67CosNd3Y6B19 alloy, inhomogeneous in the as-quenched state, crystallized after annealing at 948 K for 0.5 h and consisted of Nd2Fe14B-type, Fe2B and paramagnetic phases. The rapidly solidified Fe64Co5Nd6Y6B19 alloy contained the Nd2Fel4B-type and paramagnetic phases. The annealing of the bulk Fe67CosNd3Y6B19 alloy at 948 K for 0.5 h led to hard magnetic properties. However, the bulk Fe64Co5Nd6Y6B19 alloy exhibited good hard magnetic properties directly after preparation.
文摘The design and measuring potential of the latest generation of the magnetic scanner called Magscanner-Maglab System (MMS) was presented. It enabled the fast acquisition of 3D signals from magnetic sensors and their visualization as digitalized mag- netic images. This system was used for monitoring of a thermal demagnetization process of permanent magnets. The original method and measurement devices were capable for examination of magnetic, mechanical and thermal defects in cylindrical rods made of NdFeB and non-rare earth components. Effectiveness of the method and device was tested for the reference demagnetized magnet dedicated for magnetostrictive actuators.