Carbon nanotube （CNT） arrays were fabricated on Ct-Me-N-（O） alloys with content of Ct in the range of 6-40 at.% by chemical vapour deposition. The Ct was a catalytic metal from the group of the following elements...Carbon nanotube （CNT） arrays were fabricated on Ct-Me-N-（O） alloys with content of Ct in the range of 6-40 at.% by chemical vapour deposition. The Ct was a catalytic metal from the group of the following elements： Ni, Co, Fe, Pd, while Me was a transition metal from the group of IV-VII of the periodic table （where Me=Ti, V, Cr, Zr, Nb, Mo, Ta, W, Re）. Carbon nanotubes were found to grow efficiently on the alloy surface with its composition containing Ti, V, Cr, Zr, Hf, Nb or Ta. The growth of CNTs was not observed when the alloy contained W or Re. Additions of oxygen and nitrogen in the alloy facilitated the formation of oxynitrides and catalyst extrusion on the alloy surface. Replacement of the metals in alloy composition affected the diameter of the resulting CNTs. The obtained results showed that the alloy films of varying thickness （10-500 nm） may be used for the CNTs growth. The resulting CNT material was highly homogenous and its synthesis reproducible.展开更多
Specific conductivity of the composite nanomaterial layers with micron and submicron dimensions, consisting of carboxymethyl cellulose (CMC) and multiwalled carbon nanotubes (MWCNT) was investigated. Ultradispersed aq...Specific conductivity of the composite nanomaterial layers with micron and submicron dimensions, consisting of carboxymethyl cellulose (CMC) and multiwalled carbon nanotubes (MWCNT) was investigated. Ultradispersed aqueous suspension was deposited on soft (aluminum foil, plates made from polyester and polyimide, cotton fabric, office paper) and solid (coverslip, silicon wafers with silicon oxide layer) substrates by silk-screen printing. Electrical resistance was measured by four-probe method and by the method of square on surface from which the conductivity and conductivity per square of surface were calculated taking into account layer’s geometric dimensions. Specific conductivity of the layers with thickness range 0.5 - 5 μm was? ~1.2×104÷4×104 S/m, and max conductivity per square was ~ 0.2 S. Investigated nanomaterial is attractive to electronic and biomedical applications.展开更多
The properties of the composite nanomaterials (CNM) based on bovine serum albumin (BSA) and multi-walled carbon nanotubes (MWCNT), both functionalized and non-functionalized, were investigated. In order to obtain the ...The properties of the composite nanomaterials (CNM) based on bovine serum albumin (BSA) and multi-walled carbon nanotubes (MWCNT), both functionalized and non-functionalized, were investigated. In order to obtain the solid-state bulk CNM from the ultradispersed aqueous solutions of 25 wt.% BSA and (0.0015 - 0.04) wt.% MWCNT, the methods of nanotechnology and laser technology were used. It is revealed that the CNM density is 10% - 20% higher than that of water and the hardness is higher than that of BSA by a factor of 3 - 6 times. An increase in hardness Hv (by Vickers) of CNM correlated with an increase in the concentration of MWCNT, and Hyreached ~300 MPa for the case of the non-functionalized MWCNT, while for the case of the functionalized MWCNT, i.e. MWCNTf, Hy was 25% lower.展开更多
基金financially supported by the Russian Science Foundation(No.16-19-10625)
文摘Carbon nanotube （CNT） arrays were fabricated on Ct-Me-N-（O） alloys with content of Ct in the range of 6-40 at.% by chemical vapour deposition. The Ct was a catalytic metal from the group of the following elements： Ni, Co, Fe, Pd, while Me was a transition metal from the group of IV-VII of the periodic table （where Me=Ti, V, Cr, Zr, Nb, Mo, Ta, W, Re）. Carbon nanotubes were found to grow efficiently on the alloy surface with its composition containing Ti, V, Cr, Zr, Hf, Nb or Ta. The growth of CNTs was not observed when the alloy contained W or Re. Additions of oxygen and nitrogen in the alloy facilitated the formation of oxynitrides and catalyst extrusion on the alloy surface. Replacement of the metals in alloy composition affected the diameter of the resulting CNTs. The obtained results showed that the alloy films of varying thickness （10-500 nm） may be used for the CNTs growth. The resulting CNT material was highly homogenous and its synthesis reproducible.
文摘Specific conductivity of the composite nanomaterial layers with micron and submicron dimensions, consisting of carboxymethyl cellulose (CMC) and multiwalled carbon nanotubes (MWCNT) was investigated. Ultradispersed aqueous suspension was deposited on soft (aluminum foil, plates made from polyester and polyimide, cotton fabric, office paper) and solid (coverslip, silicon wafers with silicon oxide layer) substrates by silk-screen printing. Electrical resistance was measured by four-probe method and by the method of square on surface from which the conductivity and conductivity per square of surface were calculated taking into account layer’s geometric dimensions. Specific conductivity of the layers with thickness range 0.5 - 5 μm was? ~1.2×104÷4×104 S/m, and max conductivity per square was ~ 0.2 S. Investigated nanomaterial is attractive to electronic and biomedical applications.
文摘The properties of the composite nanomaterials (CNM) based on bovine serum albumin (BSA) and multi-walled carbon nanotubes (MWCNT), both functionalized and non-functionalized, were investigated. In order to obtain the solid-state bulk CNM from the ultradispersed aqueous solutions of 25 wt.% BSA and (0.0015 - 0.04) wt.% MWCNT, the methods of nanotechnology and laser technology were used. It is revealed that the CNM density is 10% - 20% higher than that of water and the hardness is higher than that of BSA by a factor of 3 - 6 times. An increase in hardness Hv (by Vickers) of CNM correlated with an increase in the concentration of MWCNT, and Hyreached ~300 MPa for the case of the non-functionalized MWCNT, while for the case of the functionalized MWCNT, i.e. MWCNTf, Hy was 25% lower.