In this work, the plastic of polylatic acid(PLA) film is coated by alumina(Al_2O_3)through dielectric barrier discharge plasma assisted atomic layer deposition(DBD PA-ALD) for the proposal of the barrier property enha...In this work, the plastic of polylatic acid(PLA) film is coated by alumina(Al_2O_3)through dielectric barrier discharge plasma assisted atomic layer deposition(DBD PA-ALD) for the proposal of the barrier property enhancement. The influence of ALD Al_2O_3 thickness on properties of barrier, mechanical, optical and degradation is investigated in detail. It is obtained that the growth rate of Al_2O_3 in DBD PA-ALD is as quick as 0.12 nm/cycle. After coated～40 nm Al_2O_3, the water vapor transmission rate of PLA is reduced by two orders of magnitude.Additionally, it is noticed that the tension strength of the coated film is improved slightly,whereas the light transmission rate is decreased with the increase of Al_2O_3 thickness. The degradation test shows that Al_2O_3 coating almost does not affect the self-degradation rate of PLA film.展开更多
基金supported by National Natural Science Foundation of China (Nos. 11775028, 11505013)Beijing Municipal National Science Foundation (Nos. 4162024, KM201510015009)the Collaborative Innovation Center of Green Printing & Publishing Technology (No. 20160113)
文摘In this work, the plastic of polylatic acid(PLA) film is coated by alumina(Al_2O_3)through dielectric barrier discharge plasma assisted atomic layer deposition(DBD PA-ALD) for the proposal of the barrier property enhancement. The influence of ALD Al_2O_3 thickness on properties of barrier, mechanical, optical and degradation is investigated in detail. It is obtained that the growth rate of Al_2O_3 in DBD PA-ALD is as quick as 0.12 nm/cycle. After coated～40 nm Al_2O_3, the water vapor transmission rate of PLA is reduced by two orders of magnitude.Additionally, it is noticed that the tension strength of the coated film is improved slightly,whereas the light transmission rate is decreased with the increase of Al_2O_3 thickness. The degradation test shows that Al_2O_3 coating almost does not affect the self-degradation rate of PLA film.