High Efficieney Synthesis of Isotaetie Polypropylene and Linear Polyethylene Using a New C_2-symmetric Carbon-bridged Zirconocene Catalyst

Ansa-Cyclohexyl-bis（4,5,6,7-tertrahydro-l-indenyl） zirconium dichloride （5） was used as catalyst for propylene and ethylene polymerization together with methyl aluminoxane （MAO） as the cocatalyst. Isotactic polypropylene （PP） was obtained with the highest activity of 6.37× 107g PP （molZr）^-1h^-1. The mesomeso （mmmmm） pentads sequence content of PP was determined by 13C NMR spectroscopy. The dependence of the microstructure on the reaction temperature and the AI/Zr molar ratio was examined and the catalytic activity of complex 5 was compared with that of the similar ansa-zirconocene 3. The high activity of the new zirconocene 5 for propylene isospectic polymerization at high temperature （60℃） is the result of its unique bridged-group structure. Complex 5/MAO displays also high catalytic activity of 0.46× 10^6 to 9.87× 10^6g PE（molZr）^-h^-in the homo-polymerization of ethylene, The visometric molecular weight of PE ranges from 0.97×10^4 to 11.16×10^4 g.mol^- under the given conditions.^13C NMR spectroscopy analysis proves the PE to be linear polyethylene （LPE）.

Ethylene Polymerization by a Novel Dinuclear Heter-oligated Titanium Complex with the Ligand of (Salicylaldiminato) (β-enaminoketonato)

The condensation of acetylacetone （CH3COCH2COCH3） with benzdine （H2N-C6H4-C6H4-NH2） yielded diimine ligand 1 [HOC（Me）C（H）（Me）C=N（p-C6H4）（C6H4-p）N= C（Me）C（H）C（Me）OH）], which was converted into sodium salts. And then the sodium salts reacted with monosalicylaldiminato titanium complex 2{[3,5-di-But′2-（O）C6H2CHN（PH）]TiCl3（THF）} in dried dichloromethane to give a new benzdine-bridged binuclear complex 3{[3,5-di-Bu′-2-（O）C6H2CHN（PH）]2 [OC（Me）C（H）（Me）C=N（p-C6H4）-（C6H4-p）N=C（Me）C（H） C（Me）]Ti2Cl4}. The complex 3 was characterized by ^1HNMR and elemental analysis. In the presence of MAO（methylaluminoxane）, the complex 3 in toluene was effective to catalyze polymerization, affording moderately high catalytic activity 1.93 × 10^5 g PE/（mol.Ti.h）]and high molecular weight polyethylene [5.63× 10^5 g/moll. The high temperature gel permeation chromatography （GPC） curve of polyethylene obtained revealed a single peak, but the molecular weight distribution （MWD = 3.21） is obviously broader than that of the similar mononuclear titanium complex. The melting points of the obtained polyethylene reaches 138 ℃, indicating that the polyethylene is of high crystallinity.