Atmospheric-Pressure DBD Cold Plasma for Preparation of High Active Au/P25 Catalysts for Low-Temperature CO Oxidation

Cold plasma generated by dielectric barrier discharge （DBD） at atmospheric pressure was adopted for preparation of commercial TiO2 Degussa P25 supported Au catalysts （Au/P25- P） with the assistance of the deposition-precipitation procedure. The influences of the plasma reduction time and calcination on the performance of the Au/P25-P catalysts were investigated. CO oxidation was performed to investigate the catalytic activity of the Au/P25 catalysts. The results show that DBD cold plasma for the fabrication of Au/P25-P catalysts is a fast process, and Au/P25-P （4 min） exhibited the highest CO oxidation activity due to the complete reduction of Au compounds and less consumption of oxygen vacancies. In order to form more oxygen vacancies active species, Au/P25-P was calcined to obtain Au/P25-PC catalysts. Interestingly, Au/P25- PC exhibited the highest activity for CO oxidation among the Au/P25 samples. The results of transmission electron microscopy （TEM） indicated that the smaller size and high distribution of Au nanoparticles are the mean reasons for a high performance of Au/P25-PC. Atmospheric- pressure DBD cold plasma was proved to be of great efficiency in preparing high performance supported Au catalysts.

Synthesis of Cu-Doped Mixed-Phase TiO_2 with the Assistance of Ionic Liquid by Atmospheric-Pressure Cold Plasma

An atmospheric-pressure dielectric barrier discharge （DBD） gas-liquid cold plasma was employed to synthesize Cu-doped TiO~ nanoparticles in an aqueous solution with the assistance of [C2MIM]BF4 ionic liquid （IL） and using air as the working gas. The influences of the discharge voltage, IL and the amount of copper nitrite were investigated. X-ray diffraction, N2 adsorption-desorption measurements and UV-Vis spectroscopy were adopted to characterize the samples. The results showed that the specific surface area of TiO2 was promoted with Cu-doping （from 57.6 m^2.g^-1 to 106.2 m^2.g^-1 with 3% Cu-doping）, and the content of anatase was increased. Besides, the band gap energy of TiO~ with Cu-doping decreased according to the UV-Vis spec- troscopy test. The 3%Cu-IL-TiO2 samples showed the highest eificiency in degrading methylene blue （MB） dye solutions under simulated sunlight with an apparent rate constant of 0.0223 min-1, which was 1.2 times higher than that of non-doped samples. According to the characterization results, the reasons for the high photocatalytic activity were discussed.