A cementitious material was prepared by mixing 80wt% Si-Mn slag powder, 10wt% lime, and 10wt% anhydrite. The compressive strength of mortar samples reaches 51.48 MPa after 28 d curing. The analyses of X-ray diffracti...A cementitious material was prepared by mixing 80wt% Si-Mn slag powder, 10wt% lime, and 10wt% anhydrite. The compressive strength of mortar samples reaches 51.48 MPa after 28 d curing. The analyses of X-ray diffraction （XRD） and scanning electron microscopy （SEM） show that much ettringite is formed in the sample cured for 3 d, and C-S-H gel increases rapidly during subsequent curing. Nuclear magnetic resonance （NMR） analysis of 29Si and 27Al and infrared spectroscopy （IR） analysis show that aluminum decomposition from tetrahedral network of the slag glass and its subsequent migration and re-combination play an important role in the process of hydration and strength development of the samples.展开更多
基金supported by the National High Technology Research and Development Program (No.2006BAC21B03)
文摘A cementitious material was prepared by mixing 80wt% Si-Mn slag powder, 10wt% lime, and 10wt% anhydrite. The compressive strength of mortar samples reaches 51.48 MPa after 28 d curing. The analyses of X-ray diffraction （XRD） and scanning electron microscopy （SEM） show that much ettringite is formed in the sample cured for 3 d, and C-S-H gel increases rapidly during subsequent curing. Nuclear magnetic resonance （NMR） analysis of 29Si and 27Al and infrared spectroscopy （IR） analysis show that aluminum decomposition from tetrahedral network of the slag glass and its subsequent migration and re-combination play an important role in the process of hydration and strength development of the samples.