In this paper, the partial oxidation of methane to synthesis gas using lattice oxygen of La1- SrxMO3-λ (M=Fe, x ...In this paper, the partial oxidation of methane to synthesis gas using lattice oxygen of La1- SrxMO3-λ (M=Fe, x Mn) perovskite oxides instead of molecular oxygen was investigated. The redox circulation between 11% O2/Ar flow and 11% CH4/He flow at 900℃ shows that methane can be oxidized to CO and H2 with a selectivity of over 90.7% using the lattice oxygen of La1- SrxFeO3-λ (x≤0.2) perovskite oxides in an appropriate reaction condition, while the lost lattice x oxygen can be supplemented by air re-oxidation. It is viable for the lattice oxygen of La1- SrxFeO3-λ (x≤0.2) perovskite x oxides instead of molecular oxygen to react with methane to synthesis gas in the redox mode.展开更多
For investigating the effect of dealumination on the pore structure and catalytic performance, ZSM-5/Y composite zeolites synthesized in situ from NaY gel were dealuminated by steaming at different temperatures. XRD ...For investigating the effect of dealumination on the pore structure and catalytic performance, ZSM-5/Y composite zeolites synthesized in situ from NaY gel were dealuminated by steaming at different temperatures. XRD (X-ray diffraction) characterization indicates that the relative crystallinity of the composite zeolites decreases with the increase in Si/Al ratio after steaming. N2 adsorption-desorption suggests that more mesopores are formed while the BET (Brunauer, Emmett and Teller) specific surface area and the micropore specific surface area decrease as the temperature of steaming rises. Daqing heavy oil was used as feedstock to test the catalytic cracking activity of ZSM-5/Y composite zeolites. The experimental results of the catalytic cracking performance reveal that the distribution of products differs due to the different conditions of hydrothermal treatment. Further hydrothermal treatment leads to an increase in the yield of light oil, and a decrease in the yield of gas products and coke.展开更多
文摘In this paper, the partial oxidation of methane to synthesis gas using lattice oxygen of La1- SrxMO3-λ (M=Fe, x Mn) perovskite oxides instead of molecular oxygen was investigated. The redox circulation between 11% O2/Ar flow and 11% CH4/He flow at 900℃ shows that methane can be oxidized to CO and H2 with a selectivity of over 90.7% using the lattice oxygen of La1- SrxFeO3-λ (x≤0.2) perovskite oxides in an appropriate reaction condition, while the lost lattice x oxygen can be supplemented by air re-oxidation. It is viable for the lattice oxygen of La1- SrxFeO3-λ (x≤0.2) perovskite x oxides instead of molecular oxygen to react with methane to synthesis gas in the redox mode.
文摘For investigating the effect of dealumination on the pore structure and catalytic performance, ZSM-5/Y composite zeolites synthesized in situ from NaY gel were dealuminated by steaming at different temperatures. XRD (X-ray diffraction) characterization indicates that the relative crystallinity of the composite zeolites decreases with the increase in Si/Al ratio after steaming. N2 adsorption-desorption suggests that more mesopores are formed while the BET (Brunauer, Emmett and Teller) specific surface area and the micropore specific surface area decrease as the temperature of steaming rises. Daqing heavy oil was used as feedstock to test the catalytic cracking activity of ZSM-5/Y composite zeolites. The experimental results of the catalytic cracking performance reveal that the distribution of products differs due to the different conditions of hydrothermal treatment. Further hydrothermal treatment leads to an increase in the yield of light oil, and a decrease in the yield of gas products and coke.