Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer co...Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.展开更多
The effect of single overload on the fatigue crack growth in 2024-T3 and 7075-T6 Al alloys was analyzed.Fatigue tests under constantamplitude loading with overload peak were carried out on V-notched specimens.Fractogr...The effect of single overload on the fatigue crack growth in 2024-T3 and 7075-T6 Al alloys was analyzed.Fatigue tests under constantamplitude loading with overload peak were carried out on V-notched specimens.Fractographic analysis was used as a principal approach to explain the crack growth retardation due to the overload.Scanning electron microscopy(SEM)analyses were conducted on the fractured surface of failed specimens to study the retardation effect.The obtained results show that the overload application generates a plastic zone in both aluminum alloys.The generated plastic zone is three times larger in the case of 2024-T3 compared to 7075-T6,and thus,a significant crack retardation was induced for 2024-T3.The retardation effect due to the overload for 2024-T3 and 7075-T6 lasted for about 10 mm and 1 mm,respectively,from the point of overload application.展开更多
The presence of porosities in bone cement (polymethylmethacrylate) in total hip prosthesis (THP) cemented is necessary for the diffusion of antibiotics, but it is a critical characteristic of weakening by the effect o...The presence of porosities in bone cement (polymethylmethacrylate) in total hip prosthesis (THP) cemented is necessary for the diffusion of antibiotics, but it is a critical characteristic of weakening by the effect of stress concentration and the interconnecting pores. The aim of this study was to analyse by the finite element method (FEM), the size influence of micro-cavities in cement assuming the junction cup-bone, and the effect of cavity-cavity interaction on the stress level and distribution in cement according to the human stance defined by the implant position axis compared to that of the cup.展开更多
基金The work was supported by the National Natural Science Foundation of China (Grant No. 20074033) and the High-TechResearch and Development Program of China (Grant no. 2002AA601230).
文摘Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.
基金the Deanship of Scientific Research at King Saud University for funding the work through the research group (No. RGP-VPP-035)
文摘The effect of single overload on the fatigue crack growth in 2024-T3 and 7075-T6 Al alloys was analyzed.Fatigue tests under constantamplitude loading with overload peak were carried out on V-notched specimens.Fractographic analysis was used as a principal approach to explain the crack growth retardation due to the overload.Scanning electron microscopy(SEM)analyses were conducted on the fractured surface of failed specimens to study the retardation effect.The obtained results show that the overload application generates a plastic zone in both aluminum alloys.The generated plastic zone is three times larger in the case of 2024-T3 compared to 7075-T6,and thus,a significant crack retardation was induced for 2024-T3.The retardation effect due to the overload for 2024-T3 and 7075-T6 lasted for about 10 mm and 1 mm,respectively,from the point of overload application.
文摘The presence of porosities in bone cement (polymethylmethacrylate) in total hip prosthesis (THP) cemented is necessary for the diffusion of antibiotics, but it is a critical characteristic of weakening by the effect of stress concentration and the interconnecting pores. The aim of this study was to analyse by the finite element method (FEM), the size influence of micro-cavities in cement assuming the junction cup-bone, and the effect of cavity-cavity interaction on the stress level and distribution in cement according to the human stance defined by the implant position axis compared to that of the cup.