O'-sialon-ZrO2 composite based on the cheap commercial available zircon and silicon as raw materials can be achieved by using reac-tion nitridation method,More attention was given to the nitriding process and the ...O'-sialon-ZrO2 composite based on the cheap commercial available zircon and silicon as raw materials can be achieved by using reac-tion nitridation method,More attention was given to the nitriding process and the effect of additives on it .The experimental results show that there are two nitridation paths:one is the direct nitridation of silicon powder and the other is through the reaction between the medi-um compound ZrSi2 and the nitrogen.The effects of addition of calcia and the incorpora-tion of BN on the nitriding reaction were also investigated,the primitive experimental results demonstrated that both of calcia and BN could deteriorate the nitriding degree.展开更多
The influences of four kinds of additives added into the matrix of MgO-Al2O3 unbuned products were investigated,The results show that samples with proper MgO/Al2O3 ration and proper addition of Cr2O3(2%- 4%) have good...The influences of four kinds of additives added into the matrix of MgO-Al2O3 unbuned products were investigated,The results show that samples with proper MgO/Al2O3 ration and proper addition of Cr2O3(2%- 4%) have good thermal shock resistance and slag corrosion resistance as well,XRD and SEM determination results indicate that a kind of compound spinel(Mg,Al, Cr) O4 was formed and the microstucture of the samples are denser.展开更多
文摘O'-sialon-ZrO2 composite based on the cheap commercial available zircon and silicon as raw materials can be achieved by using reac-tion nitridation method,More attention was given to the nitriding process and the effect of additives on it .The experimental results show that there are two nitridation paths:one is the direct nitridation of silicon powder and the other is through the reaction between the medi-um compound ZrSi2 and the nitrogen.The effects of addition of calcia and the incorpora-tion of BN on the nitriding reaction were also investigated,the primitive experimental results demonstrated that both of calcia and BN could deteriorate the nitriding degree.
文摘The influences of four kinds of additives added into the matrix of MgO-Al2O3 unbuned products were investigated,The results show that samples with proper MgO/Al2O3 ration and proper addition of Cr2O3(2%- 4%) have good thermal shock resistance and slag corrosion resistance as well,XRD and SEM determination results indicate that a kind of compound spinel(Mg,Al, Cr) O4 was formed and the microstucture of the samples are denser.