A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene (MA-PP) and maleic anhydride grafted ethylene-propylene-diene copolymer (MA-EPDM), on wood-flou...A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene (MA-PP) and maleic anhydride grafted ethylene-propylene-diene copolymer (MA-EPDM), on wood-flour/polypropylene (WF/PP) composites. WF/PP composites were prepared by direct extrusion profiles using a twin-screw/single-screw extruder system. DMA analysis showed that the loss factor of composites decreased and the storage modulus improved in the presence of MA-PP, which indicated much better interfacial adhesion between the PP matrix and wood flour filler than in the absence of compatibilizer. Morphological feature based on SEM observation showed that MA-PP and MA-EPDM improved the dispersion of the wood particles in the plastic matrix. MA-EPDM is a soft segment, although it improved the interfacial adhesion, storage modulus decreases with adding of MA-EPDM. As compatibilizer of wood-flour/polypropylene composites, both DMA analysis and SEM feature proved that MA-PP was superior to MA-EPDM.展开更多
基金This paper was supported by National Foundation of Application of Agricultural Scientific and Technological Achievements (2006GB23600450).
文摘A study was conducted to investigate the effects of compatibilizers, including Maleic anhydride grafted polypropylene (MA-PP) and maleic anhydride grafted ethylene-propylene-diene copolymer (MA-EPDM), on wood-flour/polypropylene (WF/PP) composites. WF/PP composites were prepared by direct extrusion profiles using a twin-screw/single-screw extruder system. DMA analysis showed that the loss factor of composites decreased and the storage modulus improved in the presence of MA-PP, which indicated much better interfacial adhesion between the PP matrix and wood flour filler than in the absence of compatibilizer. Morphological feature based on SEM observation showed that MA-PP and MA-EPDM improved the dispersion of the wood particles in the plastic matrix. MA-EPDM is a soft segment, although it improved the interfacial adhesion, storage modulus decreases with adding of MA-EPDM. As compatibilizer of wood-flour/polypropylene composites, both DMA analysis and SEM feature proved that MA-PP was superior to MA-EPDM.
基金This paper was supported by National 863 Program (2002AA245141)national Foundation of Application of Agricul-tural Scientific and Technological Achievements (2006GB23600450)