Using methyl triethoxysilicane as precursor, a moisture-resistant coating for neodymium-doped laser glass was developed by the sol-gel process. Colloidal silica was added in coating solution as modifier. The refractiv...Using methyl triethoxysilicane as precursor, a moisture-resistant coating for neodymium-doped laser glass was developed by the sol-gel process. Colloidal silica was added in coating solution as modifier. The refractive index of this coating varied from 1.31 to 1.42. A porous antireflective （AR） silica coating with the index of 1.27 was coated on the moisture-resistant coating surface. The two-layer coating possessed transmission up to 99.1% at wavelength of 966 nm, surface root-mean-square （RMS） roughaess of 1.245 am, and roughness of average （RA） of 0.961 am. In the case of laser of 1053-nm laser waveleilgth and 1-ns pulse duration, the damage threshold of the two-layer coatings was more than 15 J/cm^2.展开更多
基金This work was supported by the National "863" Project of China (No. 863-804-2).
文摘Using methyl triethoxysilicane as precursor, a moisture-resistant coating for neodymium-doped laser glass was developed by the sol-gel process. Colloidal silica was added in coating solution as modifier. The refractive index of this coating varied from 1.31 to 1.42. A porous antireflective （AR） silica coating with the index of 1.27 was coated on the moisture-resistant coating surface. The two-layer coating possessed transmission up to 99.1% at wavelength of 966 nm, surface root-mean-square （RMS） roughaess of 1.245 am, and roughness of average （RA） of 0.961 am. In the case of laser of 1053-nm laser waveleilgth and 1-ns pulse duration, the damage threshold of the two-layer coatings was more than 15 J/cm^2.