This paper studies the mechanism of formation of the deposit layer by (ESD) electro-spark deposition process. Inconel 738 substrates are coated with a deposited layer of NI6625 (Inconel 625). Selections of these two a...This paper studies the mechanism of formation of the deposit layer by (ESD) electro-spark deposition process. Inconel 738 substrates are coated with a deposited layer of NI6625 (Inconel 625). Selections of these two alloys have been done because they had wide applications and importance in the industry especially in gas turban blades in inland stations and in aircraft engines. ESD is suggested because it has a low input heat process which eliminates the effect of HAZ in these Ni-superfluous due to their sustainability to micro-cracks. The coating contains many deposited sub-layers coming from evaporated and melted micro-regions as a result of locally high heat generated by discharging a series of capacitors charged and discharged in a controlled manner between electrode and substrate material. The maximum deposition rates at the beginning of the process and decreases until been in a steady state condition due to the nature of the resultant morphology of the created surface.展开更多
The Bi-2223/Ag tapes were prepared with spray-died powders, which are of different particle sizes and phase assemblages by varying the annealing time in pure oxygen. Longer time annealing degraded the reactivity of pr...The Bi-2223/Ag tapes were prepared with spray-died powders, which are of different particle sizes and phase assemblages by varying the annealing time in pure oxygen. Longer time annealing degraded the reactivity of precursor powder, which in turn resulted in an incomplete conversion from precursors to Bi-2223, porosity core and misaligned grains in fully processed tapes. The best Jc in short pressed samples varied from 29.7 to 47kA/cm2 for the tapes made from different powders.展开更多
文摘This paper studies the mechanism of formation of the deposit layer by (ESD) electro-spark deposition process. Inconel 738 substrates are coated with a deposited layer of NI6625 (Inconel 625). Selections of these two alloys have been done because they had wide applications and importance in the industry especially in gas turban blades in inland stations and in aircraft engines. ESD is suggested because it has a low input heat process which eliminates the effect of HAZ in these Ni-superfluous due to their sustainability to micro-cracks. The coating contains many deposited sub-layers coming from evaporated and melted micro-regions as a result of locally high heat generated by discharging a series of capacitors charged and discharged in a controlled manner between electrode and substrate material. The maximum deposition rates at the beginning of the process and decreases until been in a steady state condition due to the nature of the resultant morphology of the created surface.
文摘The Bi-2223/Ag tapes were prepared with spray-died powders, which are of different particle sizes and phase assemblages by varying the annealing time in pure oxygen. Longer time annealing degraded the reactivity of precursor powder, which in turn resulted in an incomplete conversion from precursors to Bi-2223, porosity core and misaligned grains in fully processed tapes. The best Jc in short pressed samples varied from 29.7 to 47kA/cm2 for the tapes made from different powders.