Activities of space materials science research in China have been continuously supported by two main national programs.One is the China Space Station(CSS)program since 1992,and the other is the Strategic Priority Prog...Activities of space materials science research in China have been continuously supported by two main national programs.One is the China Space Station(CSS)program since 1992,and the other is the Strategic Priority Program(SPP)on Space Science since 2011.In CSS plan in 2019,eleven space materials science experimental projects were officially approved for execution during the construction of the space station.In the SPP Phase Ⅱ launched in 2018,seven pre-research projects are deployed as the first batch in 2018,and one concept study project in 2019.These pre-research projects will be cultivated as candidates for future selection as space experiment projects on the recovery of scientific experimental satellites in the future.A new apparatus of electrostatic levitation system for ground-based research of space materials science and rapid solidification research has been developed under the support of the National Natural Science Foundation of China.In order to promote domestic academic activities and to enhance the advancement of space materials science in China,the Space Materials Science and Technology Division belong to the Chinese Materials Research Society was established in 2019.We also organized scientists to write five review papers on space materials science as a special topic published in the journal Scientia Sinica to provide valuable scientific and technical references for Chinese researchers.展开更多
The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of th...The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of the film to 1.36 T at 300 K and remains 0.938 T at 380 K.As the thickness of the Y spacer layer increases,Y participates in the formation of the main phase in the film,and further regulates the formation of La-B phases.The results of the first-order reversal curve(FORC)and micromagnetic fitting show that the coercivity of all the films is dominated by nucleation mechanism.The c-axis preferred orientation,good magnetic microstructure parameters and the largest dipole interaction enhance the coercivity.Therefore,the introduction of the Y spacer layer can be an effective way to improve the coercivity of La-Nd-Fe-B film over a wide temperature range of 150 K-380 K.展开更多
Mg-6Zn-1Y(at.%)ribbons with strengthening precipitates of multi-type nanoquasicrystals were prepared by melt-spinning followed by aging treatments.Microstructural evolution of the rapidly solidified ribbons during iso...Mg-6Zn-1Y(at.%)ribbons with strengthening precipitates of multi-type nanoquasicrystals were prepared by melt-spinning followed by aging treatments.Microstructural evolution of the rapidly solidified ribbons during isothermal aging was comprehensively studied using various electron microscopy techniques.Two new kinds of decagonal quasicrystals were formed in aged ribbons,in addition to precipitation of nanometer icosahedral quasicrystals.Atomic-resolution observations reveal that both decagonal quasicrystals can be modeled by quasiperiodic tiling with decagonal clusters of 2.5 nm in diameter,but overlap of neighboring clusters in both decagonal quasicrystals is different from the Gummelt model observed in other quasicrystals.A shell composed of complex Laves Mg-Zn domains was formed surrounding each decagonal quasicrystal precipitate upon prolonged aging.In addition,all kinds of nanoprecipitates exhibit excellent structure and size stability at 573 K.Our findings may have implications for not only fundamental studies about quasicrystals,but also microstructural manipulation of high-performance Mg alloys.展开更多
Metal-ion batteries(MIBs),including alkali metal-ion(Li^(+),Na^(+),and K^(3)),multi-valent metal-ion(Zn^(2+),Mg^(2+),and Al^(3+)),metal-air,and metal-sulfur batteries,play an indispensable role in electrochemical ener...Metal-ion batteries(MIBs),including alkali metal-ion(Li^(+),Na^(+),and K^(3)),multi-valent metal-ion(Zn^(2+),Mg^(2+),and Al^(3+)),metal-air,and metal-sulfur batteries,play an indispensable role in electrochemical energy storage.However,the performance of MIBs is significantly influenced by numerous variables,resulting in multi-dimensional and long-term challenges in the field of battery research and performance enhancement.Machine learning(ML),with its capability to solve intricate tasks and perform robust data processing,is now catalyzing a revolutionary transformation in the development of MIB materials and devices.In this review,we summarize the utilization of ML algorithms that have expedited research on MIBs over the past five years.We present an extensive overview of existing algorithms,elucidating their details,advantages,and limitations in various applications,which encompass electrode screening,material property prediction,electrolyte formulation design,electrode material characterization,manufacturing parameter optimization,and real-time battery status monitoring.Finally,we propose potential solutions and future directions for the application of ML in advancing MIB development.展开更多
Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_...Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass was observed with typical spin glass behavior around 15.5 K.In addition,we find that the magnetic entropy change(-△S_(M))originates from the sample undergoing a ferromagnetic(FM)to paramagnetic(PM)transition around 20 K.Under a field change from 0 T to 7 T,the value of maximum magnetic entropy change(-△S_(M)^(max))reaches 12.5 J/kg·K,and the corresponding value of RC reaches 487.7 J/kg in the temperature range from 6 K to 60 K.The large RC and wide temperature range make the Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass be a promising material for application in magnetic refrigerators.展开更多
We demonstrated a scheme of phase-locked terahertz quantum cascade lasers(THz QCLs)array,with a single-mode pulse power of 108 mW at 13 K.The device utilizes a Talbot cavity to achieve phase locking among five ridge l...We demonstrated a scheme of phase-locked terahertz quantum cascade lasers(THz QCLs)array,with a single-mode pulse power of 108 mW at 13 K.The device utilizes a Talbot cavity to achieve phase locking among five ridge lasers with first-order buried distributed feedback(DFB)grating,resulting in nearly five times amplification of the single-mode power.Due to the optimum length of Talbot cavity depends on wavelength,the combination of Talbot cavity with the DFB grating leads to better power amplification than the combination with multimode Fabry-Perot(F-P)cavities.The Talbot cavity facet reflects light back to the ridge array direction and achieves self-imaging in the array,enabling phase-locked operation of ridges.We set the spacing between adjacent elements to be 220μm,much larger than the free-space wavelength,ensuring the operation of the fundamental supermode throughout the laser's dynamic range and obtaining a high-brightness far-field distribution.This scheme provides a new approach for enhancing the single-mode power of THz QCLs.展开更多
Helicity-dependent photocurrent(HDPC)of the surface states in a high-quality topological insulator(Bi_(0.7)Sb_(0.3))_(2)Te_(3)nanoplate grown by chemical vapor deposition(CVD)is investigated.By investigating the angle...Helicity-dependent photocurrent(HDPC)of the surface states in a high-quality topological insulator(Bi_(0.7)Sb_(0.3))_(2)Te_(3)nanoplate grown by chemical vapor deposition(CVD)is investigated.By investigating the angle-dependent HDPC,it is found that the HDPC is mainly contributed by the circular photogalvanic effect(CPGE)current when the incident plane is perpendicular to the connection of the two contacts,whereas the circular photon drag effect(CPDE)dominates the HDPC when the incident plane is parallel to the connection of the two contacts.In addition,the CPGE of the(Bi_(0.7)Sb_(0.3))_(2)Te_(3)nanoplate is regulated by temperature,light power,excitation wavelength,the source–drain and ionic liquid top-gate voltages,and the regulation mechanisms are discussed.It is demonstrated that(Bi_(0.7)Sb_(0.3))_(2)Te_(3)nanoplates may provide a good platform for novel opto-spintronics devices.展开更多
Hydrogen peroxide(H_(2)O_(2))production by the electrochemical 2-electron oxygen reduction reaction(2e−ORR)is a promising alternative to the energy-intensive anthraquinone process,and single-atom electrocatalysts show...Hydrogen peroxide(H_(2)O_(2))production by the electrochemical 2-electron oxygen reduction reaction(2e−ORR)is a promising alternative to the energy-intensive anthraquinone process,and single-atom electrocatalysts show the unique capability of high selectivity toward 2e−ORR against the 4e−one.The extremely low surface density of the single-atom sites and the inflexibility in manipulating their geometric/electronic configurations,however,compromise the H_(2)O_(2) yield and impede further performance enhancement.Herein,we construct a family of multiatom catalysts(MACs),on which two or three single atoms are closely coordinated to form high-density active sites that are versatile in their atomic configurations for optimal adsorption of essential*OOH species.Among them,the Cox–Ni MAC presents excellent electrocatalytic performance for 2e−ORR,in terms of its exceptionally high H_(2)O_(2) yield in acidic electrolytes(28.96 mol L^(−1) gcat.^(−1) h^(−1))and high selectivity under acidic to neutral conditions in a wide potential region(>80%,0–0.7 V).Operando X-ray absorption and density functional theory analyses jointly unveil its unique trimetallic Co2NiN8 configuration,which efficiently induces an appropriate Ni–d orbital filling and modulates the*OOH adsorption,together boosting the electrocatalytic 2e−ORR capability.This work thus provides a new MAC strategy for tuning the geometric/electronic structure of active sites for 2e−ORR and other potential electrochemical processes.展开更多
Optical reflection anisotropy microscopy mappings of micropipe defects on the surface of a 4H-SiC single crystal are studied by the scanning anisotropy microscopy(SAM)system.The reflection anisotropy(RA)image with a...Optical reflection anisotropy microscopy mappings of micropipe defects on the surface of a 4H-SiC single crystal are studied by the scanning anisotropy microscopy(SAM)system.The reflection anisotropy(RA)image with a'butterfly pattern'is obtained around the micropipes by SAM.The RA image of the edge dislocations is theoretically simulated based on dislocation theory and the photoelastic principle.By comparing with the Raman spectrum,it is verified that the micropipes consist of edge dislocations.The different patterns of the RA images are due to the different orientations of the Burgers vectors.Besides,the strain distribution of the micropipes is also deduced.One can identify the dislocation type,the direction of the Burgers vector and the optical anisotropy from the RA image by using SAM.Therefore,SAM is an ideal tool to measure the optical anisotropy induced by the strain field around a defect.展开更多
Mg-Y cast alloy shows excellent ductility(elongation to failure>15%)compared with pure Mg and commercial Mg cast alloys.By monitoring the microstructure evolution during an in situ tensile test of a Mg-2.5 wt%Y all...Mg-Y cast alloy shows excellent ductility(elongation to failure>15%)compared with pure Mg and commercial Mg cast alloys.By monitoring the microstructure evolution during an in situ tensile test of a Mg-2.5 wt%Y alloy,we identify the activation of prismatic<c>slip,which is rare in Mg.Synchrotron X-ray micro-beam Laue diffraction(μ-Laue)and transmission electron microscopy revealed the morphology of prismatic<c>slip bands and individual<c>dislocations.Density functional theory and molecular dynamics calculations indicate that solute Y can significantly reduce the stacking fault energy(SFE)along<c>direction on prismatic plane in Mg lattice and thus facilitate the nucleation of<c>dislocations during deformation.The presence of free<c>dislocations in the Mg lattice can also lead to nucleation of{10–12}twins even under unfavorable geometric conditions.展开更多
Compared to reforming reactions using hydrocarbons,ethanol steam reforming(ESR)is a sustainable alternative for hydrogen(H_(2))production since ethanol can be produced sustainably using biomass.This work explores the ...Compared to reforming reactions using hydrocarbons,ethanol steam reforming(ESR)is a sustainable alternative for hydrogen(H_(2))production since ethanol can be produced sustainably using biomass.This work explores the catalyst design strategies for preparing the Ni supported on ZSM-5 zeolite catalysts to promote ESR.Specifically,two-dimensional ZSM-5 nanosheet and conventional ZSM-5 crystal were used as the catalyst carriers and two synthesis strategies,i.e.,in situ encapsulation and wet impregnation method,were employed to prepare the catalysts.Based on the comparative characterization of the catalysts and comparative catalytic assessments,it was found that the combination of the in situ encapsulation synthesis and the ZSM-5 nanosheet carrier was the effective strategy to develop catalysts for promoting H_(2) production via ESR due to the improved mass transfer(through the 2-D structure of ZSM-5 nanosheet)and formation of confined small Ni nanoparticles(resulted via the in situ encapsulation synthesis).In addition,the resulting ZSM-5 nanosheet supported Ni catalyst also showed high Ni dispersion and high accessibility to Ni sites by the reactants,being able to improve the activity and stability of catalysts and suppress metal sintering and coking during ESR at high reaction temperatures.Thus,the Ni supported on ZSM-5 nanosheet catalyst prepared by encapsulation showed the stable performance with~88% ethanol conversion and~65% H_(2) yield achieved during a 48-h longevity test at 550-C.展开更多
Recently, giant intrinsic anomalous Hall effect(AHE) has been observed in the materials with kagome lattice.Here, we systematically investigate the influence of high pressure on the AHE in the ferromagnet LiMn_(6)Sn_(...Recently, giant intrinsic anomalous Hall effect(AHE) has been observed in the materials with kagome lattice.Here, we systematically investigate the influence of high pressure on the AHE in the ferromagnet LiMn_(6)Sn_(6) with clean Mn kagome lattice. Our in situ high-pressure Raman spectroscopy indicates that the crystal structure of LiMn_(6)Sn_(6) maintains a hexagonal phase under high pressures up to 8.51 GPa. The anomalous Hall conductivity(AHC) σ_(xy)^(A) remains around 150 Ω^(-1)·cm^(-1), dominated by the intrinsic mechanism. Combined with theoretical calculations, our results indicate that the stable AHE under pressure in Li Mn_(6)Sn_(6) originates from the robust electronic and magnetic structure.展开更多
Nanocarbon materials play a critical role in the development of new or improved technologies and devices for sustainable production and use of renewable energy. This perspective paper defines some of the trends and ou...Nanocarbon materials play a critical role in the development of new or improved technologies and devices for sustainable production and use of renewable energy. This perspective paper defines some of the trends and outlooks in this exciting area, with the effort of evidencing some of the possibilities offered from the growing level of knowledge, as testified from the exponentially rising number of publications, and putting bases for a more rational design of these nanomaterials. The basic members of the new carbon family are fullerene, graphene, and carbon nanotube. Derived from them are carbon quantum dots, nanohorn, nanofiber, nano ribbon, nanocapsulate, nanocage and other nanomorphologies. Second generation nanocarbons are those which have been modified by surface functionalization or doping with heteroatoms to create specific tailored properties. The third generation of nanocarbons is the nanoarchitectured supramolecular hybrids or composites of the first and second genera- tion nanocarbons, or with organic or inorganic species. The advantages of the new carbon materials, relating to the field of sustainable energy, are discussed, evidencing the unique properties that they offer for developing next generation solar devices and energy storage solutions.展开更多
CoMn layered double hydroxides(CoMn-LDH)are promising electrode materials for supercapacitors because of their excellent cyclic stability.However,they possess relatively low capacitances.In this work,hybrid CoMn-LDH@M...CoMn layered double hydroxides(CoMn-LDH)are promising electrode materials for supercapacitors because of their excellent cyclic stability.However,they possess relatively low capacitances.In this work,hybrid CoMn-LDH@MnO2 products grown on Ni foams were obtained through a facile hydrothermal method.The as-synthesized samples employed as electrodes deliver a specific capacitance of 2325.01 F g^-1 at 1 A g^-1.An assembled asymmetric supercapacitor using these products as positive electrodes shows a maximum energy density of 59.73 W h kg^-1 at 1000.09 W kg^-1.The prominent electrochemical performance of the as-prepared electrodes could be attributes to hierarchical structures.These findings suggest that hybrid structures might be potential alternatives for future flexible energy storage devices.展开更多
Vanadium pentoxide (V205) exhibits high theoretical capacities when used as a cathode in lithium ion batteries (LIBs), but its application is limited by its structural instability as well as its low lithium and el...Vanadium pentoxide (V205) exhibits high theoretical capacities when used as a cathode in lithium ion batteries (LIBs), but its application is limited by its structural instability as well as its low lithium and electronic conductivities. A porous composite of V2Os-SnO2/carbon nanotubes (CNTs) was prepared by a hydrothermal method and followed by thermal treatment. The small particles of V205, their porous structure and the coexistence of SnO2 and CNTs can all facilitate the diffusion rates of the electrons and lithium ions. Electrochemical impedance spectra indicated higher ionic and electric conductivities, as compared to commercial V205. The VzOs-SnOz/CNTs composite gave a reversible discharge capacity of 198 mAh.g- 1 at the voltage range of 2.05-4.0 V, measured at a current rate of 200 mA.g-1, while that of the commercial V205 was only 88 mAh.g-1, demonstrating that the porous V2Os-SnOz/CNTs composite is a promising candidate for high-performance lithium secondary batteries.展开更多
The deformation, damage, fracture, plasticity and melting phenomenon induced by shear fracture were investigated and summarized for Zr-, Cu-, Ti- and Mg-based bulk metallic glasses (BMGs) and their composites. The s...The deformation, damage, fracture, plasticity and melting phenomenon induced by shear fracture were investigated and summarized for Zr-, Cu-, Ti- and Mg-based bulk metallic glasses (BMGs) and their composites. The shear fracture angles of these BMG materials often display obvious differences under compression and tension, and follow either the Mohr-Coulomb criterion or the unified tensile fracture criterion. The compressive plasticity of the composites is always higher than the tensile plasticity, leading to a significant inconsistency. The enhanced plasticity of BMG composites containing ductile dendrites compared to monolithic glasses strongly depends on the details of the microstructure of the composites. A deformation and damage mechanism of pseudo-plasticity, related to local cracking, is proposed to explain the inconsistency of plastic deformation under tension and compression. Besides, significant melting on the shear fracture surfaces was observed. It is suggested that melting is a common phenomenon in these materials with high strength and high elastic energy, as it is typical for BMGs and their composites failing under shear fracture. The melting mechanism can be explained by a combined effect of a significant temperature rise in the shear bands and the instantaneous release of the large amount of elastic energy stored in the material.展开更多
Nickel/cobalt-layered double hydroxides(Ni Co-LDH) have been attracted increasing interest in the applications of anode materials for lithium ion battery(LIB), but the low cycle stability and rate performance are stil...Nickel/cobalt-layered double hydroxides(Ni Co-LDH) have been attracted increasing interest in the applications of anode materials for lithium ion battery(LIB), but the low cycle stability and rate performance are still limited its practice applications. To achieve high performance LIB, the surface-confined strategy has been applied to design and fabricate a new anode material of NiCo-LDH nanosheet anchored on the surface of Ti3C2 MXene(Ni Co-LDH/Ti3C2). The ultra-thin, bended and wrinkled α-phase crystal with an interlayer spacing of 8.1 ? can arrange on the conductive substrates Ti3C2 MXene directly, resulting in high electrolyte diffusion ability and low internal resistance. Furthermore, chemical bond interactions between the highly conductive Ti3C2 MXene and Ni Co-LDH nanosheets can greatly increase the ion and electron transport and reduce the volume expansion of NiCo-LDH during Li ion intercalation. As expected,the discharge capacity of 562 m Ah g-1 at 5.0 A g-1 for 800 cycles without degradation can be achieved,rate capability and cycle performance are better than that of NiCo-LDH(~100 mAh g-1). Furthermore, the density function theory(DFT) calculations were performed to demonstrate that Ni Co-LDH/Ti3C2 system can be used as a highly desirable and promising anode material for lithium ion battery.展开更多
As a clean and renewable energy source,solar energy is a competitive alternative to replace conventional fossil fuels.Nevertheless,its serious fluctuating nature usually leads to a poor alignment with the actual energ...As a clean and renewable energy source,solar energy is a competitive alternative to replace conventional fossil fuels.Nevertheless,its serious fluctuating nature usually leads to a poor alignment with the actual energy demand.To solve this problem,the direct solar-to-electrochemical energy conversion and storage have been regarded as a feasible strategy.In this context,the development of high-performance integrated devices based on solar energy conversion parts(i.e.,solar cells or photoelectrodes)and electrochemical energy storage units(i.e.,rechargeable batteries or supercapacitors[SCs])has become increasingly necessary and urgent,in which carbon and carbon-based functional materials play a fundamental role in determining their energy conversion/storage performances.Herein,we summarize the latest progress on these integrated devices for solar electricity energy conversion and storage,with special emphasis on the critical role of carbon-based functional materials.First,principles of integrated devices are introduced,especially roles of carbon-based materials in these hybrid energy devices.Then,two major types of important integrated devices,including photovoltaic and photoelectrochemicalrechargeable batteries or SCs,are discussed in detail.Finally,key challenges and opportunities in the future development are also discussed.By this review,we hope to pave an avenue toward the development of stable and efficient devices for solar energy conversion and storage.展开更多
Lithium intercalation into graphite contributes a theoretical capacity of 372 m Ah g-1and thus leads to an earthshaking change for energy storage[1].Lithium intercalation behaviors have been investigated via X-ray dif...Lithium intercalation into graphite contributes a theoretical capacity of 372 m Ah g-1and thus leads to an earthshaking change for energy storage[1].Lithium intercalation behaviors have been investigated via X-ray diffraction(XRD),Raman,Fourier transform infrared spectroscopy(FTIR)and X-ray absorption fine structure (XAFS)with the aid of in-situ electrochemical characterization technologies.展开更多
Silicon-based photonic integration has attracted the interest of semiconductor scientists because it has high luminous efficiency and electron mobility.Breakthroughs have been made in silicon-based integrated lasers o...Silicon-based photonic integration has attracted the interest of semiconductor scientists because it has high luminous efficiency and electron mobility.Breakthroughs have been made in silicon-based integrated lasers over the past few decades.Here we review three main methods of integration ofⅢ–Ⅴ materials on Si,namely direct growth,bonding,and selectivearea hetero-epitaxy.TheⅢ–Ⅴmaterials we introduced mainly include materials such as GaAs and InP.The lasers are mainly lasers of related communication bands.We also introduced the advantages and challenges of the three methods.展开更多
基金Supports by the Strategic Priority Research Program on Space Science,the Chinese Academy of Sciences(XDA15013200,XDA15013700,XDA15013800,XDA15051200)the China’s Manned Space Station Project(TGJZ800-2-RW024)and the National Natural Science Foundation of China(51327901)。
文摘Activities of space materials science research in China have been continuously supported by two main national programs.One is the China Space Station(CSS)program since 1992,and the other is the Strategic Priority Program(SPP)on Space Science since 2011.In CSS plan in 2019,eleven space materials science experimental projects were officially approved for execution during the construction of the space station.In the SPP Phase Ⅱ launched in 2018,seven pre-research projects are deployed as the first batch in 2018,and one concept study project in 2019.These pre-research projects will be cultivated as candidates for future selection as space experiment projects on the recovery of scientific experimental satellites in the future.A new apparatus of electrostatic levitation system for ground-based research of space materials science and rapid solidification research has been developed under the support of the National Natural Science Foundation of China.In order to promote domestic academic activities and to enhance the advancement of space materials science in China,the Space Materials Science and Technology Division belong to the Chinese Materials Research Society was established in 2019.We also organized scientists to write five review papers on space materials science as a special topic published in the journal Scientia Sinica to provide valuable scientific and technical references for Chinese researchers.
基金Project supported by the National Key Research and Development Program of China(Grant No.2021YFB3500303)the National Natural Science Foundation of China(Grant Nos.52031014 and 51971219).
文摘The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of the film to 1.36 T at 300 K and remains 0.938 T at 380 K.As the thickness of the Y spacer layer increases,Y participates in the formation of the main phase in the film,and further regulates the formation of La-B phases.The results of the first-order reversal curve(FORC)and micromagnetic fitting show that the coercivity of all the films is dominated by nucleation mechanism.The c-axis preferred orientation,good magnetic microstructure parameters and the largest dipole interaction enhance the coercivity.Therefore,the introduction of the Y spacer layer can be an effective way to improve the coercivity of La-Nd-Fe-B film over a wide temperature range of 150 K-380 K.
基金supported by the National Natural Science Foundation of China (grant number: 51771202, 51971225, 52001225)Key Research of Frontier Science, Chinese Academy of Science (grant number: QYZDY-SSW-JSC207)+1 种基金Ji Hua Laboratory (X210141TL210)Guangdong Province (2021B0301030003)
文摘Mg-6Zn-1Y(at.%)ribbons with strengthening precipitates of multi-type nanoquasicrystals were prepared by melt-spinning followed by aging treatments.Microstructural evolution of the rapidly solidified ribbons during isothermal aging was comprehensively studied using various electron microscopy techniques.Two new kinds of decagonal quasicrystals were formed in aged ribbons,in addition to precipitation of nanometer icosahedral quasicrystals.Atomic-resolution observations reveal that both decagonal quasicrystals can be modeled by quasiperiodic tiling with decagonal clusters of 2.5 nm in diameter,but overlap of neighboring clusters in both decagonal quasicrystals is different from the Gummelt model observed in other quasicrystals.A shell composed of complex Laves Mg-Zn domains was formed surrounding each decagonal quasicrystal precipitate upon prolonged aging.In addition,all kinds of nanoprecipitates exhibit excellent structure and size stability at 573 K.Our findings may have implications for not only fundamental studies about quasicrystals,but also microstructural manipulation of high-performance Mg alloys.
基金supported by the National Natural Science Foundation of China(52203364,52188101,52020105010)the National Key R&D Program of China(2021YFB3800300,2022YFB3803400)+2 种基金the Strategic Priority Research Program of Chinese Academy of Science(XDA22010602)the China Postdoctoral Science Foundation(2022M713214)the China National Postdoctoral Program for Innovative Talents(BX2021321)。
文摘Metal-ion batteries(MIBs),including alkali metal-ion(Li^(+),Na^(+),and K^(3)),multi-valent metal-ion(Zn^(2+),Mg^(2+),and Al^(3+)),metal-air,and metal-sulfur batteries,play an indispensable role in electrochemical energy storage.However,the performance of MIBs is significantly influenced by numerous variables,resulting in multi-dimensional and long-term challenges in the field of battery research and performance enhancement.Machine learning(ML),with its capability to solve intricate tasks and perform robust data processing,is now catalyzing a revolutionary transformation in the development of MIB materials and devices.In this review,we summarize the utilization of ML algorithms that have expedited research on MIBs over the past five years.We present an extensive overview of existing algorithms,elucidating their details,advantages,and limitations in various applications,which encompass electrode screening,material property prediction,electrolyte formulation design,electrode material characterization,manufacturing parameter optimization,and real-time battery status monitoring.Finally,we propose potential solutions and future directions for the application of ML in advancing MIB development.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.52371203 and 52271192)the Ministry of Science and Technology of China(Grant No.2021YFB3501201)。
文摘Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass was observed with typical spin glass behavior around 15.5 K.In addition,we find that the magnetic entropy change(-△S_(M))originates from the sample undergoing a ferromagnetic(FM)to paramagnetic(PM)transition around 20 K.Under a field change from 0 T to 7 T,the value of maximum magnetic entropy change(-△S_(M)^(max))reaches 12.5 J/kg·K,and the corresponding value of RC reaches 487.7 J/kg in the temperature range from 6 K to 60 K.The large RC and wide temperature range make the Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass be a promising material for application in magnetic refrigerators.
基金funded by National Natural Science Foundation of China,grant numbers 62335006,62274014,62235016,61734006,61835011,61991430was funded by Key Program of the Chinese Academy of Sciences,grant numbers XDB43000000,QYZDJSSWJSC027,and Beijing Municipal Science&Technology Commission,grant number Z221100002722018.
文摘We demonstrated a scheme of phase-locked terahertz quantum cascade lasers(THz QCLs)array,with a single-mode pulse power of 108 mW at 13 K.The device utilizes a Talbot cavity to achieve phase locking among five ridge lasers with first-order buried distributed feedback(DFB)grating,resulting in nearly five times amplification of the single-mode power.Due to the optimum length of Talbot cavity depends on wavelength,the combination of Talbot cavity with the DFB grating leads to better power amplification than the combination with multimode Fabry-Perot(F-P)cavities.The Talbot cavity facet reflects light back to the ridge array direction and achieves self-imaging in the array,enabling phase-locked operation of ridges.We set the spacing between adjacent elements to be 220μm,much larger than the free-space wavelength,ensuring the operation of the fundamental supermode throughout the laser's dynamic range and obtaining a high-brightness far-field distribution.This scheme provides a new approach for enhancing the single-mode power of THz QCLs.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.62074036,61674038,and 11574302)the Foreign Cooperation Project of Fujian Province,China(Grant No.2023I0005)+2 种基金the Open Research Fund Program of the State Key Laboratory of Low-Dimensional Quantum Physics(Grant No.KF202108)the National Key Research and Development Program of China(Grant No.2016YFB0402303)the Foundation of Fujian Provincial Department of Industry and Information Technology of China(Grant No.82318075)。
文摘Helicity-dependent photocurrent(HDPC)of the surface states in a high-quality topological insulator(Bi_(0.7)Sb_(0.3))_(2)Te_(3)nanoplate grown by chemical vapor deposition(CVD)is investigated.By investigating the angle-dependent HDPC,it is found that the HDPC is mainly contributed by the circular photogalvanic effect(CPGE)current when the incident plane is perpendicular to the connection of the two contacts,whereas the circular photon drag effect(CPDE)dominates the HDPC when the incident plane is parallel to the connection of the two contacts.In addition,the CPGE of the(Bi_(0.7)Sb_(0.3))_(2)Te_(3)nanoplate is regulated by temperature,light power,excitation wavelength,the source–drain and ionic liquid top-gate voltages,and the regulation mechanisms are discussed.It is demonstrated that(Bi_(0.7)Sb_(0.3))_(2)Te_(3)nanoplates may provide a good platform for novel opto-spintronics devices.
基金supported by the Natural Science Foundation of China(Grant Nos.22179093,21905202,and 51972312)the Natural Science Foundation of Liaoning Province,China(Grant No.2020-MS-003)+1 种基金the Australian Research Council through the Discovery Project(No.DP210102215)the Electron Microscopy Center in the University of Wollongong.The theoretical calculations performed in this work were carried out on TianHe-1(A)at the National Supercomputer Center in Tianjin.
文摘Hydrogen peroxide(H_(2)O_(2))production by the electrochemical 2-electron oxygen reduction reaction(2e−ORR)is a promising alternative to the energy-intensive anthraquinone process,and single-atom electrocatalysts show the unique capability of high selectivity toward 2e−ORR against the 4e−one.The extremely low surface density of the single-atom sites and the inflexibility in manipulating their geometric/electronic configurations,however,compromise the H_(2)O_(2) yield and impede further performance enhancement.Herein,we construct a family of multiatom catalysts(MACs),on which two or three single atoms are closely coordinated to form high-density active sites that are versatile in their atomic configurations for optimal adsorption of essential*OOH species.Among them,the Cox–Ni MAC presents excellent electrocatalytic performance for 2e−ORR,in terms of its exceptionally high H_(2)O_(2) yield in acidic electrolytes(28.96 mol L^(−1) gcat.^(−1) h^(−1))and high selectivity under acidic to neutral conditions in a wide potential region(>80%,0–0.7 V).Operando X-ray absorption and density functional theory analyses jointly unveil its unique trimetallic Co2NiN8 configuration,which efficiently induces an appropriate Ni–d orbital filling and modulates the*OOH adsorption,together boosting the electrocatalytic 2e−ORR capability.This work thus provides a new MAC strategy for tuning the geometric/electronic structure of active sites for 2e−ORR and other potential electrochemical processes.
基金Project supported by the National Key Research and Development Program of China(Grant Nos.2018YFE0204001,2018YFA0209103,2016YFB0400101,and 2016YFB0402303)the National Natural Science Foundation of China(Grant Nos.61627822,61704121,61991430,and 62074036)Postdoctoral Research Program of Jiangsu Province(Grant No.2021K599C).
文摘Optical reflection anisotropy microscopy mappings of micropipe defects on the surface of a 4H-SiC single crystal are studied by the scanning anisotropy microscopy(SAM)system.The reflection anisotropy(RA)image with a'butterfly pattern'is obtained around the micropipes by SAM.The RA image of the edge dislocations is theoretically simulated based on dislocation theory and the photoelastic principle.By comparing with the Raman spectrum,it is verified that the micropipes consist of edge dislocations.The different patterns of the RA images are due to the different orientations of the Burgers vectors.Besides,the strain distribution of the micropipes is also deduced.One can identify the dislocation type,the direction of the Burgers vector and the optical anisotropy from the RA image by using SAM.Therefore,SAM is an ideal tool to measure the optical anisotropy induced by the strain field around a defect.
基金financially supported by the National Natural Science Foundation of China (Nos. 51671127, 51631006, 51971168)sponsored by the Shanghai Rising-Star Programsupported by the United States Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract No. DE-AC02–06CH11357
文摘Mg-Y cast alloy shows excellent ductility(elongation to failure>15%)compared with pure Mg and commercial Mg cast alloys.By monitoring the microstructure evolution during an in situ tensile test of a Mg-2.5 wt%Y alloy,we identify the activation of prismatic<c>slip,which is rare in Mg.Synchrotron X-ray micro-beam Laue diffraction(μ-Laue)and transmission electron microscopy revealed the morphology of prismatic<c>slip bands and individual<c>dislocations.Density functional theory and molecular dynamics calculations indicate that solute Y can significantly reduce the stacking fault energy(SFE)along<c>direction on prismatic plane in Mg lattice and thus facilitate the nucleation of<c>dislocations during deformation.The presence of free<c>dislocations in the Mg lattice can also lead to nucleation of{10–12}twins even under unfavorable geometric conditions.
基金funding from the European Union's Horizon 2020 Research and Innovation Program(872102)P.S.thanks the Science Achievement Scholarship of Thailand(SAST)for her research secondment at The University of Manchester.Y.J.thanks the National Natural Science Foundation of China(22378407)for funding.
文摘Compared to reforming reactions using hydrocarbons,ethanol steam reforming(ESR)is a sustainable alternative for hydrogen(H_(2))production since ethanol can be produced sustainably using biomass.This work explores the catalyst design strategies for preparing the Ni supported on ZSM-5 zeolite catalysts to promote ESR.Specifically,two-dimensional ZSM-5 nanosheet and conventional ZSM-5 crystal were used as the catalyst carriers and two synthesis strategies,i.e.,in situ encapsulation and wet impregnation method,were employed to prepare the catalysts.Based on the comparative characterization of the catalysts and comparative catalytic assessments,it was found that the combination of the in situ encapsulation synthesis and the ZSM-5 nanosheet carrier was the effective strategy to develop catalysts for promoting H_(2) production via ESR due to the improved mass transfer(through the 2-D structure of ZSM-5 nanosheet)and formation of confined small Ni nanoparticles(resulted via the in situ encapsulation synthesis).In addition,the resulting ZSM-5 nanosheet supported Ni catalyst also showed high Ni dispersion and high accessibility to Ni sites by the reactants,being able to improve the activity and stability of catalysts and suppress metal sintering and coking during ESR at high reaction temperatures.Thus,the Ni supported on ZSM-5 nanosheet catalyst prepared by encapsulation showed the stable performance with~88% ethanol conversion and~65% H_(2) yield achieved during a 48-h longevity test at 550-C.
基金supported by the National Natural Science Foundation of China (Grant No. 52272265)the National Key R&D Program of China (Grant Nos. 2023YFA1607400 and 2018YFA0704300)+4 种基金the support from the National Natural Science Foundation of China (Grant Nos. 52271016 and 52188101)the support from Analytical Instrumentation Center (# SPST-AIC10112914), SPST, Shanghai Tech Universitythe European Research Council (ERC Advanced Grant No. 742068 ‘TOPMAT’)the DFG through SFB 1143 (Project ID 247310070)the Würzburg-Dresden Cluster of Excellence on Complexity and Topology in Quantum Matter ct.qmat (EXC2147,Project ID 390858490)。
文摘Recently, giant intrinsic anomalous Hall effect(AHE) has been observed in the materials with kagome lattice.Here, we systematically investigate the influence of high pressure on the AHE in the ferromagnet LiMn_(6)Sn_(6) with clean Mn kagome lattice. Our in situ high-pressure Raman spectroscopy indicates that the crystal structure of LiMn_(6)Sn_(6) maintains a hexagonal phase under high pressures up to 8.51 GPa. The anomalous Hall conductivity(AHC) σ_(xy)^(A) remains around 150 Ω^(-1)·cm^(-1), dominated by the intrinsic mechanism. Combined with theoretical calculations, our results indicate that the stable AHE under pressure in Li Mn_(6)Sn_(6) originates from the robust electronic and magnetic structure.
基金the financial support by MOST (2011CBA00504)NSFC (21133010, 50921004, 212111074) of China
文摘Nanocarbon materials play a critical role in the development of new or improved technologies and devices for sustainable production and use of renewable energy. This perspective paper defines some of the trends and outlooks in this exciting area, with the effort of evidencing some of the possibilities offered from the growing level of knowledge, as testified from the exponentially rising number of publications, and putting bases for a more rational design of these nanomaterials. The basic members of the new carbon family are fullerene, graphene, and carbon nanotube. Derived from them are carbon quantum dots, nanohorn, nanofiber, nano ribbon, nanocapsulate, nanocage and other nanomorphologies. Second generation nanocarbons are those which have been modified by surface functionalization or doping with heteroatoms to create specific tailored properties. The third generation of nanocarbons is the nanoarchitectured supramolecular hybrids or composites of the first and second genera- tion nanocarbons, or with organic or inorganic species. The advantages of the new carbon materials, relating to the field of sustainable energy, are discussed, evidencing the unique properties that they offer for developing next generation solar devices and energy storage solutions.
基金supported by the Fundamental Research Funds for the Central Universities (No 30919011410)。
文摘CoMn layered double hydroxides(CoMn-LDH)are promising electrode materials for supercapacitors because of their excellent cyclic stability.However,they possess relatively low capacitances.In this work,hybrid CoMn-LDH@MnO2 products grown on Ni foams were obtained through a facile hydrothermal method.The as-synthesized samples employed as electrodes deliver a specific capacitance of 2325.01 F g^-1 at 1 A g^-1.An assembled asymmetric supercapacitor using these products as positive electrodes shows a maximum energy density of 59.73 W h kg^-1 at 1000.09 W kg^-1.The prominent electrochemical performance of the as-prepared electrodes could be attributes to hierarchical structures.These findings suggest that hybrid structures might be potential alternatives for future flexible energy storage devices.
基金supported by the National Natural Science Foundation of China (No. 51001098)the Institute of Metal Research of CAS (No. 09NBA211A1)
文摘Vanadium pentoxide (V205) exhibits high theoretical capacities when used as a cathode in lithium ion batteries (LIBs), but its application is limited by its structural instability as well as its low lithium and electronic conductivities. A porous composite of V2Os-SnO2/carbon nanotubes (CNTs) was prepared by a hydrothermal method and followed by thermal treatment. The small particles of V205, their porous structure and the coexistence of SnO2 and CNTs can all facilitate the diffusion rates of the electrons and lithium ions. Electrochemical impedance spectra indicated higher ionic and electric conductivities, as compared to commercial V205. The VzOs-SnOz/CNTs composite gave a reversible discharge capacity of 198 mAh.g- 1 at the voltage range of 2.05-4.0 V, measured at a current rate of 200 mA.g-1, while that of the commercial V205 was only 88 mAh.g-1, demonstrating that the porous V2Os-SnOz/CNTs composite is a promising candidate for high-performance lithium secondary batteries.
基金financially supported by the National Natural Science Foundation of China(NSFC)under Gtrant No.50401019the“Hun-dred of Talent Project"by Chinese Academy of Sciences+1 种基金National Outstanding Young Scientist Foundation for Z.F.Zhang under Grant No.50625103the financial support of the Alexander-von-Humboldt(AvH)Foundation.
文摘The deformation, damage, fracture, plasticity and melting phenomenon induced by shear fracture were investigated and summarized for Zr-, Cu-, Ti- and Mg-based bulk metallic glasses (BMGs) and their composites. The shear fracture angles of these BMG materials often display obvious differences under compression and tension, and follow either the Mohr-Coulomb criterion or the unified tensile fracture criterion. The compressive plasticity of the composites is always higher than the tensile plasticity, leading to a significant inconsistency. The enhanced plasticity of BMG composites containing ductile dendrites compared to monolithic glasses strongly depends on the details of the microstructure of the composites. A deformation and damage mechanism of pseudo-plasticity, related to local cracking, is proposed to explain the inconsistency of plastic deformation under tension and compression. Besides, significant melting on the shear fracture surfaces was observed. It is suggested that melting is a common phenomenon in these materials with high strength and high elastic energy, as it is typical for BMGs and their composites failing under shear fracture. The melting mechanism can be explained by a combined effect of a significant temperature rise in the shear bands and the instantaneous release of the large amount of elastic energy stored in the material.
基金Rachadapisek Sompoch project,Chulalongkorn University(CU_GR_62_14_62_02)the Energy Conservation and Promotion Fund Office,Ministry of Energy+2 种基金the NSFC(grant 51421091)National Science Foundation for Distinguished Young Scholars for Hebei Province of China(grant E2016203376)Asahi Glass Foundation。
文摘Nickel/cobalt-layered double hydroxides(Ni Co-LDH) have been attracted increasing interest in the applications of anode materials for lithium ion battery(LIB), but the low cycle stability and rate performance are still limited its practice applications. To achieve high performance LIB, the surface-confined strategy has been applied to design and fabricate a new anode material of NiCo-LDH nanosheet anchored on the surface of Ti3C2 MXene(Ni Co-LDH/Ti3C2). The ultra-thin, bended and wrinkled α-phase crystal with an interlayer spacing of 8.1 ? can arrange on the conductive substrates Ti3C2 MXene directly, resulting in high electrolyte diffusion ability and low internal resistance. Furthermore, chemical bond interactions between the highly conductive Ti3C2 MXene and Ni Co-LDH nanosheets can greatly increase the ion and electron transport and reduce the volume expansion of NiCo-LDH during Li ion intercalation. As expected,the discharge capacity of 562 m Ah g-1 at 5.0 A g-1 for 800 cycles without degradation can be achieved,rate capability and cycle performance are better than that of NiCo-LDH(~100 mAh g-1). Furthermore, the density function theory(DFT) calculations were performed to demonstrate that Ni Co-LDH/Ti3C2 system can be used as a highly desirable and promising anode material for lithium ion battery.
基金This study was supported by the Natural Science Foundation of China(No.51072130,51502045,and 21905202)Innovative Research in the University of Tianjin(TD13‐5077)+2 种基金Developed and Applied Funding of Tianjin Normal University(135202XK1702)the Australian Research Council(ARC)through the Discovery Project(No.DP200100365)Discovery Early Career Researcher Award(DECRA,DE170100871)program.
文摘As a clean and renewable energy source,solar energy is a competitive alternative to replace conventional fossil fuels.Nevertheless,its serious fluctuating nature usually leads to a poor alignment with the actual energy demand.To solve this problem,the direct solar-to-electrochemical energy conversion and storage have been regarded as a feasible strategy.In this context,the development of high-performance integrated devices based on solar energy conversion parts(i.e.,solar cells or photoelectrodes)and electrochemical energy storage units(i.e.,rechargeable batteries or supercapacitors[SCs])has become increasingly necessary and urgent,in which carbon and carbon-based functional materials play a fundamental role in determining their energy conversion/storage performances.Herein,we summarize the latest progress on these integrated devices for solar electricity energy conversion and storage,with special emphasis on the critical role of carbon-based functional materials.First,principles of integrated devices are introduced,especially roles of carbon-based materials in these hybrid energy devices.Then,two major types of important integrated devices,including photovoltaic and photoelectrochemicalrechargeable batteries or SCs,are discussed in detail.Finally,key challenges and opportunities in the future development are also discussed.By this review,we hope to pave an avenue toward the development of stable and efficient devices for solar energy conversion and storage.
文摘Lithium intercalation into graphite contributes a theoretical capacity of 372 m Ah g-1and thus leads to an earthshaking change for energy storage[1].Lithium intercalation behaviors have been investigated via X-ray diffraction(XRD),Raman,Fourier transform infrared spectroscopy(FTIR)and X-ray absorption fine structure (XAFS)with the aid of in-situ electrochemical characterization technologies.
基金supported by the National Key Technology R&D Program (Grant No. 2018YFA0209001)Frontier Science Research Project of CAS (Grant No. QYZDY-SSWJSC021)
文摘Silicon-based photonic integration has attracted the interest of semiconductor scientists because it has high luminous efficiency and electron mobility.Breakthroughs have been made in silicon-based integrated lasers over the past few decades.Here we review three main methods of integration ofⅢ–Ⅴ materials on Si,namely direct growth,bonding,and selectivearea hetero-epitaxy.TheⅢ–Ⅴmaterials we introduced mainly include materials such as GaAs and InP.The lasers are mainly lasers of related communication bands.We also introduced the advantages and challenges of the three methods.