Hydrogen absorption and desorption characteristics for high coercivity NdDyFeCoNbCuB sintered bulk magnets were studied, by differential scanning calorimetry （DSC） measurement and hydrogenation kinetics measurement....Hydrogen absorption and desorption characteristics for high coercivity NdDyFeCoNbCuB sintered bulk magnets were studied, by differential scanning calorimetry （DSC） measurement and hydrogenation kinetics measurement. The DSC measurements showed that hydrogenation of Nd-rich phase occurred in the temperature range of 40-185 ℃, hydrogenation of the tetragonal （Ф） phase in the temperature range of 185-220 ℃, as well as the disproportionation of the Ф phase that occurred in a broad temperature range from around 500 to 800 ℃. The hydrogenation kinetics measurements indicated that hydrogen absorption of the bulk magnets at 50 ℃ absorbed more hydrogen than at 150 ℃, although this procedure was slower at 50 ℃ than at 150℃. This phenomenon was discussed by means of pressure-concentration-temperature （p-c-T） diagrams.展开更多
Anisotropic powder was prepared with precursor （NdDy）-（FeCoNbCu）-B sintered magnets by hydrogen decrepitation, desorption, and subsequent annealing treatment. The hydrogen desorption was performed in magnetic fiel...Anisotropic powder was prepared with precursor （NdDy）-（FeCoNbCu）-B sintered magnets by hydrogen decrepitation, desorption, and subsequent annealing treatment. The hydrogen desorption was performed in magnetic fields of 0, 1, 3, and 5 T. The orientation of tetragonal phase grains of the powder was evaluated from the hysteresis loops measured by extraction magnetometer. Residual hydrogen content of the powder was evaluated by thermal-magnetic analysis. The powder with Hcj, Br, and （BH）max of 1138 kA.m^-1, 1.029 T, and 172.5 kJ.m^-3, respectively, was achieved under the condition of the magnetic field of 3 T. Magnetic properties of the powder, especially, the remanence of the powder, are enhanced upon magnetic fields, which is due to better orientation of powder particles and less residual hydrogen in the powder resulted from the magnetic field during the hydrogen desorption process.展开更多
文摘Hydrogen absorption and desorption characteristics for high coercivity NdDyFeCoNbCuB sintered bulk magnets were studied, by differential scanning calorimetry （DSC） measurement and hydrogenation kinetics measurement. The DSC measurements showed that hydrogenation of Nd-rich phase occurred in the temperature range of 40-185 ℃, hydrogenation of the tetragonal （Ф） phase in the temperature range of 185-220 ℃, as well as the disproportionation of the Ф phase that occurred in a broad temperature range from around 500 to 800 ℃. The hydrogenation kinetics measurements indicated that hydrogen absorption of the bulk magnets at 50 ℃ absorbed more hydrogen than at 150 ℃, although this procedure was slower at 50 ℃ than at 150℃. This phenomenon was discussed by means of pressure-concentration-temperature （p-c-T） diagrams.
基金the French Embassy in Beijing for provision of a collaborative research grant as part of a co-research program under the frame of LIA-LAS2M between Northwestern Polytechnic University-Xi'an,China and CNRS-Grenoble,France
文摘Anisotropic powder was prepared with precursor （NdDy）-（FeCoNbCu）-B sintered magnets by hydrogen decrepitation, desorption, and subsequent annealing treatment. The hydrogen desorption was performed in magnetic fields of 0, 1, 3, and 5 T. The orientation of tetragonal phase grains of the powder was evaluated from the hysteresis loops measured by extraction magnetometer. Residual hydrogen content of the powder was evaluated by thermal-magnetic analysis. The powder with Hcj, Br, and （BH）max of 1138 kA.m^-1, 1.029 T, and 172.5 kJ.m^-3, respectively, was achieved under the condition of the magnetic field of 3 T. Magnetic properties of the powder, especially, the remanence of the powder, are enhanced upon magnetic fields, which is due to better orientation of powder particles and less residual hydrogen in the powder resulted from the magnetic field during the hydrogen desorption process.