The high-pressure polymorphs and structural transformation of Sn were experimentally investigated using angle- dispersive synchrotron x-ray diffraction up to 108.9 GPa. The results show that at least at 12.8 GPa β-Sn...The high-pressure polymorphs and structural transformation of Sn were experimentally investigated using angle- dispersive synchrotron x-ray diffraction up to 108.9 GPa. The results show that at least at 12.8 GPa β-Sn→bct structure transformation was completed and no two-phase coexistence was found. By using a long-wavelength x-ray, we resolved the diffraction peaks splitting and discovered the formation of a new distorted orthorhombic structure bco from the bct structure at 31.8 GPa. The variation of the lattice parameters and their ratios with pressure further validate the observation of the bco polymorph. The bcc structure appears at 40.9 GPa and coexists with the bco phase throughout a wide pressure range of 40.9 GPa-73.1 GPa. Above 73.1 GPa, only the bcc polymorph is observed, The systematically experimental investigation confirms the phase transition sequence of Sn asβ-Sn→bct→bco→bco ＋ bcc→bcc upon compression to 108.9 GPa at room temperature.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.11304294 and 11274281)the Science Fund from the National Laboratory of Shock Wave and Detonation Physics of China(Grant Nos.9140C670201140C67281 and 9140C670102150C67288)
文摘The high-pressure polymorphs and structural transformation of Sn were experimentally investigated using angle- dispersive synchrotron x-ray diffraction up to 108.9 GPa. The results show that at least at 12.8 GPa β-Sn→bct structure transformation was completed and no two-phase coexistence was found. By using a long-wavelength x-ray, we resolved the diffraction peaks splitting and discovered the formation of a new distorted orthorhombic structure bco from the bct structure at 31.8 GPa. The variation of the lattice parameters and their ratios with pressure further validate the observation of the bco polymorph. The bcc structure appears at 40.9 GPa and coexists with the bco phase throughout a wide pressure range of 40.9 GPa-73.1 GPa. Above 73.1 GPa, only the bcc polymorph is observed, The systematically experimental investigation confirms the phase transition sequence of Sn asβ-Sn→bct→bco→bco ＋ bcc→bcc upon compression to 108.9 GPa at room temperature.