Perovskite PZT variants were synthesized from stoichiometric oxide ratios of Pb, Zr, Ti, Cr, Ni and Sb. The oxide powders were mixed mechanically and calcinated, and then sintered to form the desired perovskite phase....Perovskite PZT variants were synthesized from stoichiometric oxide ratios of Pb, Zr, Ti, Cr, Ni and Sb. The oxide powders were mixed mechanically and calcinated, and then sintered to form the desired perovskite phase. The detailed structural and ferroelectric properties were carried out for sintered specimens. The results of X-ray diffraction showed that all the ceramics specimens have a perovskite phase. The multi-component ceramic system consists of the (0.80?- x)Pb(Cr1/5,Ni1/5,Sb3/5)O3-xPbTiO3-0.20PbZrO3 (PZT-CNS), with 0.30 ≤ x ≤ 0.42, and the ternary system near the rhombohedral/tetragonal morphotropic phase boundary(MPB) was investigated by X-ray diffraction and dielectric properties. In the present system, the MPB that coexists with the tetragonal and rhombohedral phases is a narrow composition region of x = 0.38 - 0.42. The scanning Electron Microscopy (SEM) showed an increase of the mean grain size when the sintering temperature was increased. A sintered density of 92.93% of the theoretical density was obtained for Ti = 42% after sintering at 1180°C. Ceramics sintered at 1180°C with Ti = 42% achieve excellent dielectric properties, which are as follows εr = 4262.48, and Tc = 340°C.展开更多
Bismuth (Bi) and lanthanum (La) doped lead manganese antimoine zirconate titanate (PZMST) ceramic powders have been synthesized by high temperature solid-state reaction method. Preliminary X-ray structural analysis of...Bismuth (Bi) and lanthanum (La) doped lead manganese antimoine zirconate titanate (PZMST) ceramic powders have been synthesized by high temperature solid-state reaction method. Preliminary X-ray structural analysis of the compounds shows the formation of tetragonal structure. Scanning electron micrographs (SEM) shows a uniform grain distribution and grain size of the order of ~2.28 μm. Detailed dielectric studies of the Pb0.95(La1-z Biz)0.05[(Zr0.6Ti0.4)0.95(Mn1/3Sb2/3)0.05]O3 samples as a function of the temperature (from 25°C to 450°C) at frequency 1 kHz suggest that the compounds undergo a diffuse phase transition. The transition temperature shifts increase with increasing the Bi ratio. Diffusivity (γ) study of phase transition of these compounds provided its value from 1.59 to 1.78 indicating the degree of the disordering in the system.展开更多
文摘Perovskite PZT variants were synthesized from stoichiometric oxide ratios of Pb, Zr, Ti, Cr, Ni and Sb. The oxide powders were mixed mechanically and calcinated, and then sintered to form the desired perovskite phase. The detailed structural and ferroelectric properties were carried out for sintered specimens. The results of X-ray diffraction showed that all the ceramics specimens have a perovskite phase. The multi-component ceramic system consists of the (0.80?- x)Pb(Cr1/5,Ni1/5,Sb3/5)O3-xPbTiO3-0.20PbZrO3 (PZT-CNS), with 0.30 ≤ x ≤ 0.42, and the ternary system near the rhombohedral/tetragonal morphotropic phase boundary(MPB) was investigated by X-ray diffraction and dielectric properties. In the present system, the MPB that coexists with the tetragonal and rhombohedral phases is a narrow composition region of x = 0.38 - 0.42. The scanning Electron Microscopy (SEM) showed an increase of the mean grain size when the sintering temperature was increased. A sintered density of 92.93% of the theoretical density was obtained for Ti = 42% after sintering at 1180°C. Ceramics sintered at 1180°C with Ti = 42% achieve excellent dielectric properties, which are as follows εr = 4262.48, and Tc = 340°C.
文摘Bismuth (Bi) and lanthanum (La) doped lead manganese antimoine zirconate titanate (PZMST) ceramic powders have been synthesized by high temperature solid-state reaction method. Preliminary X-ray structural analysis of the compounds shows the formation of tetragonal structure. Scanning electron micrographs (SEM) shows a uniform grain distribution and grain size of the order of ~2.28 μm. Detailed dielectric studies of the Pb0.95(La1-z Biz)0.05[(Zr0.6Ti0.4)0.95(Mn1/3Sb2/3)0.05]O3 samples as a function of the temperature (from 25°C to 450°C) at frequency 1 kHz suggest that the compounds undergo a diffuse phase transition. The transition temperature shifts increase with increasing the Bi ratio. Diffusivity (γ) study of phase transition of these compounds provided its value from 1.59 to 1.78 indicating the degree of the disordering in the system.
