The microstructure and mechanical properties of novel Al-Y-Sc alloys with high thermal stability and electrical conductivity were investigated.Eutectic Al3 Y-phase particles of size 100-200 nm were detected in the as-...The microstructure and mechanical properties of novel Al-Y-Sc alloys with high thermal stability and electrical conductivity were investigated.Eutectic Al3 Y-phase particles of size 100-200 nm were detected in the as-cast microstructure of the alloys.Al3 Y-phase particles provided a higher hardness to as cast alloys than homogenized alloys in the temperature range of 370-440℃.L12 precipitates of the Al3(ScxYy) phase were nucleated homogenously within the aluminium matrix and heterogeneously on the dislocations during annealing at 400℃.The average size of the L12 precipitates was 11±2 nm after annealing for 1 h,and 25-30 nm after annealing for 5 h,which led to a decrease in the hardness of the Al-0.2 Y-0.2 Sc alloy to15 HV.The recrystallization temperature exceeded 350℃and 450℃for the Al-0.2 Y-0.05 Sc and Al-0.2 Y-0.2 Sc alloys,respectively.The investigated alloys demonstrated good thermal stability of the hardness and tensile properties after annealing the rolled alloys at 200 and 300℃,due to fixing of the dislocations and grain boundaries by L12 precipitates and eutectic Al3 Y-phase particles.The good combination of strength,plasticity,and electrical conductivity of the investigated Al-0.2 Y-0.2 Sc alloys make it a promising candidate for electrical conductors.The alloys exhibited a yield stress of 177-183 MPa,ultimate tensile stress of 199-202 MPa,elongation of 15.2-15.8%,and electrical conductivity of 60.8%-61.5% IACS.展开更多
基金supported financially by the Russian Science Foundation(No.17-79-10256)。
文摘The microstructure and mechanical properties of novel Al-Y-Sc alloys with high thermal stability and electrical conductivity were investigated.Eutectic Al3 Y-phase particles of size 100-200 nm were detected in the as-cast microstructure of the alloys.Al3 Y-phase particles provided a higher hardness to as cast alloys than homogenized alloys in the temperature range of 370-440℃.L12 precipitates of the Al3(ScxYy) phase were nucleated homogenously within the aluminium matrix and heterogeneously on the dislocations during annealing at 400℃.The average size of the L12 precipitates was 11±2 nm after annealing for 1 h,and 25-30 nm after annealing for 5 h,which led to a decrease in the hardness of the Al-0.2 Y-0.2 Sc alloy to15 HV.The recrystallization temperature exceeded 350℃and 450℃for the Al-0.2 Y-0.05 Sc and Al-0.2 Y-0.2 Sc alloys,respectively.The investigated alloys demonstrated good thermal stability of the hardness and tensile properties after annealing the rolled alloys at 200 and 300℃,due to fixing of the dislocations and grain boundaries by L12 precipitates and eutectic Al3 Y-phase particles.The good combination of strength,plasticity,and electrical conductivity of the investigated Al-0.2 Y-0.2 Sc alloys make it a promising candidate for electrical conductors.The alloys exhibited a yield stress of 177-183 MPa,ultimate tensile stress of 199-202 MPa,elongation of 15.2-15.8%,and electrical conductivity of 60.8%-61.5% IACS.