The fracture toughness of carbon fiber reinforced epoxy composite(CFRP)was investigated through mode I and mode II shaped fracture system in this paper.A novel polyimide with trifluoromethyl groups and grafted nanosil...The fracture toughness of carbon fiber reinforced epoxy composite(CFRP)was investigated through mode I and mode II shaped fracture system in this paper.A novel polyimide with trifluoromethyl groups and grafted nanosilica were used to modify epoxy resin.Effect of modified resin and unmodified resin on fracture toughness of CFRP was compared and discussed.Lay-up angles and thicknesses effects on fracture toughness of composites were also investigated.The fracture toughness of CFRP was obtained through double cantilever beam(DCB)and end notched flexure(ENF)tests.The results showed that the composites prepared by modified resin exhibited high fracture toughness compared with unmodified composites.The fracture toughness value of mode I increased from 1.83 kJ/m2 to 4.55 kJ/m2.The fracture toughness value of mode II increased from 2.30 kJ/m2 to 6.47 kJ/m2.展开更多
A graphene oxide/nano-silica(GOS)hybrid was rapidly and easily synthesized using graphene oxide(GO)and nano-silica(nano-SiO_(2))as raw materials,and the synthesized GOS was used to improve the mechanical properties of...A graphene oxide/nano-silica(GOS)hybrid was rapidly and easily synthesized using graphene oxide(GO)and nano-silica(nano-SiO_(2))as raw materials,and the synthesized GOS was used to improve the mechanical properties of epoxy resin(EP).The modified EP with different mass fractions of GOS(0,0.1%,0.2%,0.3%and 0.4%)were prepared and studied.The structure,thermal stability,mechanical properties,fracture toughness and failure morphology of the modified EP were analyzed.The results showed that the tensile strength of GOS modified EP increased from 40.6 MPa to 80.2 MPa compared with EP,the critical stress intensity factor of GOS modified EP increased by 65.9%from 0.82 MPa·m^(1/2)to 1.36 MPa·m^(1/2),indicating a significant enhancement in fracture toughness.In addition,failure morphology was observed by scanning electron microscopy(SEM)observation.The toughness mechanism of the modified EP was also discussed.Finally,the thermal stability of the modified EP was improved by the addition of GOS.Compared with neat EP,the initial thermal degradation temperature and glass transition temperature of GOS modified EP increased by 4.5℃and 10.3℃,respectively.展开更多
基金National Natural Science Foundation of China(No.11802192)Natural Science Foundation of Jiangsu Province,China(No.BK20180244)Nantong Science and Technology Project,China(No.JC2019012)。
文摘The fracture toughness of carbon fiber reinforced epoxy composite(CFRP)was investigated through mode I and mode II shaped fracture system in this paper.A novel polyimide with trifluoromethyl groups and grafted nanosilica were used to modify epoxy resin.Effect of modified resin and unmodified resin on fracture toughness of CFRP was compared and discussed.Lay-up angles and thicknesses effects on fracture toughness of composites were also investigated.The fracture toughness of CFRP was obtained through double cantilever beam(DCB)and end notched flexure(ENF)tests.The results showed that the composites prepared by modified resin exhibited high fracture toughness compared with unmodified composites.The fracture toughness value of mode I increased from 1.83 kJ/m2 to 4.55 kJ/m2.The fracture toughness value of mode II increased from 2.30 kJ/m2 to 6.47 kJ/m2.
基金Natural Science Foundation of Jiangsu Province,China(No.BK 20180244)Foundation of Qing Lan Project,ChinaOpening Project of Key Laboratory of Jiangsu Province for Silk Engineering,Soochow University,China(No.KJS2278)。
文摘A graphene oxide/nano-silica(GOS)hybrid was rapidly and easily synthesized using graphene oxide(GO)and nano-silica(nano-SiO_(2))as raw materials,and the synthesized GOS was used to improve the mechanical properties of epoxy resin(EP).The modified EP with different mass fractions of GOS(0,0.1%,0.2%,0.3%and 0.4%)were prepared and studied.The structure,thermal stability,mechanical properties,fracture toughness and failure morphology of the modified EP were analyzed.The results showed that the tensile strength of GOS modified EP increased from 40.6 MPa to 80.2 MPa compared with EP,the critical stress intensity factor of GOS modified EP increased by 65.9%from 0.82 MPa·m^(1/2)to 1.36 MPa·m^(1/2),indicating a significant enhancement in fracture toughness.In addition,failure morphology was observed by scanning electron microscopy(SEM)observation.The toughness mechanism of the modified EP was also discussed.Finally,the thermal stability of the modified EP was improved by the addition of GOS.Compared with neat EP,the initial thermal degradation temperature and glass transition temperature of GOS modified EP increased by 4.5℃and 10.3℃,respectively.