The Ho：YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho：YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt i...The Ho：YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho：YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt intensity parameters Ω2 = 1.42 × 10^-20cm^2, Ω4 = 2.92 ×10^-20 cm^2, and Ω6 =1.71 ×10^-20cm^2, this paper calculated the fluorescence lifetime to be 6 ms for ^5I7→^5Is transition, and the integrated emission cross section to be 2.24 × 10^-18 cm^2. It investigates the room-temperature Ho：YAP laser end-pumped by a 1.91-μm Tm：YLF laser. The maximum output power was 4.1 W when the incident 1.91-μm pump power was 14.4W. The slope efficiency is 40.8%, corresponding to an optical-to-optical conversion efficiency of 28.4%. The Ho：YAP output wavelength was centred at 2118 nm with full width at half maximum of about 0.8nm.展开更多
This paper reports that the Tm^3＋：Lu2SiO5 （Tm：LSO） crystal is grown by Czochralski technique. The roomtemperature absorption spectra of Tm：LSO crystal are measured on a b-cut sample with 4 at.% thulium. Accordin...This paper reports that the Tm^3＋：Lu2SiO5 （Tm：LSO） crystal is grown by Czochralski technique. The roomtemperature absorption spectra of Tm：LSO crystal are measured on a b-cut sample with 4 at.% thulium. According to the obtained Judd-Ofelt intensity parameters Ω2=9.3155×10^-20 cm^2, Ω4=8.4103×10^-20 cm^2, Ω6=1.5908×10^-20 cm^2, the fluorescence lifetime is calculated to be 2.03 ms for ^3F4 → ^3H6 transition, and the integrated emission cross section is 5.81×10^-18 cm^2. Room-temperature laser action near 2μm under diode pumping is experimentally evaluated in Tm：LSO. An optical-optical conversion efficiency of 9.1% and a slope efficiency of 16.2% are obtained with continuouswave maximum output power of 0.67 W. The emission wavelengths of Tm：LSO laser are centred around 2.06μm with spectral bandwidth of -13.6 nm.展开更多
基金supported by the Program of Excellent Team in Harbin Institute of Technology of China
文摘The Ho：YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho：YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt intensity parameters Ω2 = 1.42 × 10^-20cm^2, Ω4 = 2.92 ×10^-20 cm^2, and Ω6 =1.71 ×10^-20cm^2, this paper calculated the fluorescence lifetime to be 6 ms for ^5I7→^5Is transition, and the integrated emission cross section to be 2.24 × 10^-18 cm^2. It investigates the room-temperature Ho：YAP laser end-pumped by a 1.91-μm Tm：YLF laser. The maximum output power was 4.1 W when the incident 1.91-μm pump power was 14.4W. The slope efficiency is 40.8%, corresponding to an optical-to-optical conversion efficiency of 28.4%. The Ho：YAP output wavelength was centred at 2118 nm with full width at half maximum of about 0.8nm.
基金Project supported by the Program of Excellent Team in Harbin Institute of Technology, China (Grant No 60878011)
文摘This paper reports that the Tm^3＋：Lu2SiO5 （Tm：LSO） crystal is grown by Czochralski technique. The roomtemperature absorption spectra of Tm：LSO crystal are measured on a b-cut sample with 4 at.% thulium. According to the obtained Judd-Ofelt intensity parameters Ω2=9.3155×10^-20 cm^2, Ω4=8.4103×10^-20 cm^2, Ω6=1.5908×10^-20 cm^2, the fluorescence lifetime is calculated to be 2.03 ms for ^3F4 → ^3H6 transition, and the integrated emission cross section is 5.81×10^-18 cm^2. Room-temperature laser action near 2μm under diode pumping is experimentally evaluated in Tm：LSO. An optical-optical conversion efficiency of 9.1% and a slope efficiency of 16.2% are obtained with continuouswave maximum output power of 0.67 W. The emission wavelengths of Tm：LSO laser are centred around 2.06μm with spectral bandwidth of -13.6 nm.