In order to effectively improve the corrosion resistance of aluminum alloys, anodic oxidation technique was used to generate the oxide film. We investigated the influences of two inorganic corrosion inhibitors(ammoniu...In order to effectively improve the corrosion resistance of aluminum alloys, anodic oxidation technique was used to generate the oxide film. We investigated the influences of two inorganic corrosion inhibitors(ammonium dihydrogen phosphate and sodium molybdate) on the corrosion resistance of anodic oxidation films on 2024 aluminum alloy, and studied the synergistic effect of two corrosion inhibitors. The corrosion resistance of anodic oxidation film in 3.5 wt% NaCl solution was evaluated by electrochemical impedance spectroscopy(EIS) and potentiodynamic polarization curves. Results show that, after adding the single ammonium dihydrogen phosphate or sodium molybdate of 0.01 M to oxalic acid electrolyte, inhibition efficiencies of the anodized samples are 10% and 47%, respectively. However, in the presence of two inhibitors with the same concentration of 0.01 M, inhibition efficiency can be as high as 92%. Therefore, we observed the significantly synergistic corrosion inhibition effect of molybdate and phosphate ions for anodic oxidation film formed on 2024 aluminum alloy.展开更多
基金Funded by the General Program of Natural Science Foundation of Jiangsu Province of China(No.BK20171440)the Natural Science Foundation of Nanjing University of Posts and Telecommunications(NY218039)
文摘In order to effectively improve the corrosion resistance of aluminum alloys, anodic oxidation technique was used to generate the oxide film. We investigated the influences of two inorganic corrosion inhibitors(ammonium dihydrogen phosphate and sodium molybdate) on the corrosion resistance of anodic oxidation films on 2024 aluminum alloy, and studied the synergistic effect of two corrosion inhibitors. The corrosion resistance of anodic oxidation film in 3.5 wt% NaCl solution was evaluated by electrochemical impedance spectroscopy(EIS) and potentiodynamic polarization curves. Results show that, after adding the single ammonium dihydrogen phosphate or sodium molybdate of 0.01 M to oxalic acid electrolyte, inhibition efficiencies of the anodized samples are 10% and 47%, respectively. However, in the presence of two inhibitors with the same concentration of 0.01 M, inhibition efficiency can be as high as 92%. Therefore, we observed the significantly synergistic corrosion inhibition effect of molybdate and phosphate ions for anodic oxidation film formed on 2024 aluminum alloy.