The preparation of the single domain GBCO bulk with 25 mm in diameter in air was reported. In order to avoid the Gd ions substituted the Ba sites, different BaCuO2 contents was added into the precursor powders. Tc of ...The preparation of the single domain GBCO bulk with 25 mm in diameter in air was reported. In order to avoid the Gd ions substituted the Ba sites, different BaCuO2 contents was added into the precursor powders. Tc of the samples achieved 94.3 K. The magnetization hysteresis loops of the samples were measured at 77 K. It is shown that the irreverswas obtained.展开更多
文摘The preparation of the single domain GBCO bulk with 25 mm in diameter in air was reported. In order to avoid the Gd ions substituted the Ba sites, different BaCuO2 contents was added into the precursor powders. Tc of the samples achieved 94.3 K. The magnetization hysteresis loops of the samples were measured at 77 K. It is shown that the irreverswas obtained.