Supersonically sprayed self-aligne d rGO nanosheets and ZnO/ZnMn_(2)O_(4)nanowires for high-energy and high-power-density supercapacitors

Core-shell-type bimetallic oxide and carbon composites comprising zinc oxide(ZnO)nanospheres and zinc manganese oxide(ZnMn_(2)O_(4))nanowires were produced by a hydrothermal method,and supersoni-cally sprayed together with reduced graphene oxide(rGO)nanosheets onto Ni foil to fabricate flexible su-percapacitors.The supersonic impact facilitated the exfoliation of the rGO nanosheets,thereby increasing the surface area and adhesion of the composite particles to the substrate.The rGO nanosheets were vertically aligned during the supersonic impact and formed localized zones,enabling optimal accommodation of the ZnO/ZnMn_(2)O_(4)particles.This localization,with the addition of rGO,reduced the agglomeration of ZnO/ZnMn_(2)O_(4)particles.The molar concentration of MnSO_(4)used in the synthesis of ZnO/ZnMn_(2)O_(4)was varied from 0.05 to 0.15 mol/L to determine the optimal MnSO_(4)concentration that would result in the highest energy storage capacitance.The unique nanostructure of ZnO/ZnMn_(2)O_(4)and the self-alignment of rGO sheets facilitated a favorable environment for high energy storage capability with a specific capaci-tance of 276.3 mF·cm^(−2)at a current density of 0.5 mA·cm^(−2)and an energy density of 98.2μWh·cm^(−2)at a power density of 1600μW·cm^(−2).The width of the potential window was increased to 1.2 V,imply-ing a significant increase in the energy storage capability of the supercapacitor.Capacitance retention of 88%was achieved after 10,000 charge/discharge cycles for the supercapacitor fabricated using an optimal MnSO_(4)concentration(0.10 mol/L)during the composite synthesis.

Wearable sensors and supercapacitors using electroplated-Ni/ZnO antibacterial fabric

Herein,nickel nanocones and zinc oxide nanosheets were electroplated onto a fabric to produce multifunctional(wearable,stretchable,washable,hydrophobic,and antibacterial)materials with sensing,heating,and supercapacitive properties.All these functionalities are integrated into a one-layered fabric that can be used as a portable intelligent electronic textile for potential application in healthcare monitoring,smart sportswear,and energy storage.Electroplated nickel enhances the electrical conductivity and thus increases the electron charge transfer for supercapacitor applications.The integration of ZnO with the Ni-plated fabric provides pseudocapacitance via redox reactions with the electrolyte.The resistance of the Ni/ZnO fabric changes in response to external stimuli such as temperature and strain.When voltage is applied,the fabric generates heat through Joule heating,demonstrating its potential application as winter sportswear.The superior mechanical durability of the fabric was confirmed through bending and stretching tests.The hydrophobic surface prevents viruses contained in liquid droplets from infiltrating the fabric.In addition,bacterial growth is inhibited because of the antibacterial properties of the Ni/ZnO fabric and because of Joule heating.The one-layered fabric integrated with such multiple functionalities is expected to be applicable in the development of next-generation portable and wearable electronic textiles in various industries.