Delafossite AgFeO_(2)nanoparticles with a mixture of 2H and 3R phases were successfully fabricated by using a simple co-precipitation method.The resulting precursor was calcined at temperatures of 100,200,300,400,and ...Delafossite AgFeO_(2)nanoparticles with a mixture of 2H and 3R phases were successfully fabricated by using a simple co-precipitation method.The resulting precursor was calcined at temperatures of 100,200,300,400,and 500℃to obtain the delafossite AgFe0_(2)phase.The morphology and microstructure of the prepared AgFeO_(2)samples were characterized by using field emission scanning electron microscopy(FESEM),transmission electron microscopy(TEM),N_(2) adsorption/desorption,X-ray absorption spectroscopy(XAS),and Xray photoelectron spectroscopy(XPS)techniques.A three-electrode system was employed to investigate the electrochemical properties of the delafossite AgFeO_(2)nanoparticles in a 3 M KOH electrolyte.The delafossite AgFeO_(2)nanoparticles calcined at 100℃(AFO100)exhibited the highest surface area of 28.02 m^(2)·g^(-1)and outstanding electrochemical performance with specific capacitances of 229.71 F·g^(-1)at a current density of 1 A·g^(-1)and 358.32 F·g^(-1)at a scan rate of 2 mV·s^(-1).This sample also demonstrated the capacitance retention of 82.99% after 1000 charge/discharge cycles,along with superior specific power and specific energy values of 797.46 W·kg^(-1)and 72.74Wh·kg^(-1),respectively.These findings indicate that delafossite AgFeO_(2)has great potential as an electrode material for supercapacitor applications.展开更多
基金Suranaree University of Technology(SUT)Thailand Science,Research and Innovation(TSRI)National Science,Research and Innovation Fund(NSRF)(project cord.179314)。
文摘Delafossite AgFeO_(2)nanoparticles with a mixture of 2H and 3R phases were successfully fabricated by using a simple co-precipitation method.The resulting precursor was calcined at temperatures of 100,200,300,400,and 500℃to obtain the delafossite AgFe0_(2)phase.The morphology and microstructure of the prepared AgFeO_(2)samples were characterized by using field emission scanning electron microscopy(FESEM),transmission electron microscopy(TEM),N_(2) adsorption/desorption,X-ray absorption spectroscopy(XAS),and Xray photoelectron spectroscopy(XPS)techniques.A three-electrode system was employed to investigate the electrochemical properties of the delafossite AgFeO_(2)nanoparticles in a 3 M KOH electrolyte.The delafossite AgFeO_(2)nanoparticles calcined at 100℃(AFO100)exhibited the highest surface area of 28.02 m^(2)·g^(-1)and outstanding electrochemical performance with specific capacitances of 229.71 F·g^(-1)at a current density of 1 A·g^(-1)and 358.32 F·g^(-1)at a scan rate of 2 mV·s^(-1).This sample also demonstrated the capacitance retention of 82.99% after 1000 charge/discharge cycles,along with superior specific power and specific energy values of 797.46 W·kg^(-1)and 72.74Wh·kg^(-1),respectively.These findings indicate that delafossite AgFeO_(2)has great potential as an electrode material for supercapacitor applications.