A series of nitrogen-doped SrMoO_(4) with different Sr/N mole ratio (R=0,0.05,0.10,0.15,0.20,0.40,and 0.60) were synthesized using urea as the N source via the vapor-thermal method.The photocatalytic degradation abili...A series of nitrogen-doped SrMoO_(4) with different Sr/N mole ratio (R=0,0.05,0.10,0.15,0.20,0.40,and 0.60) were synthesized using urea as the N source via the vapor-thermal method.The photocatalytic degradation ability of all samples was evaluated using methylene blue (MB) as a target contaminant.The band gaps of N-doped samples are all higher than that of pristine ones,which is only 3.12 eV.BET specific surface area S_(BET) and pore volume are increased due to the N doping.And the greater increase of S_(BET),the faster the photodegradation speed of methylene blue on SrMoO_(4).More specifically,the degradation efficiency of MB is improved up to 87%in 100 min.展开更多
基金Funded by National Key Research and Development Program of China (No.2021YFA1600203)。
文摘A series of nitrogen-doped SrMoO_(4) with different Sr/N mole ratio (R=0,0.05,0.10,0.15,0.20,0.40,and 0.60) were synthesized using urea as the N source via the vapor-thermal method.The photocatalytic degradation ability of all samples was evaluated using methylene blue (MB) as a target contaminant.The band gaps of N-doped samples are all higher than that of pristine ones,which is only 3.12 eV.BET specific surface area S_(BET) and pore volume are increased due to the N doping.And the greater increase of S_(BET),the faster the photodegradation speed of methylene blue on SrMoO_(4).More specifically,the degradation efficiency of MB is improved up to 87%in 100 min.