Effect of solution concentration on the structures and corrosion inhibition behavior of γ-APS films fabricated on surface of low carbon steel was systematically studied by EIS, RA-IR, and AFM. The experimental result...Effect of solution concentration on the structures and corrosion inhibition behavior of γ-APS films fabricated on surface of low carbon steel was systematically studied by EIS, RA-IR, and AFM. The experimental results indicated that the impedance ofy-APS silane treated substratcs and the cross-linking degree of γ-APS films gradually increased with the increasing solution concentration. There was some noticeable transformation in molecular orientation and protective performance of y-APS films when solution concentration was above 10vo1%. High cross-linking degree and changes in molecular orientation generated γ-APS films with excellent protective performance and ordered arrangement.展开更多
The effects of Y_2O_3 adding methods (i.e.,co-precipitated and mixed) on the microstructure and properties of alumina-strengthened ytrria-stabilized tetragonal zirconia polycrystal (ASZ) were investigated. CYASZ and M...The effects of Y_2O_3 adding methods (i.e.,co-precipitated and mixed) on the microstructure and properties of alumina-strengthened ytrria-stabilized tetragonal zirconia polycrystal (ASZ) were investigated. CYASZ and MYASZ were made by different adding method of Y_2O_3,co-precipitated and mixed,respectively. The results show that CYASZ is of uniform microstructure with fine grain size,however,MYASZ is of inhomogeneous microstructure due to the inhomogeneous distribution of ytrria. Comparing with CYASZ,the density and the strength of MYASZ are decreased,but the toughness is changed only a little. Under sliding wear test,the wear resistance of CYASZ is better than that of MYASZ.展开更多
The effect of relative humidity on the corrosion-resisting property of fluorocarbon coating was investigated by water vapor transmission technique and electrochemical impedance spectroscopy technique. Measuremerits we...The effect of relative humidity on the corrosion-resisting property of fluorocarbon coating was investigated by water vapor transmission technique and electrochemical impedance spectroscopy technique. Measuremerits were carried out on samples, which were tested in an accelerated corrosion environment for the same time (300, 500, 800 and 1000 h ). The experimental results were obtained as follows: (i) The water absorption, coating resistance and corrosion rate of metal under the coating changed with relative humidity and aging time, the results obtained by EIS are good consistent with those by water vapor transmission technique ; ( ii ) when the subject investigated presented two time constant, the goodness of fit by EEC R ( C ( R ( CR ) ) ) was inferior to that by EEC R( C( R(QR) ) ), but the error of parameters acquired from the former was smaller, by which we could analyze the experiment result quantitatively. With the appearance of diffusion layer on the metal, the difference of metal capacitance was aggravated, the error of parameters acquired from EEC R( C( R( C(RW) ) ) )was bigger than that from EEC R( C( R( Q( RW) ) ) ) .展开更多
基金Funded by the National Natural Science Foundation of China(No.50801057)the Special Fund for Basic Scientific Research of Central Colleges,China University of Geosciences(Wuhan)(No.007-G1323521109)
文摘Effect of solution concentration on the structures and corrosion inhibition behavior of γ-APS films fabricated on surface of low carbon steel was systematically studied by EIS, RA-IR, and AFM. The experimental results indicated that the impedance ofy-APS silane treated substratcs and the cross-linking degree of γ-APS films gradually increased with the increasing solution concentration. There was some noticeable transformation in molecular orientation and protective performance of y-APS films when solution concentration was above 10vo1%. High cross-linking degree and changes in molecular orientation generated γ-APS films with excellent protective performance and ordered arrangement.
文摘The effects of Y_2O_3 adding methods (i.e.,co-precipitated and mixed) on the microstructure and properties of alumina-strengthened ytrria-stabilized tetragonal zirconia polycrystal (ASZ) were investigated. CYASZ and MYASZ were made by different adding method of Y_2O_3,co-precipitated and mixed,respectively. The results show that CYASZ is of uniform microstructure with fine grain size,however,MYASZ is of inhomogeneous microstructure due to the inhomogeneous distribution of ytrria. Comparing with CYASZ,the density and the strength of MYASZ are decreased,but the toughness is changed only a little. Under sliding wear test,the wear resistance of CYASZ is better than that of MYASZ.
文摘The effect of relative humidity on the corrosion-resisting property of fluorocarbon coating was investigated by water vapor transmission technique and electrochemical impedance spectroscopy technique. Measuremerits were carried out on samples, which were tested in an accelerated corrosion environment for the same time (300, 500, 800 and 1000 h ). The experimental results were obtained as follows: (i) The water absorption, coating resistance and corrosion rate of metal under the coating changed with relative humidity and aging time, the results obtained by EIS are good consistent with those by water vapor transmission technique ; ( ii ) when the subject investigated presented two time constant, the goodness of fit by EEC R ( C ( R ( CR ) ) ) was inferior to that by EEC R( C( R(QR) ) ), but the error of parameters acquired from the former was smaller, by which we could analyze the experiment result quantitatively. With the appearance of diffusion layer on the metal, the difference of metal capacitance was aggravated, the error of parameters acquired from EEC R( C( R( C(RW) ) ) )was bigger than that from EEC R( C( R( Q( RW) ) ) ) .