The coagulation process is a widely applied technology in water and wastewater treatment.Novel composite polyferric mag-nesium-silicate-sulfate(PFMS)coagulants were synthesized using Na_(2)SiO_(3)·9H_(2)O,Fe_(2)(...The coagulation process is a widely applied technology in water and wastewater treatment.Novel composite polyferric mag-nesium-silicate-sulfate(PFMS)coagulants were synthesized using Na_(2)SiO_(3)·9H_(2)O,Fe_(2)(SO_(4))_(3),and MgSO_(4) as raw materials in this paper.The effects of aging time,Fe:Si:Mg,and OH:M molar ratios(M represents the metal ions)on the coagulation performance of the as-pre-pared PFMS were systematically investigated to obtain optimum coagulants.The results showed that PFMS coagulant exhibited good co-agulation properties in the treatment of simulated humic acid-kaolin surface water and reactive dye wastewater.When the molar ratio was controlled at Fe:Si:Mg=2:2:1 and OH:M=0.32,the obtained PFMS presented excellent stability and a high coagulation efficiency.The removal efficiency of ultraviolet UV254 was 99.81%,and the residual turbidity of the surface water reached 0.56 NTU at a dosage of 30 mg·L^(-1).After standing the coagulant for 120 d in the laboratory,the removal efficiency of UV254 and residual turbidity of the surface wa-ter were 88.12%and 0.68 NTU,respectively,which accord with the surface water treatment requirements.In addition,the coagulation performance in the treatment of reactive dye wastewater was greatly improved by combining the advantages of magnesium and iron salts.Compared with polyferric silicate-sulfate(PFS)and polymagnesium silicate-sulfate(PMS),the PFMS coagulant played a better decolor-ization role within the pH range of 7-13.展开更多
Plastic instability,including both the discontinuous yielding and stress serrations,has been frequently observed during the tensile deformation of medium-Mn steels(MMnS)and has been intensively studied in recent years...Plastic instability,including both the discontinuous yielding and stress serrations,has been frequently observed during the tensile deformation of medium-Mn steels(MMnS)and has been intensively studied in recent years.Unfortunately,research results are controversial,and no consensus has been achieved regarding the topic.Here,we first summarize all the possible factors that affect the yielding and flow stress serrations in MMnS,including the morphology and stability of austenite,the feature of the phase interface,and the deformation parameters.Then,we propose a universal mechanism to explain the conflicting experimental results.We conclude that the discontinuous yielding can be attributed to the lack of mobile dislocation before deformation and the rapid dislocation multiplication at the beginning of plastic deformation.Meanwhile,the results show that the stress serrations are formed due to the pinning and depinning between dislocations and interstitial atoms in austenite.Strain-induced martensitic transformation,influenced by the mechanical stability of austenite grain and deformation parameters,should not be the intrinsic cause of plastic instability.However,it can intensify or weaken the discontinuous yielding and the stress serrations by affecting the mobility and density of dislocations,as well as the interaction between the interstitial atoms and dislocations in austenite grains.展开更多
In an effort to clarify the formation mechanism of LPSO structure in Mg-Y-Zn alloy,the chemical environment and structural ordering in liquid Mg-rich Mg-Y-Zn system are investigated with the aid of ab-initio molecular...In an effort to clarify the formation mechanism of LPSO structure in Mg-Y-Zn alloy,the chemical environment and structural ordering in liquid Mg-rich Mg-Y-Zn system are investigated with the aid of ab-initio molecular dynamics simulation.In liquid Mg-rich Mg-Y alloys,the strong Mg-Y interaction is determined,which promotes the formation of fivefold symmetric local structure.For Mg-Zn alloys,the weak Mg-Zn interaction results in the fivefold symmetry weakening in the liquid structure.Due to the coexistence of Y and Zn,the strong attractive interaction is introduced in liquid Mg-Y-Zn ternary alloy,and contributes to the clustering of Mg,Y,Zn launched from Zn.What is more,the distribution of local structures becomes closer to that in pure Mg compared with that in binary Mg-Y and Mg-Zn alloys.These results should relate to the origins of the Y/Zn segregation zone and close-packed stacking mode in LPSO structure,which provides a new insight into the formation mechanism of LPSO structure at atomic level.展开更多
This paper comprehensively introduces a new magnesium production technology the compound-vertical-retort technology, involving in the related fundamental researches, core equipment development, working flow, and techn...This paper comprehensively introduces a new magnesium production technology the compound-vertical-retort technology, involving in the related fundamental researches, core equipment development, working flow, and technical characteristics. Scale-up test and an annual1200-ton-magnesium demonstration-level test was conducted to confirm the rationality, reliability, and advancement of the equipment, system and process design. It is indicated that the new technology solved a series of problems of traditional silicothermic process including adhesion and glaze, short life of retort, low efficiency, high impurity of crystallized magnesium, large heat losses, and poor working environment,making a great technological breakthrough in this field. Representatively, the new well-designed ceramic-lined steel retort serves 2~3 times in life than the normal retorts. The magnesium yield per retort is improved 4~5 times, with purity of >99.8%. The energy consumption in reduction stage is reduced by more than 20%. The mechanical production is fully realized and operating environment is significantly improved.展开更多
In order to study the sintering characteristics of Ca-rich iron ore,chemical analysis,laser diffraction,scanning electron microscopy,XRD-Rietveld method,and micro-sintering were used to analyze the mineralogical prope...In order to study the sintering characteristics of Ca-rich iron ore,chemical analysis,laser diffraction,scanning electron microscopy,XRD-Rietveld method,and micro-sintering were used to analyze the mineralogical properties and sintering pot tests were used to study the sintering behavior.In addition,a grey correlation mathematical model was used to calculate and compare the comprehensive sintering performance under different calcium-rich iron ore contents.The results demonstrate that the Ca-rich iron ore has coarse grain size and strong self-fusing characteristics with Ca element in the form of calcite(CaCO_(3)) and the liquid phase produced by the self-fusing of the calcium-rich iron ore is well crystallized.Its application with a 20wt%content in sintering improves sinter productivity,reduces fuel consumption,enhances reduction index,and improves gas permeability in blast furnace by 0.45 t/(m^(2)·h),6.11 kg/t,6.17%,and 65.39 kPa·℃,respectively.The Ca-rich iron ore sintering can improve the calorific value of sintering flue gas compared with magnetite sintering,which is conducive to recovering heat for secondary use.As the content of the Ca-rich iron ore increases,sinter agglomeration shifts from localized liquid-phase bonding to a combination of localized liquid-phase bonding and iron oxide crystal connection.Based on an examination of the greater weight value of productivity with grey correlation analysis,the Ca-rich iron ore is beneficial for the comprehensive index of sintering in the range of 0-20wt%content.Therefore,it may be used in sintering with magnetite concentrates as the major ore species.展开更多
Electric arc furnace dust(EAFD)is a hazardous waste but can also be a potential secondary resource for valuable metals,such as Zn and Fe.Given the increased awareness of carbon emission reduction,energy conservation,a...Electric arc furnace dust(EAFD)is a hazardous waste but can also be a potential secondary resource for valuable metals,such as Zn and Fe.Given the increased awareness of carbon emission reduction,energy conservation,and environmental protection,hydrometallurgical technologies for the detoxification and resource use of EAFD have been developing rapidly.This work summarizes the generation mechanisms,compositions,and characteristics of EAFD and presents a critical review of various hydrometallurgical treatment methods for EAFD,e.g.,acid leaching,alkaline leaching,salt leaching,and pretreatment–enhanced leaching methods.Simultaneously,the phase transformation mechanisms of zinc-containing components in acid and alkali solutions and pretreatment processes are expounded.Finally,two novel combined methods,i.e.,oxygen pressure sulfuric acid leaching combined with composite catalyst preparation,and synergistic roasting of EAFD and municipal solid waste incineration fly ash combined with alkaline leaching,are proposed,which can provide future development directions to completely recycling EAFD by recovering valuable metals and using zinc residue.展开更多
Currently,the process of extracting rubidium from ores has attracted a great deal of attention due to the increasing application of rubidium in high-technology field.A novel process for the comprehensive utilization o...Currently,the process of extracting rubidium from ores has attracted a great deal of attention due to the increasing application of rubidium in high-technology field.A novel process for the comprehensive utilization of rubidium ore resources is proposed in this paper.The process consists mainly of mineral dissociation,selective leaching,and desilication.The results showed that the stable silicon–oxygen tetrahedral structure of the rubidium ore was completely disrupted by thermal activation and the mineral was completely dissociated,which was conducive to subsequent selective leaching.Under the optimal conditions,extractions of 98.67% Rb and 96.23%K were obtained by leaching the rubidium ore.Moreover,the addition of a certain amount of activated Al(OH)_(3) during leaching can effectively inhibit the leaching of silicon.In the meantime,the leach residue was sodalite,which was successfully synthesized to zeolite A by hydrothermal conversion.The proposed process provided a feasible strategy for the green extraction of rubidium and the sustainable utilization of various resources.展开更多
Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur ...Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur during continuous casting,which includes depression,longitudinal cracks,deep oscillation marks,and severe level fluctuation with slag entrapment.The high-efficiency production of hypo-peritectic steels by continuous casting is still a great challenge due to the limited understanding of the mechanism of peritectic solidification.This work reviews the definition and classification of hypo-peritectic steels and introduces the formation tendency of common surface defects related to peritectic solidification.New achievements in the mechanism of peritectic reaction and transformation have been listed.Finally,countermeasures to avoiding surface defects of hypo-peritectic steels duiring continuous casting are summarized.Enlightening certain points in the continuous casting of hypo-peritectic steels and the development of new techniques to overcome the present problems will be a great aid to researchers.展开更多
Platinum group metals(PGMs),especially Pd,Pt,and Rh,have drawn great attention due to their unique features.Direct separation of Pd and Pt from highly acidic automobile catalyst leach liquors is disturbed by various f...Platinum group metals(PGMs),especially Pd,Pt,and Rh,have drawn great attention due to their unique features.Direct separation of Pd and Pt from highly acidic automobile catalyst leach liquors is disturbed by various factors.This work investigates the effect of various parameters including the acidity,extractant concentration,phase ratio A/O,and diluents on the Pd and Pt extraction and their stripping behaviors.The results show that the Pd and Pt are successfully separated from simulated leach liquor of spent automobile catalysts with monothioCyanex 272 and trioctylamine(TOA).Monothio-Cyanex 272 shows strong extractability and specific selectivity for Pd,and only one single stage is needed to recover more than 99.9% of Pd,leaving behind all the Pt,Rh,and base metals of Fe,Mg,Ce,Ni,Cu,and Co in the raffinate.The loaded Pd is efficiently stripped by acidic thiourea solutions.TOA shows strong extractability for Pt and Fe at acidity of 6 mol·L^(–1) HCl.More than 99.9% of Pt and all of the Fe are extracted into the organic phase after two stages of countercurrent extraction.Diluted HCl easily scrubs the loaded base metals(Fe,Cu,and Co).The loaded Pt is efficiently stripped by 1.0 mol·L^(–1) thiourea and 0.05–0.1 mol·L^(–1) Na OH solutions.Monothio-Cyanex 272 and TOA can realize the separation of Pd and Pt from highly acidic leach liquor of spent automobile catalysts.展开更多
Copper-indium-gallium-diselenide(CIGS)is a fast-evolving commercial solar cell.The firm demand for global carbon reduction and the rise of potential environmental threats necessitate spent CIGS solar cell recycling.In...Copper-indium-gallium-diselenide(CIGS)is a fast-evolving commercial solar cell.The firm demand for global carbon reduction and the rise of potential environmental threats necessitate spent CIGS solar cell recycling.In this paper,the sources and characteristics of valuable metals in spent CIGS solar cells were reviewed.The potential environmental impacts of CIGS,including service life,critical material,and material toxicity,were outlined.The main recovery methods of valuable metals in the various types of spent CIGS,including hydrometallurgy,pyrometallurgy,and comprehensive treatment processes,were compared and discussed.The mechanism of different recovery processes was summarized.The challenges faced by different recycling processes of spent CIGS were also covered in this review.Finally,the economic viability of the recycling process was assessed.The purpose of this review is to provide reasonable suggestions for the sustainable development of CIGS and the harmless disposal of spent CIGS.展开更多
Chifeng is a concentrated mining area for non-ferrous metal minerals,as well as a key prevention and control area for heavyduty enterprises.This situation necessitates an efective ecological and human health risk asse...Chifeng is a concentrated mining area for non-ferrous metal minerals,as well as a key prevention and control area for heavyduty enterprises.This situation necessitates an efective ecological and human health risk assessment of heavy metal(loid)s driven by the wide distribution of metal ore processing,mining,and smelting factories in Hexigten Banner and Bairin Left Banner.We conducted surveys to assess the levels of heavy metal(loid)s(Cr,As,Pb,Cd,and Hg)in the topsoil and groundwater of the areas.The results indicated that the concentrations of As,Cd,and Pb in partial soil samples exceeded the environmental quality standards of Grade II.Based on contamination assessments,such as geoaccumulation indices and pollution indices,we inferred that Cd,Pb,and As were primary pollutants in topsoil.Potential ecological risks when considered as part of the average risk indices(RI)are up to 1626.40 and 2818.76,respectively,in the two areas.Comparative analysis revealed that Cd posed a very high potential ecological risk,followed by As.Moreover,the evaluation showed that the three exposure pathways of carcinogenic and non-carcinogenic risk followed a descending order:inhalation>ingestion>dermal contact,except for Pb.Arsenic in topsoil posed a potential non-carcinogenic risk to human health,while there were no adverse efects of As in groundwater.In addition,the average total carcinogenic risk for As in the two areas,as well as the risk of Pb in the topsoil of Bairin Left Banner and all the fve heavy metal(loid)s in groundwater,exceeded human tolerance.Pb–Zn mines caused higher human health risks.In addition,the tandem contamination of heavy metal(loid)s in soil and groundwater was not obvious.This research study provides a basis for pollution remediation to control heavy industry-induced ecological and health risks of heavy metal(loid)s.展开更多
Decarbonization is a critical issue for peaking CO_(2) emissions of energy-intensive industries,such as the iron and steel industry.The decarbonization options of China’s ironmaking and steelmaking sector were discus...Decarbonization is a critical issue for peaking CO_(2) emissions of energy-intensive industries,such as the iron and steel industry.The decarbonization options of China’s ironmaking and steelmaking sector were discussed based on a systematic three-dimensional low-carbon analysis from the aspects of resource utilization(Y),energy utilization(Q),and energy cleanliness which is evaluated by a process general emission factor(PGEF)on all the related processes,including the current blast furnace(BF)-basic oxygen furnace(BOF)integrated process and the specific sub-processes,as well as the electric arc furnace(EAF)process,typical direct reduction(DR)process,and smelting reduction(SR)process.The study indicates that the three-dimensional aspects,particularly the energy structure,should be comprehensively considered to quantitatively evaluate the decarbonization road map based on novel technologies or processes.Promoting scrap utilization(improvement of Y)and the substitution of carbon-based energy(improvement of PGEF)in particular is critical.In terms of process scale,promoting the development of the scrap-based EAF or DR-EAF process is highly encouraged because of their lower PGEF.The three-dimensional method is expected to extend to other processes or industries,such as the cement production and thermal electricity generation industries.展开更多
The low-reactivity mold flux with low SiO_(2)content is considered suitable for the continuous casting of high-aluminum steel since it can significantly reduce the reaction between Al in steel and SiO_(2)in mold flux....The low-reactivity mold flux with low SiO_(2)content is considered suitable for the continuous casting of high-aluminum steel since it can significantly reduce the reaction between Al in steel and SiO_(2)in mold flux.However,the traditional low-reactivity mold flux still presents some problems such as high viscosity and strong crystallization tendency.In this study,the co-addition of Li_(2)O and B_(2)O_(3)in CaO–Al_(2)O_(3)–10wt%Si O_(2)based low-reactivity mold flux was proposed to improve properties of mold flux for high-aluminum steel,and the effect of Li_(2)O replacing B_(2)O_(3)on properties of mold flux was investigated.The viscosity of the mold flux with 2wt%Li_(2)O and 6wt%B_(2)O_(3)reached a minimum value of 0.07 Pa·s.The break temperature and melting point showed a similar trend with the viscosity.Besides,the melt structure and precipitation of the crystalline phase were studied using Raman and X-ray diffraction spectra to better understand the evolution of viscosity.It demonstrated that with increasing Li_(2)O content in the mold flux from 0 to 6 wt%,the degree of polymerization of aluminate and the aluminosilicate network structure increased because of increasing Li+released by Li_(2)O,indicating the added Li_(2)O was preferentially associated with Al^(3+)as a charge compensator.The precipitation of LiAlO_(2)crystalline phase gradually increased with the replacement of B_(2)O_(3)by Li_(2)O.Therefore,Li_(2)O content should be controlled below 2wt%to avoid LiAlO_(2)precipitation,which was harmful to the continuous casting of highaluminum steels.展开更多
Huge quantities of zinc leaching residues(ZLRs) generated from zinc production are dumped continuously around the world and pose a potential environmental threat because of their considerable amounts of entrained heav...Huge quantities of zinc leaching residues(ZLRs) generated from zinc production are dumped continuously around the world and pose a potential environmental threat because of their considerable amounts of entrained heavy metals(mainly lead). Most ZLRs have not been properly treated and the valuable metals in them have not yet been effectively recovered. Herein, the deep cleaning of a ZLR and recovery of valuable metals via a hydrometallurgical route were investigated. The cleaning process consists of two essential stages: acid leaching followed by calcium chloride leaching. The optimum conditions for extracting zinc, copper, and indium by acid leaching were a sulfuric acid concentration of 200 g·L^(-1), a liquid/solid ratio of 4:1(m L/g), a leaching time of 2 h, and a temperature of 90°C. For lead and silver extractions, the optimum conditions were a calcium chloride concentration of 400 g·L^(-1), a pH value of 1.0, a leaching time of 1 h, and a temperature of 30°C. After calcium chloride leaching, silver and lead were extracted out and the lead was finally recovered as electrolytic lead by electrowinning. The anglesite phase, which poses the greatest potential environmental hazard, was removed from the ZLR after deep cleaning, thus reducing the cost of environmental management of ZLRs. The treatment of chlorine and spent electrolyte generated in the process was discussed.展开更多
Low-nickel matte was intensively characterized,and Ni,Cu,and Co were determined to exist mainly as(Fe,Ni)_9S_8 and Fe Ni_3,Cu_5FeS_4,and(Fe,Ni)_9S_8 and Fe_3O_4(in isomorphic form),respectively.The efficient and selec...Low-nickel matte was intensively characterized,and Ni,Cu,and Co were determined to exist mainly as(Fe,Ni)_9S_8 and Fe Ni_3,Cu_5FeS_4,and(Fe,Ni)_9S_8 and Fe_3O_4(in isomorphic form),respectively.The efficient and selective extraction of Ni,Cu,and Co from the low-nickel matte in an(NH_4)_2S_2O_8/NH_3·H_2O solution system was studied.The effects of(NH_4)_2S_2O_8 and NH_3·H_2O concentrations,leaching time,and leaching temperature on the metal extraction efficiency were systematically investigated.During the oxidative ammonia leaching process,the metal extraction efficiencies of Ni 81.07%,Cu 93.81%,and Co 71.74% were obtained under the optimal conditions.The relatively low leaching efficiency of Ni was mainly ascribed to Ni Fe alloy deactivation in ammonia solution.By introducing an acid pre-leaching process into the oxidative ammonia leaching process,we achieved the high extraction efficiencies of 98.03%,99.13%,and 85.60% for the valuable metals Ni,Cu,and Co,respectively,from the low-nickel matte.展开更多
Circulating fluidized bed fly ash(CFBFA)is a solid waste product from circulating fluidized bed(CFB)boilers in power plants,and the storage of CFBFA is increasingly become an environmental problem.Previous scholars ha...Circulating fluidized bed fly ash(CFBFA)is a solid waste product from circulating fluidized bed(CFB)boilers in power plants,and the storage of CFBFA is increasingly become an environmental problem.Previous scholars have made contributions to improve the resource utilization of CFBFA.Especially,ecological cement is prepared by CFBFA,which is more conducive to its large-scale utilization.In recent years,a lot of effort has been paid to improve the properties of ecological cement containing CFBFA.In this work,the physicochemical properties of CFBFA are introduced,and recent research progress on the mechanical,expansion,and rheological properties of CFBFA based ecological cement(CEC)is extensively reviewed.The problem of over-expansion of f-CaO is summarized,which limits the scale application of CFBFA in ecological cement.Hence,the challenge for f-CaO in CFBFA to compensate for cement volume shrinkage is proposed,which is beneficial to the utilization of CFBFA in ecological cement,and the reduction of CO_(2) emissions from the cement industry.In addition,the environmental performance,durability,and economy of CEC should be valued in future research,especially the environmental performance,because the CFBFA contains heavy metals,such as Cr,As,which may pollute groundwater.展开更多
In order to achieve higher efficient cohesion match of procedure and equipment between ironmaking and steelmaking interface, the theory of multi-dimensional material flow control was applied to analyze torpedo ladle-i...In order to achieve higher efficient cohesion match of procedure and equipment between ironmaking and steelmaking interface, the theory of multi-dimensional material flow control was applied to analyze torpedo ladle-iron ladle transportation process between blast furnace and basic oxygen furnace. Moreover, basic parameters of material flow were analyzed and optimized, such as time, temperature and material quantity. Based on operating principles of material flow, control methods were optimized, such as product organization mode, scheduling discipline and scheduling plan of hot metal ladle. Finally, the material flow control technology of ironmaking and steelmaking interface was integrated. Satisfactory effects are obtained after applying the technology in practice. The total turnover number of torpedo ladle decreases from 20 to 18, the hot metal temperature of 1# BF torpedo ladle decreases from 36 °C to 19.5 °C, the hot metal temperature of 2# BF torpedo ladle decreases from 36.6 °C to 19.8 °C, the temperature drop of desulfurization hot metal decreases by 4 °C, and the temperature drop of non-desulfurization hot metal decreases by 2.8 °C. Furthermore, the ironmaking and steelmaking interface system will realize high-efficiency control by using this control technology.展开更多
Layered oxide is a promising cathode material for sodium-ion batteries because of its high-capacity,high operating voltage,and simple synthesis.Cycling performance is an important criterion for evaluating the applicat...Layered oxide is a promising cathode material for sodium-ion batteries because of its high-capacity,high operating voltage,and simple synthesis.Cycling performance is an important criterion for evaluating the application prospects of batteries.However,facing challenges,including phase transitions,ambient stability,side reactions,and irreversible anionic oxygen activity,the cycling performance of layered oxide cathode materials still cannot meet the application requirements.Therefore,this review proposes several strategies to address these challenges.First,bulk doping is introduced from three aspects:cationic single doping,anionic single doping,and multi-ion doping.Second,homogeneous surface coating and concentration gradient modification are reviewed.In addition,methods such as mixed structure design,particle engineering,high-entropy material construction,and integrated modification are proposed.Finally,a summary and outlook provide a new horizon for developing and modifying layered oxide cathode materials.展开更多
In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitroge...In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitrogen atmosphere. The effects of reaction temperature, reaction time, and carbon content on the metallization and dezincification ratios of the composite briquettes were studied. The reduced com- posite briquettes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive spectroscopy (EDS). The results show that the gravity dust and converter sludge are combined into the composite briquettes and a reasonable combination not only improves the performance of the composite briquettes, but also leads to the reduction with no or little reductant and flux. As the re- action temperature is increased and the reaction time is extended, the metallization and dezincification ratios of the composite briquettes in- crease gradually. When the composite briquettes are roasted at 1300℃ for 30 rain, the metallization ratio and dezineification ratio reaches 91.35% and 99.25%, respectively, indicating that most of the iron oxide is reduced and the zinc is almost completely removed. The carbon content is observed to exert a lesser effect on the reduction process; as the C/O molar ratio increases, the metallization and dezincification ra- tios first increase and then decrease.展开更多
Nanostructured Fe-doped titanium dioxide was synthesized from titanium containing electric furnace molten slag (TCEFMS) by using an alkali fusion, followed by a hydrolyzation-acidolysis-cMcination route. The effects...Nanostructured Fe-doped titanium dioxide was synthesized from titanium containing electric furnace molten slag (TCEFMS) by using an alkali fusion, followed by a hydrolyzation-acidolysis-cMcination route. The effects of Mkali/slag mass ratio, calcinating temperature, calcinating time, and water/slag mass ratio on the extraction efficiency and purity of products were systematically studied in this paper. It is indicated that the best extraction efficiency of nanostructured Fe- doped titanium dioxide is 99.35%, when the molten slag is calcinated at 700℃ for 1 h with the mass ratio of alkali/molten slag of 1.5:1. The influence of alkali/slag mass ratio on the photocatalytic activity of final products was evaluated by the photodegradation of methyl blue under visible light irradiation. A maximum photodegradation efficiency of 88.12% over 30 min was achieved under the optimum conditions.展开更多
基金supported by the National Natural Science Foundation of China (No.U1810205).
文摘The coagulation process is a widely applied technology in water and wastewater treatment.Novel composite polyferric mag-nesium-silicate-sulfate(PFMS)coagulants were synthesized using Na_(2)SiO_(3)·9H_(2)O,Fe_(2)(SO_(4))_(3),and MgSO_(4) as raw materials in this paper.The effects of aging time,Fe:Si:Mg,and OH:M molar ratios(M represents the metal ions)on the coagulation performance of the as-pre-pared PFMS were systematically investigated to obtain optimum coagulants.The results showed that PFMS coagulant exhibited good co-agulation properties in the treatment of simulated humic acid-kaolin surface water and reactive dye wastewater.When the molar ratio was controlled at Fe:Si:Mg=2:2:1 and OH:M=0.32,the obtained PFMS presented excellent stability and a high coagulation efficiency.The removal efficiency of ultraviolet UV254 was 99.81%,and the residual turbidity of the surface water reached 0.56 NTU at a dosage of 30 mg·L^(-1).After standing the coagulant for 120 d in the laboratory,the removal efficiency of UV254 and residual turbidity of the surface wa-ter were 88.12%and 0.68 NTU,respectively,which accord with the surface water treatment requirements.In addition,the coagulation performance in the treatment of reactive dye wastewater was greatly improved by combining the advantages of magnesium and iron salts.Compared with polyferric silicate-sulfate(PFS)and polymagnesium silicate-sulfate(PMS),the PFMS coagulant played a better decolor-ization role within the pH range of 7-13.
基金support from the National Natural Science Foundation of China(Nos.51831002,51904028,and 52233018)the Beijing Municipal Natural Science Foundation(No.2242048)the Fundamental Research Funds for the Central Universities,China(No.FRF-EYIT-23-08).
文摘Plastic instability,including both the discontinuous yielding and stress serrations,has been frequently observed during the tensile deformation of medium-Mn steels(MMnS)and has been intensively studied in recent years.Unfortunately,research results are controversial,and no consensus has been achieved regarding the topic.Here,we first summarize all the possible factors that affect the yielding and flow stress serrations in MMnS,including the morphology and stability of austenite,the feature of the phase interface,and the deformation parameters.Then,we propose a universal mechanism to explain the conflicting experimental results.We conclude that the discontinuous yielding can be attributed to the lack of mobile dislocation before deformation and the rapid dislocation multiplication at the beginning of plastic deformation.Meanwhile,the results show that the stress serrations are formed due to the pinning and depinning between dislocations and interstitial atoms in austenite.Strain-induced martensitic transformation,influenced by the mechanical stability of austenite grain and deformation parameters,should not be the intrinsic cause of plastic instability.However,it can intensify or weaken the discontinuous yielding and the stress serrations by affecting the mobility and density of dislocations,as well as the interaction between the interstitial atoms and dislocations in austenite grains.
基金supported by National Natural Science Foundation of China,China(No.51901117,51801116)Youth Innovation and Technology Support Program of Shandong Provincial Colleges and Universities,China(No.2020KJA002)+2 种基金Youth Fund of Shandong Academy of Sciences,China(2020QN0021)Innovation Pilot Project for Fusion of Science,Education and Industry(International Cooperation)from Qilu University of Technology(Shandong Academy of Sciences),China(No.2020KJC-GH03)Several Policies on Promoting Collaborative Innovation and Industrialization of Achievements in Universities and Research Institutes,China(No.2019GXRC030)。
文摘In an effort to clarify the formation mechanism of LPSO structure in Mg-Y-Zn alloy,the chemical environment and structural ordering in liquid Mg-rich Mg-Y-Zn system are investigated with the aid of ab-initio molecular dynamics simulation.In liquid Mg-rich Mg-Y alloys,the strong Mg-Y interaction is determined,which promotes the formation of fivefold symmetric local structure.For Mg-Zn alloys,the weak Mg-Zn interaction results in the fivefold symmetry weakening in the liquid structure.Due to the coexistence of Y and Zn,the strong attractive interaction is introduced in liquid Mg-Y-Zn ternary alloy,and contributes to the clustering of Mg,Y,Zn launched from Zn.What is more,the distribution of local structures becomes closer to that in pure Mg compared with that in binary Mg-Y and Mg-Zn alloys.These results should relate to the origins of the Y/Zn segregation zone and close-packed stacking mode in LPSO structure,which provides a new insight into the formation mechanism of LPSO structure at atomic level.
基金the financial support from the Zhengzhou Collaborative Innovation Major Funding (18XTZX12010)National Key Research and Development Project (2016YFB0301101)Baosteel Metals Co.,Ltd.
文摘This paper comprehensively introduces a new magnesium production technology the compound-vertical-retort technology, involving in the related fundamental researches, core equipment development, working flow, and technical characteristics. Scale-up test and an annual1200-ton-magnesium demonstration-level test was conducted to confirm the rationality, reliability, and advancement of the equipment, system and process design. It is indicated that the new technology solved a series of problems of traditional silicothermic process including adhesion and glaze, short life of retort, low efficiency, high impurity of crystallized magnesium, large heat losses, and poor working environment,making a great technological breakthrough in this field. Representatively, the new well-designed ceramic-lined steel retort serves 2~3 times in life than the normal retorts. The magnesium yield per retort is improved 4~5 times, with purity of >99.8%. The energy consumption in reduction stage is reduced by more than 20%. The mechanical production is fully realized and operating environment is significantly improved.
基金financially supported by the National Natural Science Foundation of China(No.52174291)。
文摘In order to study the sintering characteristics of Ca-rich iron ore,chemical analysis,laser diffraction,scanning electron microscopy,XRD-Rietveld method,and micro-sintering were used to analyze the mineralogical properties and sintering pot tests were used to study the sintering behavior.In addition,a grey correlation mathematical model was used to calculate and compare the comprehensive sintering performance under different calcium-rich iron ore contents.The results demonstrate that the Ca-rich iron ore has coarse grain size and strong self-fusing characteristics with Ca element in the form of calcite(CaCO_(3)) and the liquid phase produced by the self-fusing of the calcium-rich iron ore is well crystallized.Its application with a 20wt%content in sintering improves sinter productivity,reduces fuel consumption,enhances reduction index,and improves gas permeability in blast furnace by 0.45 t/(m^(2)·h),6.11 kg/t,6.17%,and 65.39 kPa·℃,respectively.The Ca-rich iron ore sintering can improve the calorific value of sintering flue gas compared with magnetite sintering,which is conducive to recovering heat for secondary use.As the content of the Ca-rich iron ore increases,sinter agglomeration shifts from localized liquid-phase bonding to a combination of localized liquid-phase bonding and iron oxide crystal connection.Based on an examination of the greater weight value of productivity with grey correlation analysis,the Ca-rich iron ore is beneficial for the comprehensive index of sintering in the range of 0-20wt%content.Therefore,it may be used in sintering with magnetite concentrates as the major ore species.
基金financially supported by the National Natural Science Foundation of China(No.52074035)the Fundamental Research Funds for the Central Universities(No.00007720)the National Key Research and Development Program of China(No.2020YFC1910000)。
文摘Electric arc furnace dust(EAFD)is a hazardous waste but can also be a potential secondary resource for valuable metals,such as Zn and Fe.Given the increased awareness of carbon emission reduction,energy conservation,and environmental protection,hydrometallurgical technologies for the detoxification and resource use of EAFD have been developing rapidly.This work summarizes the generation mechanisms,compositions,and characteristics of EAFD and presents a critical review of various hydrometallurgical treatment methods for EAFD,e.g.,acid leaching,alkaline leaching,salt leaching,and pretreatment–enhanced leaching methods.Simultaneously,the phase transformation mechanisms of zinc-containing components in acid and alkali solutions and pretreatment processes are expounded.Finally,two novel combined methods,i.e.,oxygen pressure sulfuric acid leaching combined with composite catalyst preparation,and synergistic roasting of EAFD and municipal solid waste incineration fly ash combined with alkaline leaching,are proposed,which can provide future development directions to completely recycling EAFD by recovering valuable metals and using zinc residue.
基金financially supported by the National Natural Science Foundation of China(Nos.U1802253 and 52034002)the Fundamental Research Funds for the Central Universities,China(No.FRF-TT-19-001)。
文摘Currently,the process of extracting rubidium from ores has attracted a great deal of attention due to the increasing application of rubidium in high-technology field.A novel process for the comprehensive utilization of rubidium ore resources is proposed in this paper.The process consists mainly of mineral dissociation,selective leaching,and desilication.The results showed that the stable silicon–oxygen tetrahedral structure of the rubidium ore was completely disrupted by thermal activation and the mineral was completely dissociated,which was conducive to subsequent selective leaching.Under the optimal conditions,extractions of 98.67% Rb and 96.23%K were obtained by leaching the rubidium ore.Moreover,the addition of a certain amount of activated Al(OH)_(3) during leaching can effectively inhibit the leaching of silicon.In the meantime,the leach residue was sodalite,which was successfully synthesized to zeolite A by hydrothermal conversion.The proposed process provided a feasible strategy for the green extraction of rubidium and the sustainable utilization of various resources.
基金financially supported by the Fundamental Research Funds for the Central Universities(No.FRF-TP-19-017A3)the National Natural Science Foundation of China(No.51874026)。
文摘Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur during continuous casting,which includes depression,longitudinal cracks,deep oscillation marks,and severe level fluctuation with slag entrapment.The high-efficiency production of hypo-peritectic steels by continuous casting is still a great challenge due to the limited understanding of the mechanism of peritectic solidification.This work reviews the definition and classification of hypo-peritectic steels and introduces the formation tendency of common surface defects related to peritectic solidification.New achievements in the mechanism of peritectic reaction and transformation have been listed.Finally,countermeasures to avoiding surface defects of hypo-peritectic steels duiring continuous casting are summarized.Enlightening certain points in the continuous casting of hypo-peritectic steels and the development of new techniques to overcome the present problems will be a great aid to researchers.
基金financially supported by the National Key Research and Development Program for Young Scientists,China(No.2021YFC2901100)。
文摘Platinum group metals(PGMs),especially Pd,Pt,and Rh,have drawn great attention due to their unique features.Direct separation of Pd and Pt from highly acidic automobile catalyst leach liquors is disturbed by various factors.This work investigates the effect of various parameters including the acidity,extractant concentration,phase ratio A/O,and diluents on the Pd and Pt extraction and their stripping behaviors.The results show that the Pd and Pt are successfully separated from simulated leach liquor of spent automobile catalysts with monothioCyanex 272 and trioctylamine(TOA).Monothio-Cyanex 272 shows strong extractability and specific selectivity for Pd,and only one single stage is needed to recover more than 99.9% of Pd,leaving behind all the Pt,Rh,and base metals of Fe,Mg,Ce,Ni,Cu,and Co in the raffinate.The loaded Pd is efficiently stripped by acidic thiourea solutions.TOA shows strong extractability for Pt and Fe at acidity of 6 mol·L^(–1) HCl.More than 99.9% of Pt and all of the Fe are extracted into the organic phase after two stages of countercurrent extraction.Diluted HCl easily scrubs the loaded base metals(Fe,Cu,and Co).The loaded Pt is efficiently stripped by 1.0 mol·L^(–1) thiourea and 0.05–0.1 mol·L^(–1) Na OH solutions.Monothio-Cyanex 272 and TOA can realize the separation of Pd and Pt from highly acidic leach liquor of spent automobile catalysts.
基金financially supported by the Beijing Natural Science Foundation of China (No. 2232038)the National Natural Science Foundation of China (Nos. 52034002 and U1802253)the Fundamental Research Funds for the Central Universities (No. FRF-TT-19-001)
文摘Copper-indium-gallium-diselenide(CIGS)is a fast-evolving commercial solar cell.The firm demand for global carbon reduction and the rise of potential environmental threats necessitate spent CIGS solar cell recycling.In this paper,the sources and characteristics of valuable metals in spent CIGS solar cells were reviewed.The potential environmental impacts of CIGS,including service life,critical material,and material toxicity,were outlined.The main recovery methods of valuable metals in the various types of spent CIGS,including hydrometallurgy,pyrometallurgy,and comprehensive treatment processes,were compared and discussed.The mechanism of different recovery processes was summarized.The challenges faced by different recycling processes of spent CIGS were also covered in this review.Finally,the economic viability of the recycling process was assessed.The purpose of this review is to provide reasonable suggestions for the sustainable development of CIGS and the harmless disposal of spent CIGS.
基金the National Natural Science Foundation of China(No.42072284,No.42027801,No.41877186)the National Key R&D Program of China(2021YFC2902004)+1 种基金the Major Science and Technology Projects of Inner Mongolia Autonomous Region(2020ZD0020-4)the Fundamental Research Funds for the Central Universities(2022YQSH01,2020YJSSH01,2021YJSSH01)。
文摘Chifeng is a concentrated mining area for non-ferrous metal minerals,as well as a key prevention and control area for heavyduty enterprises.This situation necessitates an efective ecological and human health risk assessment of heavy metal(loid)s driven by the wide distribution of metal ore processing,mining,and smelting factories in Hexigten Banner and Bairin Left Banner.We conducted surveys to assess the levels of heavy metal(loid)s(Cr,As,Pb,Cd,and Hg)in the topsoil and groundwater of the areas.The results indicated that the concentrations of As,Cd,and Pb in partial soil samples exceeded the environmental quality standards of Grade II.Based on contamination assessments,such as geoaccumulation indices and pollution indices,we inferred that Cd,Pb,and As were primary pollutants in topsoil.Potential ecological risks when considered as part of the average risk indices(RI)are up to 1626.40 and 2818.76,respectively,in the two areas.Comparative analysis revealed that Cd posed a very high potential ecological risk,followed by As.Moreover,the evaluation showed that the three exposure pathways of carcinogenic and non-carcinogenic risk followed a descending order:inhalation>ingestion>dermal contact,except for Pb.Arsenic in topsoil posed a potential non-carcinogenic risk to human health,while there were no adverse efects of As in groundwater.In addition,the average total carcinogenic risk for As in the two areas,as well as the risk of Pb in the topsoil of Bairin Left Banner and all the fve heavy metal(loid)s in groundwater,exceeded human tolerance.Pb–Zn mines caused higher human health risks.In addition,the tandem contamination of heavy metal(loid)s in soil and groundwater was not obvious.This research study provides a basis for pollution remediation to control heavy industry-induced ecological and health risks of heavy metal(loid)s.
基金supported by the State Key Laboratory of Advanced Metallurgy,China(Project Code:41603006).
文摘Decarbonization is a critical issue for peaking CO_(2) emissions of energy-intensive industries,such as the iron and steel industry.The decarbonization options of China’s ironmaking and steelmaking sector were discussed based on a systematic three-dimensional low-carbon analysis from the aspects of resource utilization(Y),energy utilization(Q),and energy cleanliness which is evaluated by a process general emission factor(PGEF)on all the related processes,including the current blast furnace(BF)-basic oxygen furnace(BOF)integrated process and the specific sub-processes,as well as the electric arc furnace(EAF)process,typical direct reduction(DR)process,and smelting reduction(SR)process.The study indicates that the three-dimensional aspects,particularly the energy structure,should be comprehensively considered to quantitatively evaluate the decarbonization road map based on novel technologies or processes.Promoting scrap utilization(improvement of Y)and the substitution of carbon-based energy(improvement of PGEF)in particular is critical.In terms of process scale,promoting the development of the scrap-based EAF or DR-EAF process is highly encouraged because of their lower PGEF.The three-dimensional method is expected to extend to other processes or industries,such as the cement production and thermal electricity generation industries.
基金financially supported by the National Science Foundation China (No.U22A20171)the Scinence and Technology Program of Hebei,China (No.20311004D)。
文摘The low-reactivity mold flux with low SiO_(2)content is considered suitable for the continuous casting of high-aluminum steel since it can significantly reduce the reaction between Al in steel and SiO_(2)in mold flux.However,the traditional low-reactivity mold flux still presents some problems such as high viscosity and strong crystallization tendency.In this study,the co-addition of Li_(2)O and B_(2)O_(3)in CaO–Al_(2)O_(3)–10wt%Si O_(2)based low-reactivity mold flux was proposed to improve properties of mold flux for high-aluminum steel,and the effect of Li_(2)O replacing B_(2)O_(3)on properties of mold flux was investigated.The viscosity of the mold flux with 2wt%Li_(2)O and 6wt%B_(2)O_(3)reached a minimum value of 0.07 Pa·s.The break temperature and melting point showed a similar trend with the viscosity.Besides,the melt structure and precipitation of the crystalline phase were studied using Raman and X-ray diffraction spectra to better understand the evolution of viscosity.It demonstrated that with increasing Li_(2)O content in the mold flux from 0 to 6 wt%,the degree of polymerization of aluminate and the aluminosilicate network structure increased because of increasing Li+released by Li_(2)O,indicating the added Li_(2)O was preferentially associated with Al^(3+)as a charge compensator.The precipitation of LiAlO_(2)crystalline phase gradually increased with the replacement of B_(2)O_(3)by Li_(2)O.Therefore,Li_(2)O content should be controlled below 2wt%to avoid LiAlO_(2)precipitation,which was harmful to the continuous casting of highaluminum steels.
基金financially supported by the National Natural Science Foundation of China (Nos. U1302274 and 51674026)the Fundamental Research Funds for the Central Universities (No. 230201606500078)the Yunnan Technical Innovation and Personnel Training Program
文摘Huge quantities of zinc leaching residues(ZLRs) generated from zinc production are dumped continuously around the world and pose a potential environmental threat because of their considerable amounts of entrained heavy metals(mainly lead). Most ZLRs have not been properly treated and the valuable metals in them have not yet been effectively recovered. Herein, the deep cleaning of a ZLR and recovery of valuable metals via a hydrometallurgical route were investigated. The cleaning process consists of two essential stages: acid leaching followed by calcium chloride leaching. The optimum conditions for extracting zinc, copper, and indium by acid leaching were a sulfuric acid concentration of 200 g·L^(-1), a liquid/solid ratio of 4:1(m L/g), a leaching time of 2 h, and a temperature of 90°C. For lead and silver extractions, the optimum conditions were a calcium chloride concentration of 400 g·L^(-1), a pH value of 1.0, a leaching time of 1 h, and a temperature of 30°C. After calcium chloride leaching, silver and lead were extracted out and the lead was finally recovered as electrolytic lead by electrowinning. The anglesite phase, which poses the greatest potential environmental hazard, was removed from the ZLR after deep cleaning, thus reducing the cost of environmental management of ZLRs. The treatment of chlorine and spent electrolyte generated in the process was discussed.
基金financially supported by the National Basic Research Priorities Program of China(Nos.2014CB643401 and 2013AA032003)the National Natural Science Foundation of China(No.51372019)Shanxi Collaborative Innovation Center of High Value-added Utilization of Coal-related Wastes
文摘Low-nickel matte was intensively characterized,and Ni,Cu,and Co were determined to exist mainly as(Fe,Ni)_9S_8 and Fe Ni_3,Cu_5FeS_4,and(Fe,Ni)_9S_8 and Fe_3O_4(in isomorphic form),respectively.The efficient and selective extraction of Ni,Cu,and Co from the low-nickel matte in an(NH_4)_2S_2O_8/NH_3·H_2O solution system was studied.The effects of(NH_4)_2S_2O_8 and NH_3·H_2O concentrations,leaching time,and leaching temperature on the metal extraction efficiency were systematically investigated.During the oxidative ammonia leaching process,the metal extraction efficiencies of Ni 81.07%,Cu 93.81%,and Co 71.74% were obtained under the optimal conditions.The relatively low leaching efficiency of Ni was mainly ascribed to Ni Fe alloy deactivation in ammonia solution.By introducing an acid pre-leaching process into the oxidative ammonia leaching process,we achieved the high extraction efficiencies of 98.03%,99.13%,and 85.60% for the valuable metals Ni,Cu,and Co,respectively,from the low-nickel matte.
基金financially supported by the National Natural Science Foundation of China(Nos.52074035 and 52008229)the Key Technologies Research and Develo pment Program,China(No.2020YFB0606200)。
文摘Circulating fluidized bed fly ash(CFBFA)is a solid waste product from circulating fluidized bed(CFB)boilers in power plants,and the storage of CFBFA is increasingly become an environmental problem.Previous scholars have made contributions to improve the resource utilization of CFBFA.Especially,ecological cement is prepared by CFBFA,which is more conducive to its large-scale utilization.In recent years,a lot of effort has been paid to improve the properties of ecological cement containing CFBFA.In this work,the physicochemical properties of CFBFA are introduced,and recent research progress on the mechanical,expansion,and rheological properties of CFBFA based ecological cement(CEC)is extensively reviewed.The problem of over-expansion of f-CaO is summarized,which limits the scale application of CFBFA in ecological cement.Hence,the challenge for f-CaO in CFBFA to compensate for cement volume shrinkage is proposed,which is beneficial to the utilization of CFBFA in ecological cement,and the reduction of CO_(2) emissions from the cement industry.In addition,the environmental performance,durability,and economy of CEC should be valued in future research,especially the environmental performance,because the CFBFA contains heavy metals,such as Cr,As,which may pollute groundwater.
基金Project(2011FZ056)supported by the Applied Basic Research Plan Program of Yunnan Province,China
文摘In order to achieve higher efficient cohesion match of procedure and equipment between ironmaking and steelmaking interface, the theory of multi-dimensional material flow control was applied to analyze torpedo ladle-iron ladle transportation process between blast furnace and basic oxygen furnace. Moreover, basic parameters of material flow were analyzed and optimized, such as time, temperature and material quantity. Based on operating principles of material flow, control methods were optimized, such as product organization mode, scheduling discipline and scheduling plan of hot metal ladle. Finally, the material flow control technology of ironmaking and steelmaking interface was integrated. Satisfactory effects are obtained after applying the technology in practice. The total turnover number of torpedo ladle decreases from 20 to 18, the hot metal temperature of 1# BF torpedo ladle decreases from 36 °C to 19.5 °C, the hot metal temperature of 2# BF torpedo ladle decreases from 36.6 °C to 19.8 °C, the temperature drop of desulfurization hot metal decreases by 4 °C, and the temperature drop of non-desulfurization hot metal decreases by 2.8 °C. Furthermore, the ironmaking and steelmaking interface system will realize high-efficiency control by using this control technology.
基金the Fundamental Research Funds for the Central Universities,China(No.06500177)the National Natural Science Foundation of China Joint Fund Project(No.U1764255)。
文摘Layered oxide is a promising cathode material for sodium-ion batteries because of its high-capacity,high operating voltage,and simple synthesis.Cycling performance is an important criterion for evaluating the application prospects of batteries.However,facing challenges,including phase transitions,ambient stability,side reactions,and irreversible anionic oxygen activity,the cycling performance of layered oxide cathode materials still cannot meet the application requirements.Therefore,this review proposes several strategies to address these challenges.First,bulk doping is introduced from three aspects:cationic single doping,anionic single doping,and multi-ion doping.Second,homogeneous surface coating and concentration gradient modification are reviewed.In addition,methods such as mixed structure design,particle engineering,high-entropy material construction,and integrated modification are proposed.Finally,a summary and outlook provide a new horizon for developing and modifying layered oxide cathode materials.
基金financially supported by the National Natural Science Foundation of China(No.U1260202)the National Basic Research Priorities Program of China(No.2012CB720401)the State Key Laboratory of Solid Waste Reuse for Building Materials
文摘In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitrogen atmosphere. The effects of reaction temperature, reaction time, and carbon content on the metallization and dezincification ratios of the composite briquettes were studied. The reduced com- posite briquettes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive spectroscopy (EDS). The results show that the gravity dust and converter sludge are combined into the composite briquettes and a reasonable combination not only improves the performance of the composite briquettes, but also leads to the reduction with no or little reductant and flux. As the re- action temperature is increased and the reaction time is extended, the metallization and dezincification ratios of the composite briquettes in- crease gradually. When the composite briquettes are roasted at 1300℃ for 30 rain, the metallization ratio and dezineification ratio reaches 91.35% and 99.25%, respectively, indicating that most of the iron oxide is reduced and the zinc is almost completely removed. The carbon content is observed to exert a lesser effect on the reduction process; as the C/O molar ratio increases, the metallization and dezincification ra- tios first increase and then decrease.
基金supported by the National Nature Science Foundation of China(Nos.51272025,50872011,and 50672006)the Major State Basic Research and Development Program of China(No.2007CB613608)
文摘Nanostructured Fe-doped titanium dioxide was synthesized from titanium containing electric furnace molten slag (TCEFMS) by using an alkali fusion, followed by a hydrolyzation-acidolysis-cMcination route. The effects of Mkali/slag mass ratio, calcinating temperature, calcinating time, and water/slag mass ratio on the extraction efficiency and purity of products were systematically studied in this paper. It is indicated that the best extraction efficiency of nanostructured Fe- doped titanium dioxide is 99.35%, when the molten slag is calcinated at 700℃ for 1 h with the mass ratio of alkali/molten slag of 1.5:1. The influence of alkali/slag mass ratio on the photocatalytic activity of final products was evaluated by the photodegradation of methyl blue under visible light irradiation. A maximum photodegradation efficiency of 88.12% over 30 min was achieved under the optimum conditions.