BaxSr1-xTiO3 sol-gel thin films with x--0.5, 0.7 and 0.8 have been fabricated as AI/BST/Pt capacitor. The AC conductivity and dielectric properties over a frequency rang of 10 Hz and I MHz have been studied in order t...BaxSr1-xTiO3 sol-gel thin films with x--0.5, 0.7 and 0.8 have been fabricated as AI/BST/Pt capacitor. The AC conductivity and dielectric properties over a frequency rang of 10 Hz and I MHz have been studied in order to explore the ion dynamics and relaxation mechanisms in the films. The frequency dependent conductivity plots show three regions of conduction processes. Dielectric results show that ε＇ at low frequencies increases as Sr content decreases, whereas at high frequencies, it shows opposite variation, which is attributed to the dipole dynamics. The electric modulus plots reveal the relaxation peaks which are not observed in the ε＂ plots and the contribution of the grains, grain boundaries and electrode to the relaxation mechanisms.展开更多
Synthesis of Ni0.sLixZn（0.5-x）Fe204 nanoparticles with x=0, 0.1, 0.2, 0.3, 0.4 and 0.5 were realized via coprecipitation method. X-ray diffraction （XRD） and vibrating sample magnetometer （VSM） measurements were ...Synthesis of Ni0.sLixZn（0.5-x）Fe204 nanoparticles with x=0, 0.1, 0.2, 0.3, 0.4 and 0.5 were realized via coprecipitation method. X-ray diffraction （XRD） and vibrating sample magnetometer （VSM） measurements were performed on the samples to determine the characteristics of the crystal structures and the magnetic properties of the samples, respectively. The spinel phase structures of the samples were confirmed by XRD analysis. Patterns of decreased lattice parameter and increased crystallite size values were observed by increasing the Li concentration at longer synthesis reaction periods. Similarly, for the magnetic properties, both the saturation magnetization （Ms） and coercivity （Hc） were found to vary with increasing patterns at higher Li doping levels and longer synthesis reaction periods. The results and mechanisms concerned were discussed.展开更多
文摘BaxSr1-xTiO3 sol-gel thin films with x--0.5, 0.7 and 0.8 have been fabricated as AI/BST/Pt capacitor. The AC conductivity and dielectric properties over a frequency rang of 10 Hz and I MHz have been studied in order to explore the ion dynamics and relaxation mechanisms in the films. The frequency dependent conductivity plots show three regions of conduction processes. Dielectric results show that ε＇ at low frequencies increases as Sr content decreases, whereas at high frequencies, it shows opposite variation, which is attributed to the dipole dynamics. The electric modulus plots reveal the relaxation peaks which are not observed in the ε＂ plots and the contribution of the grains, grain boundaries and electrode to the relaxation mechanisms.
基金the grant provided under the Fundamental Research Grant Scheme (FRGS) from the Ministry of Higher Education, Malaysia to carry out this researchthe financial assistance provided under the Graduate Assistant Scheme (GA) to one of the authors (D.N. Rohadiana) awarded by Universiti Malaysia Perlis
文摘Synthesis of Ni0.sLixZn（0.5-x）Fe204 nanoparticles with x=0, 0.1, 0.2, 0.3, 0.4 and 0.5 were realized via coprecipitation method. X-ray diffraction （XRD） and vibrating sample magnetometer （VSM） measurements were performed on the samples to determine the characteristics of the crystal structures and the magnetic properties of the samples, respectively. The spinel phase structures of the samples were confirmed by XRD analysis. Patterns of decreased lattice parameter and increased crystallite size values were observed by increasing the Li concentration at longer synthesis reaction periods. Similarly, for the magnetic properties, both the saturation magnetization （Ms） and coercivity （Hc） were found to vary with increasing patterns at higher Li doping levels and longer synthesis reaction periods. The results and mechanisms concerned were discussed.