The effect of undissolved ferrite amount in subcritically quenched 42CrMo steel on contact fatigue properties and failure mechanism were studied. The amount of undissolved ferrite in the steel were 0%,3%,10%,15% and 2...The effect of undissolved ferrite amount in subcritically quenched 42CrMo steel on contact fatigue properties and failure mechanism were studied. The amount of undissolved ferrite in the steel were 0%,3%,10%,15% and 20% in volume fraction, respectively. The experimental results show that the existence of undissolved ferrite can increase the contact fatigue life The contact fatigue life can be prolonged with increasing the amounts of undissolved ferrite The grain size can be fined by using subcritical quenching process and the area of phase boundaries can also be greatly increased. The stress relaxation and grain refinement due to occurring of plastic deformation are main reasons for improving the fatigue life. The existence of undissolved ferrite can increase the crack initiation period. Under the experiment conditions, when the amount of undissolved ferrite is 10%, the longest contact fatigue life can be the obtained.展开更多
A series of tests was performed with three-point single-edge-notched-bend (SENB) specimens in a condenser material (Titanium alloy). Results show that the J-integral values of welded joint and HAZ are obviously smalle...A series of tests was performed with three-point single-edge-notched-bend (SENB) specimens in a condenser material (Titanium alloy). Results show that the J-integral values of welded joint and HAZ are obviously smaller than those of the base metal. It signifies that the welding process can result in a reduced toughness of Titanium alloy and the effect of crack orientation on toughness value is not negligible for engineering applications. Besides, the J-integral values of L-T direction specimens are much higher than those of L-S ones. The J-integral values of rolled ring are:JC-R>JC-L>JL-R.展开更多
文摘The effect of undissolved ferrite amount in subcritically quenched 42CrMo steel on contact fatigue properties and failure mechanism were studied. The amount of undissolved ferrite in the steel were 0%,3%,10%,15% and 20% in volume fraction, respectively. The experimental results show that the existence of undissolved ferrite can increase the contact fatigue life The contact fatigue life can be prolonged with increasing the amounts of undissolved ferrite The grain size can be fined by using subcritical quenching process and the area of phase boundaries can also be greatly increased. The stress relaxation and grain refinement due to occurring of plastic deformation are main reasons for improving the fatigue life. The existence of undissolved ferrite can increase the crack initiation period. Under the experiment conditions, when the amount of undissolved ferrite is 10%, the longest contact fatigue life can be the obtained.
文摘A series of tests was performed with three-point single-edge-notched-bend (SENB) specimens in a condenser material (Titanium alloy). Results show that the J-integral values of welded joint and HAZ are obviously smaller than those of the base metal. It signifies that the welding process can result in a reduced toughness of Titanium alloy and the effect of crack orientation on toughness value is not negligible for engineering applications. Besides, the J-integral values of L-T direction specimens are much higher than those of L-S ones. The J-integral values of rolled ring are:JC-R>JC-L>JL-R.
