SiBN fibers are one of the most admirable microwave-transparent reinforced materials for high Mach number aircrafts.Currently,the detailed high-temperature oxidation behavior of SiBN fibers has not been studied yet.In...SiBN fibers are one of the most admirable microwave-transparent reinforced materials for high Mach number aircrafts.Currently,the detailed high-temperature oxidation behavior of SiBN fibers has not been studied yet.In this work,we studied the high-temperature oxidation behavior of SiBN fibers with different boron contents at the temperature range of 1000-1400℃in air.SiBN fibers started to be oxidized at 1100℃,with Si_(3)N_(4) and BN phase oxidized to SiO2 and B_(2)O_(3),respectively.Due to the gasification and the escape of molten B_(2)O_(3) at high temperatures,amorphous SiO_(2) could be remained at the fiber surface.As the fiber further oxidized,the molten B_(2)O_(3) at the inside may infiltrate into the fiber interior to react with Si_(3)N_(4),causing the precipitation of hexagonal boron nitride(h-BN)nanoparticles and the formation of SiO_(2)/BN layer.Finally,complex oxidation layers with two distinct concentric sublayers accompanied with two transition sublayers could be formed after the oxidizing treatment.展开更多
基金supported by the National Natural Science Foundation of China(No.52073304).
文摘SiBN fibers are one of the most admirable microwave-transparent reinforced materials for high Mach number aircrafts.Currently,the detailed high-temperature oxidation behavior of SiBN fibers has not been studied yet.In this work,we studied the high-temperature oxidation behavior of SiBN fibers with different boron contents at the temperature range of 1000-1400℃in air.SiBN fibers started to be oxidized at 1100℃,with Si_(3)N_(4) and BN phase oxidized to SiO2 and B_(2)O_(3),respectively.Due to the gasification and the escape of molten B_(2)O_(3) at high temperatures,amorphous SiO_(2) could be remained at the fiber surface.As the fiber further oxidized,the molten B_(2)O_(3) at the inside may infiltrate into the fiber interior to react with Si_(3)N_(4),causing the precipitation of hexagonal boron nitride(h-BN)nanoparticles and the formation of SiO_(2)/BN layer.Finally,complex oxidation layers with two distinct concentric sublayers accompanied with two transition sublayers could be formed after the oxidizing treatment.