Aluminum(Al) 2024 matrix composites reinforced with alumina short fibers(Al_2O_(3sf)) and silicon carbide particles(SiC_p) as wear-resistant materials were prepared by pressure infiltration in this study. Further, the...Aluminum(Al) 2024 matrix composites reinforced with alumina short fibers(Al_2O_(3sf)) and silicon carbide particles(SiC_p) as wear-resistant materials were prepared by pressure infiltration in this study. Further, the effect of Al_2O_(3sf) on the friction and wear properties of the as-synthesized composites was systematically investigated, and the relationship between volume fraction and wear mechanism was discussed. The results showed that the addition of Al_2O_(3sf), characterized by the ratio of Al_2O_(3sf) to SiC_p, significantly affected the properties of the composites and resulted in changes in wear mechanisms. When the volume ratio of Al_2O_(3sf) to SiC_p was increased from 0 to 1, the rate of wear mass loss(K_m) and coefficients of friction(COFs) of the composites decreased, and the wear mechanisms were abrasive wear and furrow wear. When the volume ratio was increased from 1 to 3, the COF decreased continuously; however, the K_m increased rapidly and the wear mechanism became adhesive wear.展开更多
Microstructural evolution and strengthening mechanisms of Mg-3Sn-1Ca based alloys with additions of different amounts of Al N nanoparticles were investigated.It was found that with increasing the amount of AlN nano-pa...Microstructural evolution and strengthening mechanisms of Mg-3Sn-1Ca based alloys with additions of different amounts of Al N nanoparticles were investigated.It was found that with increasing the amount of AlN nano-particles the grain size decreases obviously.The existence of AlN nano-particles could refine the primary crystal phases CaMgSn,which provided more heterogeneous nucleation sites for the formation of magnesium.Moreover,such nano-particles could also restrict the grain growth during solidification.After adding AlN nano-particles,both the tensile properties at room temperature and high temperature 250℃and the hardness are largely improved.The improvement of strength is attributed to grain refinement and second phase refinement.展开更多
A new modifying agent, ZnS, was used as a refiner to modify primary silicon in hypereutectic AlSi alloy. The factors affecting the modification results, including addition level of ZnS and holding time, were investiga...A new modifying agent, ZnS, was used as a refiner to modify primary silicon in hypereutectic AlSi alloy. The factors affecting the modification results, including addition level of ZnS and holding time, were investigated. The results showed that the average size of the most effectively modified primary silicon was 28.5 μm when the ZnS mixed powder addition was 0.15 wt.% with a holding time of 10 min. More important, the average size of primary silicon could remain below 40 μm despite the holding time extending to 120 min, which means ZnS is a promising modifying agent of primarySi in industrial applications.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51374028)
文摘Aluminum(Al) 2024 matrix composites reinforced with alumina short fibers(Al_2O_(3sf)) and silicon carbide particles(SiC_p) as wear-resistant materials were prepared by pressure infiltration in this study. Further, the effect of Al_2O_(3sf) on the friction and wear properties of the as-synthesized composites was systematically investigated, and the relationship between volume fraction and wear mechanism was discussed. The results showed that the addition of Al_2O_(3sf), characterized by the ratio of Al_2O_(3sf) to SiC_p, significantly affected the properties of the composites and resulted in changes in wear mechanisms. When the volume ratio of Al_2O_(3sf) to SiC_p was increased from 0 to 1, the rate of wear mass loss(K_m) and coefficients of friction(COFs) of the composites decreased, and the wear mechanisms were abrasive wear and furrow wear. When the volume ratio was increased from 1 to 3, the COF decreased continuously; however, the K_m increased rapidly and the wear mechanism became adhesive wear.
基金financially supported by the Study Abroad Program by the Government of Shandong Province(201802005)Linyi Industrial Technology Research Institute and Shandong Yinguang Yuyuan Light Metal Precise Forming Co.,Ltd。
文摘Microstructural evolution and strengthening mechanisms of Mg-3Sn-1Ca based alloys with additions of different amounts of Al N nanoparticles were investigated.It was found that with increasing the amount of AlN nano-particles the grain size decreases obviously.The existence of AlN nano-particles could refine the primary crystal phases CaMgSn,which provided more heterogeneous nucleation sites for the formation of magnesium.Moreover,such nano-particles could also restrict the grain growth during solidification.After adding AlN nano-particles,both the tensile properties at room temperature and high temperature 250℃and the hardness are largely improved.The improvement of strength is attributed to grain refinement and second phase refinement.
基金supported by the Applied Basic Research Programs of Qingdao,China(No.14-2-4-50-jch)
文摘A new modifying agent, ZnS, was used as a refiner to modify primary silicon in hypereutectic AlSi alloy. The factors affecting the modification results, including addition level of ZnS and holding time, were investigated. The results showed that the average size of the most effectively modified primary silicon was 28.5 μm when the ZnS mixed powder addition was 0.15 wt.% with a holding time of 10 min. More important, the average size of primary silicon could remain below 40 μm despite the holding time extending to 120 min, which means ZnS is a promising modifying agent of primarySi in industrial applications.