The processing parameters of tube extrusion for superalloy Inconel 718 (IN 718), such as slug temperature, tools temperature, choice of lubricant, extrusion ratio and extrusion speed, were determined by experiment in ...The processing parameters of tube extrusion for superalloy Inconel 718 (IN 718), such as slug temperature, tools temperature, choice of lubricant, extrusion ratio and extrusion speed, were determined by experiment in this paper. An appropriate temperature range recommended for the slug is 1080-1120℃, and the temperature range recommended for the tools is 350-500℃. The microstructural evolution of superalloy IN 718 during tube extrusion was analyzed. With the increase of the deformation the cross crystal grains were slightly refined. While the vertical crystal grain is elongated evidently and the tensile strength increased along the axial rake. Glass lubricants have to be spread on the slug surface after being heated to 150-200℃, vegetable oil or animal oil can be used as the lubricant on the surface of the tools to reduce the extrusion force remarkably.展开更多
The effect of manganese on the as-cast structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied. The results indicate that the fraction of retained austenite an...The effect of manganese on the as-cast structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied. The results indicate that the fraction of retained austenite and the manganese distribution in as-cast alloys are controlled by manganese content. The manganese distribution in as-cast alloys is not homogeneous. The manganese content in carbide is higher than that in matrix. Whether the secondary hardening occurs or not and the peak hardness of secondary hardening is controlled by manganese content in retained austenite in as-cast structure. Higher manganese content can cause more retained austenite. The secondary hardening occurs in sub-critical treating process if the fraction of retained austenite is high.展开更多
文摘The processing parameters of tube extrusion for superalloy Inconel 718 (IN 718), such as slug temperature, tools temperature, choice of lubricant, extrusion ratio and extrusion speed, were determined by experiment in this paper. An appropriate temperature range recommended for the slug is 1080-1120℃, and the temperature range recommended for the tools is 350-500℃. The microstructural evolution of superalloy IN 718 during tube extrusion was analyzed. With the increase of the deformation the cross crystal grains were slightly refined. While the vertical crystal grain is elongated evidently and the tensile strength increased along the axial rake. Glass lubricants have to be spread on the slug surface after being heated to 150-200℃, vegetable oil or animal oil can be used as the lubricant on the surface of the tools to reduce the extrusion force remarkably.
文摘The effect of manganese on the as-cast structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied. The results indicate that the fraction of retained austenite and the manganese distribution in as-cast alloys are controlled by manganese content. The manganese distribution in as-cast alloys is not homogeneous. The manganese content in carbide is higher than that in matrix. Whether the secondary hardening occurs or not and the peak hardness of secondary hardening is controlled by manganese content in retained austenite in as-cast structure. Higher manganese content can cause more retained austenite. The secondary hardening occurs in sub-critical treating process if the fraction of retained austenite is high.