The variation in altitude density function （ADF） of the surface topography of mild steel during electrochemical polishing （ECP） was investigated, and the mechanism of the variation of surface roughness with polish...The variation in altitude density function （ADF） of the surface topography of mild steel during electrochemical polishing （ECP） was investigated, and the mechanism of the variation of surface roughness with polishing time was analyzed. The results show that the variation trend of ADF with polishing time is flat-steep-flat; the variation of surface roughness results in the different distri- butions of surface current density, and there is a fine surface smoothness in the special period of ECP from 4 to 8 s.展开更多
The effects of phase transformation on mechanical properties and pitting corrosion of 2205 duplex stainless steel were investigated. The amount of a phase in the test specimen varied up to a maximum of 6 % by thermal ...The effects of phase transformation on mechanical properties and pitting corrosion of 2205 duplex stainless steel were investigated. The amount of a phase in the test specimen varied up to a maximum of 6 % by thermal treatment at 850 ℃ for up to 60 min. The results showed that ~ phase markedly increased the hardness and decreased the impact toughness of the test steel. But the increasing tendency of the ultimate tensile strength and the yield strength was not obvious, while the total elongation abruptly decreased with the aging time from 5 to 60 min. SEM impact microfractograph analysis revealed that the types of impact fracture changed from ductile mode to transcrystalline mode when the specimens were aged for 5-60 min. Furthermore, the extent of pitting potential reducing was found to be strongly temperature dependent, more pronounced at the higher temperature. During the incubation period of σ phase nucleation, the pitting corrosion test temperature and the aging time had collaborative effects on evidently displacing the pitting potential towards less noble values. After 15 min, the higher temperature contributed more to decreasing the pitting potential than the aging time.展开更多
基金the National Natural Science Foundation of China (No.59831030).
文摘The variation in altitude density function （ADF） of the surface topography of mild steel during electrochemical polishing （ECP） was investigated, and the mechanism of the variation of surface roughness with polishing time was analyzed. The results show that the variation trend of ADF with polishing time is flat-steep-flat; the variation of surface roughness results in the different distri- butions of surface current density, and there is a fine surface smoothness in the special period of ECP from 4 to 8 s.
基金Item Sponsored by Special Project of Education Depart ment of Shaanxi Province of China (07JK309)Project of Science andTechnology Research and Development Program of Shaanxi Province of China (2010K10-13)
文摘The effects of phase transformation on mechanical properties and pitting corrosion of 2205 duplex stainless steel were investigated. The amount of a phase in the test specimen varied up to a maximum of 6 % by thermal treatment at 850 ℃ for up to 60 min. The results showed that ~ phase markedly increased the hardness and decreased the impact toughness of the test steel. But the increasing tendency of the ultimate tensile strength and the yield strength was not obvious, while the total elongation abruptly decreased with the aging time from 5 to 60 min. SEM impact microfractograph analysis revealed that the types of impact fracture changed from ductile mode to transcrystalline mode when the specimens were aged for 5-60 min. Furthermore, the extent of pitting potential reducing was found to be strongly temperature dependent, more pronounced at the higher temperature. During the incubation period of σ phase nucleation, the pitting corrosion test temperature and the aging time had collaborative effects on evidently displacing the pitting potential towards less noble values. After 15 min, the higher temperature contributed more to decreasing the pitting potential than the aging time.