Three different groups of ceramic powders for the thermal-swayed coating were firstly prepared using sintering and ball milling. Then, these powders were separately deposited on three stainless steel substrates, follo...Three different groups of ceramic powders for the thermal-swayed coating were firstly prepared using sintering and ball milling. Then, these powders were separately deposited on three stainless steel substrates, followed by individual corrosion resistance examination. Microstructural characterization showed that the levels of micro-void and micro-crack at the bonding interface （between coating and substrate） depended on the proportions of different ceramic particles. Meanwhile, a significantly enhanced corrosion resistance was reproducibly observed in one group of as-coated samples that have the optimal combination of given ceramic powders. Furthermore, the mechanism of corresponding enhanced corrosion resistance was discussed. It was found that the optimal ceramic powders for the present thermal-sprayed coating should contain 30.2 wt% SiO2, 54 wt% Cr2O3, 6.8 wt% Al2O3, 4.8 wt% CaO and 1.8 wt% TiO2. The corrosion velocities of such samples in the 3.5 vol.% HCl, 15 wt% NaOH and 5 wt% NaCl solutions were 3.74, 2.98 and 0.50 g h-1 m-2 for 168, 336 and 336 h, respectively.展开更多
文摘Three different groups of ceramic powders for the thermal-swayed coating were firstly prepared using sintering and ball milling. Then, these powders were separately deposited on three stainless steel substrates, followed by individual corrosion resistance examination. Microstructural characterization showed that the levels of micro-void and micro-crack at the bonding interface （between coating and substrate） depended on the proportions of different ceramic particles. Meanwhile, a significantly enhanced corrosion resistance was reproducibly observed in one group of as-coated samples that have the optimal combination of given ceramic powders. Furthermore, the mechanism of corresponding enhanced corrosion resistance was discussed. It was found that the optimal ceramic powders for the present thermal-sprayed coating should contain 30.2 wt% SiO2, 54 wt% Cr2O3, 6.8 wt% Al2O3, 4.8 wt% CaO and 1.8 wt% TiO2. The corrosion velocities of such samples in the 3.5 vol.% HCl, 15 wt% NaOH and 5 wt% NaCl solutions were 3.74, 2.98 and 0.50 g h-1 m-2 for 168, 336 and 336 h, respectively.