Electroless Nickel Plating and Electroplating on FBG Temperature Sensor

Metal-coated fiber Bragg grating（FBG）temperature sensors were prepared via electroless nickel（EN）plating and tin electroplating methods on the surface of normal bare FBG.The surface morphologies of the metal-coated layers were observed under a metallographic microscope.The effects of pretreatment sequence,pH value of EN plating solution and current density of electroplating on the performance of the metal-coated layers were analyzed.Meanwhile, the Bragg wavelength shift induced by temperature was monitored by an optical spectrum analyzer.Sensitivity of the metal-coated FBG（MFBG）sensor was almost two times that of normal bare FBG sensor.The measuring temperature of the MFBG sensor could be up to 280℃,which was much better than that of conventional FBG sensor.

High Sensitive Long Period Fiber Grating Sensor for Detection of Nitrite

A high sensitive long period fiber grating（LPFG） sensor for the detection of nitrite is proposed, which is realized by coating multiple poly（sodium 4-styrensulfonate）（PSS） and poly（diallyldimethylammonium） chloride （PDDA） layers on the fiber grating surface. The sensitivity of this LPFG sensor is maximum when the number of assembled layers is 70. Under this condition, a nitrite concentration of 3×10^-3 mol/L, which is lower than the National Food Additive Standard, 4.2×10^-3 mol/L, can be distinguished. The sensitivity is further increased by 30% when nitrite was determined in the sucrose solution with a concentration of 65%, which provides a new solution for the best refraction index approaching matched index of the fiber cladding. Compared with chemical methods, this nitrite detection technology offers some advantages, such as high accuracy, non toxicity, high speed, low cost, without chemical reagent, and is suitable for foodstuff security detection.

Absorption Line Profile Recovery Based on TDLS and MEMS Micro-Mirror for Photoacoustic Gas Sensing

A novel and efficient absorption line recovery technique is presented.A micro-electromechanical systems(MEMS) mirror driven by an electrothermal actuator is used to generate laser intensity modulation through the mirror reflection.Tunable diode laser spectroscopy(TDLS) and photoacoustic spectroscopy(PAS) are used to recover the target absorption line profile which is compared with the theoretical Voigt profile.The target gas is 0.01% acetylene(C2H2) in a nitrogen host gas.The laser diode wavelength is swept across the P17 absorption line of acetylene at 1 535.4 nm by a current ramp,and an erbium-doped fibre amplifier(EDFA) is used to enhance the optical intensity and increase the signal-to-noise ratio(SNR).A SNR of about 35 is obtained with 100 mW laser power from the EDFA.Good agreement is achieved between the experimental results and the theoretical simulation for the P17 absorption line profile.

High Performance Micro-Structure Sensor Based on TiO2 Nanofibers for Ethanol Detection

TiO2 nanofibers are synthesized via a simple electrospinning method and coated on a silicon substrate with Pt electrodes to fabricate a micro-structure sensor. This sensor exhibits high ethanol sensing properties at 300℃. The sensitivity is up to 4 when the sensor is exposed to 1 ppm ethanol, the response time is about 3s, and the recovery is about 5 s.

Synthesis of Flowerlike Zn Nanoplate Aggregates by Vapor Deposition

1 IntroductionIn the very recent years, low-dimensional nanomaterials have attracted a great interest in nanoscience and nanotechnology due to their exciting application in electronics[1], optoelectronics[2] and mechanics[3] in nanoscale. Compared to bulk materials,

Ferrofluids Containing Fe3O4 Nanoparticles in Solidified Photoresist Carrier

Ferrofluids, formed by magnetic nanoparticles uniformly dispersed in a liquid carrier, respond to an external magnetic field, which enable the fluid＇s position by applying a magnetic field. Here, ferrofluids composed of Fe3O4 nanoparticles with oleic acid and oleylamine as the surfactant and photoresist, respectively, were prepared. Under an external magnetic field, the movement and the position of ferrofluids and the injection of the fluids into complex shapes were easily achieved. The ferrofluid surfaces were distorted under the magnetic field, and the surface structue was controlled by the applied field strength. Using a photoresist as the liquid carrier, it was possible to solidify the ferrofluids by UV irradiation. The shape and the position of the solid superparamagnetic nanoparticles/polymer composites were also determined by the external magnetic field.