Binary titanium–niobium(Ti–Nb)alloys have recently been attracted due to low Young’s moduli and non-toxic properties.This study explores the influence of low Nb content(0–25 wt%)on the comprehensive parameters of ...Binary titanium–niobium(Ti–Nb)alloys have recently been attracted due to low Young’s moduli and non-toxic properties.This study explores the influence of low Nb content(0–25 wt%)on the comprehensive parameters of tensile stress–strain relationships(ultimate strength(rUTS),yield strength(r0.2)and elastic modulus(E)),surfaces properties(Vickers microhardness,surface roughness(Ra),water contact angle(WCA),X-ray diffraction(XRD)and scanning electron microscopy(SEM)),corrosion resistance(in artificial saliva and lactic acid)and biological properties(cytotoxicity and alkaline phosphatase activity of MC3T3-E1 pre-osteoblasts)of Ti–xNb alloys(x紏5,10,15,20 and 25 wt%),with using commercially pure grade 2 titanium(cp-Ti)as control.XRD results shown that all the Ti–xNb alloys comprised atb Ti alloy phases,such that the b phase increased correspondingly with the increased amount of Nb in the alloy,as well as the reduction of E(69–87 GPa).Except Ti–5Nb,all other Ti–xNb alloys showed a significantly higher hardness,increased rUTS and r0.2,and decreased WCA compared with cp-Ti.No corrosion was detected on Ti–xNb alloys and cp-Ti in artificial saliva and lactic acid solutions.The cytotoxicity of Ti–xNb alloys was comparable to that of cp-Ti in MC3T3-E1 pre-osteoblasts without interference from differentiation behaviour,but the proliferation rate of the Ti–5Nb alloy was lower than other groups.In overall,binary Ti–(10–25 wt%)Nb alloys are promising candidate for orthopaedic and dental implants due to their improved mechanical properties and comparable biological performance,while Ti–5Nb should be used with caution.展开更多
基金The study was partially supported by the National Natural Science Foundation of China(NSFC)(grant number 81771126).
文摘Binary titanium–niobium(Ti–Nb)alloys have recently been attracted due to low Young’s moduli and non-toxic properties.This study explores the influence of low Nb content(0–25 wt%)on the comprehensive parameters of tensile stress–strain relationships(ultimate strength(rUTS),yield strength(r0.2)and elastic modulus(E)),surfaces properties(Vickers microhardness,surface roughness(Ra),water contact angle(WCA),X-ray diffraction(XRD)and scanning electron microscopy(SEM)),corrosion resistance(in artificial saliva and lactic acid)and biological properties(cytotoxicity and alkaline phosphatase activity of MC3T3-E1 pre-osteoblasts)of Ti–xNb alloys(x紏5,10,15,20 and 25 wt%),with using commercially pure grade 2 titanium(cp-Ti)as control.XRD results shown that all the Ti–xNb alloys comprised atb Ti alloy phases,such that the b phase increased correspondingly with the increased amount of Nb in the alloy,as well as the reduction of E(69–87 GPa).Except Ti–5Nb,all other Ti–xNb alloys showed a significantly higher hardness,increased rUTS and r0.2,and decreased WCA compared with cp-Ti.No corrosion was detected on Ti–xNb alloys and cp-Ti in artificial saliva and lactic acid solutions.The cytotoxicity of Ti–xNb alloys was comparable to that of cp-Ti in MC3T3-E1 pre-osteoblasts without interference from differentiation behaviour,but the proliferation rate of the Ti–5Nb alloy was lower than other groups.In overall,binary Ti–(10–25 wt%)Nb alloys are promising candidate for orthopaedic and dental implants due to their improved mechanical properties and comparable biological performance,while Ti–5Nb should be used with caution.
