Symmetric rolling(SR)and asymmetric rolling(ASR)processes were carried out on 6 mm thick AZ31 magnesium alloy sheets that were produced by twin roll casting(TRC)technique.Before rolling processes,sheets were heat trea...Symmetric rolling(SR)and asymmetric rolling(ASR)processes were carried out on 6 mm thick AZ31 magnesium alloy sheets that were produced by twin roll casting(TRC)technique.Before rolling processes,sheets were heat treated in order to obtain a homogenized microstructure.In this study,for the ASR process the rolling speed ratio between upper roller and lower was selected as 1.25.Both SR and ASR processes were utilized with 40%reduction per passes using 2 pass schedule for a total reduction ratio of 0.67.Symmetric and asymmetric rolled sheets were characterized using optical microscopy(OM),scanning electron microscopy(SEM)and transmission electron microscopy(TEM)techniques.Texture measurements were performed by using X-ray diffraction(XRD)technique and mechanical properties were investigated by tensile tests and also hardness measurements.展开更多
文摘Symmetric rolling(SR)and asymmetric rolling(ASR)processes were carried out on 6 mm thick AZ31 magnesium alloy sheets that were produced by twin roll casting(TRC)technique.Before rolling processes,sheets were heat treated in order to obtain a homogenized microstructure.In this study,for the ASR process the rolling speed ratio between upper roller and lower was selected as 1.25.Both SR and ASR processes were utilized with 40%reduction per passes using 2 pass schedule for a total reduction ratio of 0.67.Symmetric and asymmetric rolled sheets were characterized using optical microscopy(OM),scanning electron microscopy(SEM)and transmission electron microscopy(TEM)techniques.Texture measurements were performed by using X-ray diffraction(XRD)technique and mechanical properties were investigated by tensile tests and also hardness measurements.