Poly（vinylidene fluoride）（PVDF）/multi-walled carbon nanotube（MWCNT） nanocomposites were prepared by means of ultrasonic dispersion method. X-ray diffraction（XRD） results indicate that incorporating MWCNTs into...Poly（vinylidene fluoride）（PVDF）/multi-walled carbon nanotube（MWCNT） nanocomposites were prepared by means of ultrasonic dispersion method. X-ray diffraction（XRD） results indicate that incorporating MWCNTs into PVDF caused the formation of β phase. A thermal annealing at 130 ℃ confirmed that the β phase was stable in the nanocomposites. Differential scanning calorimetry（DSC） results indicate that the melting temperature slightly increased while the heat of fusion markedly decreased with increasing MWCNT content. The tensile strength and modulus of PVDF were improved by loading the MWCNTs. The scanning electron microscopy（SEM） observations showed that MWCNTs were uniformly dispersed in the PVDF matrix and an interfacial adhesion between MWCNT and PVDF was achieved, which was responsible for the enhancement in the tensile strength and modulus of PVDE.展开更多
Polycrystalline diamond compacts (PDC) were synthesized using diamond powder of average crystal size 3-20 μm by the Ni 70 Mn 25 Co 5 alloy infiltration technique at high temperature and high pressure (HPHT).The surfa...Polycrystalline diamond compacts (PDC) were synthesized using diamond powder of average crystal size 3-20 μm by the Ni 70 Mn 25 Co 5 alloy infiltration technique at high temperature and high pressure (HPHT).The surface residual stress of polycrystalline diamond (PCD) layer was measured using micro-Raman spectroscopy with hydrostatic stress model and X-ray diffraction (XRD).Measurements of the stress levels of PCDs show that the residual compressive stresses range from 0.12 to 0.22 GPa,which increase with the crystal size of diamond.Scanning electron microscopy (SEM) was used to observe the morphology of initial diamond grains and PCD cross-section.The results indicate that PCD has a dense and interlaced microstructure with diamond-diamond (D-D) direct bonding.And the smaller the crystal size of diamond,the better the growth of diamond direct bonding and the smaller the binder metal between diamond boundaries will be.展开更多
基金Supported by the Research Fund for the Doctoral Program of Higher Education of China(No.20060183009)
文摘Poly（vinylidene fluoride）（PVDF）/multi-walled carbon nanotube（MWCNT） nanocomposites were prepared by means of ultrasonic dispersion method. X-ray diffraction（XRD） results indicate that incorporating MWCNTs into PVDF caused the formation of β phase. A thermal annealing at 130 ℃ confirmed that the β phase was stable in the nanocomposites. Differential scanning calorimetry（DSC） results indicate that the melting temperature slightly increased while the heat of fusion markedly decreased with increasing MWCNT content. The tensile strength and modulus of PVDF were improved by loading the MWCNTs. The scanning electron microscopy（SEM） observations showed that MWCNTs were uniformly dispersed in the PVDF matrix and an interfacial adhesion between MWCNT and PVDF was achieved, which was responsible for the enhancement in the tensile strength and modulus of PVDE.
基金supported by the National Natural Science Foundation of China (Grant Nos.50572032,50801030 and 50731006)
文摘Polycrystalline diamond compacts (PDC) were synthesized using diamond powder of average crystal size 3-20 μm by the Ni 70 Mn 25 Co 5 alloy infiltration technique at high temperature and high pressure (HPHT).The surface residual stress of polycrystalline diamond (PCD) layer was measured using micro-Raman spectroscopy with hydrostatic stress model and X-ray diffraction (XRD).Measurements of the stress levels of PCDs show that the residual compressive stresses range from 0.12 to 0.22 GPa,which increase with the crystal size of diamond.Scanning electron microscopy (SEM) was used to observe the morphology of initial diamond grains and PCD cross-section.The results indicate that PCD has a dense and interlaced microstructure with diamond-diamond (D-D) direct bonding.And the smaller the crystal size of diamond,the better the growth of diamond direct bonding and the smaller the binder metal between diamond boundaries will be.