Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wi...Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wire method and pouring method were compared. Conclusions have been drawn that, under these conditions in the experiments, the optimal feeding speed is 15m/min, treatment temperature should be as low as possible, 1400-1450℃ generally; and cored-wire method can act more effective in ductile iron melt desulphurization and spheroid than pouring method.展开更多
A martensitic microalloyed steel, 25Si2MnCrMo, was developed to meet the demands of the high-strength bars. Microstructure and mechanical properties of the steel were evaluated by using optical metallography, scanning...A martensitic microalloyed steel, 25Si2MnCrMo, was developed to meet the demands of the high-strength bars. Microstructure and mechanical properties of the steel were evaluated by using optical metallography, scanning electron microscopy, transmission electron microscopy, dilatometry and tensometry. Those measurements suggested that the steel consisted of martensite and retained austenite, which existed between the martensitic laths in a stable thin film, and that the steel showed very high tensile strength of 1400 MPa and good ductility of 15% in elongation after 300°C tempering.展开更多
基金the High Technology Research and Development Program of China(No.2002A4336072)
文摘Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wire method and pouring method were compared. Conclusions have been drawn that, under these conditions in the experiments, the optimal feeding speed is 15m/min, treatment temperature should be as low as possible, 1400-1450℃ generally; and cored-wire method can act more effective in ductile iron melt desulphurization and spheroid than pouring method.
文摘A martensitic microalloyed steel, 25Si2MnCrMo, was developed to meet the demands of the high-strength bars. Microstructure and mechanical properties of the steel were evaluated by using optical metallography, scanning electron microscopy, transmission electron microscopy, dilatometry and tensometry. Those measurements suggested that the steel consisted of martensite and retained austenite, which existed between the martensitic laths in a stable thin film, and that the steel showed very high tensile strength of 1400 MPa and good ductility of 15% in elongation after 300°C tempering.