Glass-ceramics obtained from the electric arc furnace molten slag of incinerator fly ash was produced by applying nucleation and crystallization through heat treatment process. The effects of nucleating agent(TiO2and ...Glass-ceramics obtained from the electric arc furnace molten slag of incinerator fly ash was produced by applying nucleation and crystallization through heat treatment process. The effects of nucleating agent(TiO2and Cr2O3)on the crystallization kinetics and heat treatment schedule of the slag were investigated. The results show that the nucleating agents changed the crystallization phase and morphology of the obtained glass-ceramics. The optimum heat treatment schedule of the glass with TiO2 was determined as nucleation at 952 K for 1.5 h and crystal growth at 1258 K for 1.5 h, while those values with Cr2O3 were estimated at 971 K for 2 h and at 1 238 K for 2 h. TiO2 acting as nucleating agent could decrease the activation energy of the slag and shorten the total thermal treatment time in comparison with Cr2O3. The glass-ceramics obtained under the optimum heat treatment condition was environmentfriendly and had remarkable physical/mechanical properties and chemical durability.展开更多
A new method was developed for effective enrichment of Cd2+ ions from water with a calcium alginate(CaAlg) hydrogel filtration membrane. First, the CaAlg hydrogel filtration membrane was prepared without a pore-formin...A new method was developed for effective enrichment of Cd2+ ions from water with a calcium alginate(CaAlg) hydrogel filtration membrane. First, the CaAlg hydrogel filtration membrane was prepared without a pore-forming agent. This membrane was used to remove Cd^(2+) via ion exchange with Ca^(2+), and the Cd^(2+) was preserved in the CaAlg hydrogel. Then, the CaAlg hydrogel containing Cd^(2+) was soaked in a sodium citrate solution, and the hydrogel was fully dissolved. The removal rate of the CaAlg filtration membrane reached almost 100% within 120 min when the Cd^(2+) concentration was under 1 mg/L. Factors affecting the removal rate were investigated, such as NaAlg concentration, operating pressure, operating time and the initial concentration of Cd^(2+). The effects of initial Cd^(2+) concentration, pressure and filtration time on the enrichment factor were also investigated. The results show that the enrichment factor reached 87.3 when the pressure was 0.18 MPa and the filtration time was 240 min. Different enrichment factors could be achieved by adjusting the operating pressure and filtration time.展开更多
基金Supported by the National Natural Science Foundation of China(No.51378332 and No.20806051)Science and Technology Project of Housing and Urban-Rural Ministry(No.2014-K4-014)Chinese Postdoctoral Science Foundation(No.2013M530872)
文摘Glass-ceramics obtained from the electric arc furnace molten slag of incinerator fly ash was produced by applying nucleation and crystallization through heat treatment process. The effects of nucleating agent(TiO2and Cr2O3)on the crystallization kinetics and heat treatment schedule of the slag were investigated. The results show that the nucleating agents changed the crystallization phase and morphology of the obtained glass-ceramics. The optimum heat treatment schedule of the glass with TiO2 was determined as nucleation at 952 K for 1.5 h and crystal growth at 1258 K for 1.5 h, while those values with Cr2O3 were estimated at 971 K for 2 h and at 1 238 K for 2 h. TiO2 acting as nucleating agent could decrease the activation energy of the slag and shorten the total thermal treatment time in comparison with Cr2O3. The glass-ceramics obtained under the optimum heat treatment condition was environmentfriendly and had remarkable physical/mechanical properties and chemical durability.
基金supported by the National Natural Science Foundation of China(Grant Nos.51678409,21504063&51708407)the Special Scientific Research Fund of Agricultural Public Welfare Profession of China(Grant No.21403014-1)+1 种基金the Tianjin Science Technology Research Funds of China(Grant Nos.16JCZDJC37500,15JCQNJC08900&17JCQNJC08700)the Tianjin Science and Technology Correspondent Project(Grant No.16JCTPJC44800)
文摘A new method was developed for effective enrichment of Cd2+ ions from water with a calcium alginate(CaAlg) hydrogel filtration membrane. First, the CaAlg hydrogel filtration membrane was prepared without a pore-forming agent. This membrane was used to remove Cd^(2+) via ion exchange with Ca^(2+), and the Cd^(2+) was preserved in the CaAlg hydrogel. Then, the CaAlg hydrogel containing Cd^(2+) was soaked in a sodium citrate solution, and the hydrogel was fully dissolved. The removal rate of the CaAlg filtration membrane reached almost 100% within 120 min when the Cd^(2+) concentration was under 1 mg/L. Factors affecting the removal rate were investigated, such as NaAlg concentration, operating pressure, operating time and the initial concentration of Cd^(2+). The effects of initial Cd^(2+) concentration, pressure and filtration time on the enrichment factor were also investigated. The results show that the enrichment factor reached 87.3 when the pressure was 0.18 MPa and the filtration time was 240 min. Different enrichment factors could be achieved by adjusting the operating pressure and filtration time.