The influence of different coating formulas and times on the water and oil resistance of paperboard was studied. The water and oil resistance of paperboard coated with a modified butadiene-styrene copolymer latex and ...The influence of different coating formulas and times on the water and oil resistance of paperboard was studied. The water and oil resistance of paperboard coated with a modified butadiene-styrene copolymer latex and fluorinated anion grease-proof agent was better than that coated with modified butadiene-styrene copolymer latex,where the modified butadiene-styrene copolymer latex was used as the pre-coating substrate and the F1516 fluorinated grease-proof agent was used as the top coating material. By coating modified butadiene-styrene copolymer latex with 30% solid content and F1516 fluorinated grease-proof agent with 24% solid content,the oil resistance of paperboard could reach anti-oil grade 12 and the water resistance could increased by98. 64%( compared with the base paperboard without any coating treatment).展开更多
The refining performances of mixed poplar and eucalyptwoodchips(mixture ratio 6:4)were investigated at medium and highpulp consistency via chemi-mechanical pulping(CMP).The specificrefining energy consumption(SEC),fib...The refining performances of mixed poplar and eucalyptwoodchips(mixture ratio 6:4)were investigated at medium and highpulp consistency via chemi-mechanical pulping(CMP).The specificrefining energy consumption(SEC),fiber fraction proportion,andCanadian standard freeness(CSF)were determined to evaluate the effectsof pulp consistency and NaOH dosage on the refining performancesof mixed poplar and eucalypt woodchips.While the dosage of NaOHfor impregnation was maintained constant,the SEC and shive contentincreased with increasing pulp consistency.Different fractions obtainedfrom the Bauer-McNett classifier showed that higher pulp consistencycould be expected to yield more long fibers and shive in the stock.Upon increasing the NaOH dosage,the shive content and SEC reducedsignificantly.When the NaOH dosage was increased to 6%,the resultsindicated that it was difficult to reduce the shive content to less than 1%athigh pulp consistencies(25%~35%),whereas 0.18%shive fraction couldbe achieved at a medium pulp consistency(15%).展开更多
文摘The influence of different coating formulas and times on the water and oil resistance of paperboard was studied. The water and oil resistance of paperboard coated with a modified butadiene-styrene copolymer latex and fluorinated anion grease-proof agent was better than that coated with modified butadiene-styrene copolymer latex,where the modified butadiene-styrene copolymer latex was used as the pre-coating substrate and the F1516 fluorinated grease-proof agent was used as the top coating material. By coating modified butadiene-styrene copolymer latex with 30% solid content and F1516 fluorinated grease-proof agent with 24% solid content,the oil resistance of paperboard could reach anti-oil grade 12 and the water resistance could increased by98. 64%( compared with the base paperboard without any coating treatment).
文摘The refining performances of mixed poplar and eucalyptwoodchips(mixture ratio 6:4)were investigated at medium and highpulp consistency via chemi-mechanical pulping(CMP).The specificrefining energy consumption(SEC),fiber fraction proportion,andCanadian standard freeness(CSF)were determined to evaluate the effectsof pulp consistency and NaOH dosage on the refining performancesof mixed poplar and eucalypt woodchips.While the dosage of NaOHfor impregnation was maintained constant,the SEC and shive contentincreased with increasing pulp consistency.Different fractions obtainedfrom the Bauer-McNett classifier showed that higher pulp consistencycould be expected to yield more long fibers and shive in the stock.Upon increasing the NaOH dosage,the shive content and SEC reducedsignificantly.When the NaOH dosage was increased to 6%,the resultsindicated that it was difficult to reduce the shive content to less than 1%athigh pulp consistencies(25%~35%),whereas 0.18%shive fraction couldbe achieved at a medium pulp consistency(15%).