The tempering microstructure and mechanical properties of X80 steel used for heating-bent pipe were analyzed. The results show that the microstructure of X80 steel tempered at 550 ℃ and 600 ℃ is bainitic ferrite (BF...The tempering microstructure and mechanical properties of X80 steel used for heating-bent pipe were analyzed. The results show that the microstructure of X80 steel tempered at 550 ℃ and 600 ℃ is bainitic ferrite (BF)+granular bainite (GB), and partial ferrite laths in BF merge and broaden. The interior sub-lath boundary of some GB begins to disappear due to merging, the M/A constituent (a mixture of martensite plus retained austenite) in GB is orbicular. At the two tempering temperatures the tested X80 steel shows a certain degree of tempering stability. After being tempered at 650 ℃, the microstructure of X80 steel is GB+quasi-polygonal ferrite(QF), and the original BF laths have merged to form smaller GB crystal grains. The reason is that the steel shows better match of strength and toughness. After being tempered at 700 ℃ , the microstructure of X80 steel is composed mainly of QF, which can improve the plasticity but decline severely the yield strength of X80, and the M/A constituent assembles and grows up at the grain boundary of QF, resulting in excellent lower low-temperature toughness of X80.展开更多
Based on an analysis of the existing models of CO 2 corrosion in literatures and the autoclave simulative experiments, a predictive model of corrosion rate (r corr) in CO 2/H 2S corrosion for oil tubes has been ...Based on an analysis of the existing models of CO 2 corrosion in literatures and the autoclave simulative experiments, a predictive model of corrosion rate (r corr) in CO 2/H 2S corrosion for oil tubes has been established, in which r corr is expressed as a function of pH, temperature (T), pressure of CO 2 (P CO 2) and pressure of H 2S (P H 2S). The model has been verified by experimental data obtained on N80 steel. The improved features of the predictive model include the following aspects: (1) The influence of temperature on the protectiveness of corrosion film is taken into consideration for establishment of predictive model of the r corr in CO 2/H 2S corrosion. The Equations of scale temperature and scale factor are put forward, and they fit the experimental result very well. (2) The linear relationship still exists between ln r corr and ln P CO 2 in CO 2/H 2S corrosion (as same as that in CO 2 corrosion). Therefore, a correction factor as a function of P H 2S has been introduced into the predictive model in CO 2/H 2S corrosion. (3) The model is compatible with the main existing models.展开更多
The local induction heating process and the whole induction heating process were adopted to develop the X80 Ф1219 mm × 22 mm induction bends in this paper. After the tempering of the bends, the effect of inducti...The local induction heating process and the whole induction heating process were adopted to develop the X80 Ф1219 mm × 22 mm induction bends in this paper. After the tempering of the bends, the effect of induction heating on the properties of X80 longitudinal submerged-arc welding line pipe was studied. The results show that for the X80 bend manufactured via the local induction heating, both the tensile strength and yield ratio of unquenehed straight tangents are higher than those of the quenched bend area. The toughness of straight tangents is lower than that of the bend area. The strength and toughness of straight tangents do not match pegrectly that of the bend area. The induction heating can improve effectively the toughness of weld pipe, reduce the tensile strength and yield ratio to some extent. The whole induction heating makes the match of properties between the straight tangents and the bend area reasonable, thus it is an optimum process for the manufacturing of X80 induction bend.展开更多
Prospect of engineering technologies for pipelines in ChinaIn recent years,China National Petroleum Corporation (CNPC) has made remarkable achievements in the field of oil and gas transmission pipeline engineering.
基金Project(6990-HT-XEX-03-(2008)-0137) supported by the Major Special Project of Science and Technology of China National Petroleum Corporation
文摘The tempering microstructure and mechanical properties of X80 steel used for heating-bent pipe were analyzed. The results show that the microstructure of X80 steel tempered at 550 ℃ and 600 ℃ is bainitic ferrite (BF)+granular bainite (GB), and partial ferrite laths in BF merge and broaden. The interior sub-lath boundary of some GB begins to disappear due to merging, the M/A constituent (a mixture of martensite plus retained austenite) in GB is orbicular. At the two tempering temperatures the tested X80 steel shows a certain degree of tempering stability. After being tempered at 650 ℃, the microstructure of X80 steel is GB+quasi-polygonal ferrite(QF), and the original BF laths have merged to form smaller GB crystal grains. The reason is that the steel shows better match of strength and toughness. After being tempered at 700 ℃ , the microstructure of X80 steel is composed mainly of QF, which can improve the plasticity but decline severely the yield strength of X80, and the M/A constituent assembles and grows up at the grain boundary of QF, resulting in excellent lower low-temperature toughness of X80.
基金TheResearchProjectofTubularGoodsRe searchCenterofChinaNationalPetroleumCorporation (No .2 3 5 2 4)andtheResearchProjectofHenanUniversityofScienceandTechnology (No .2 0 0 10 1)
文摘Based on an analysis of the existing models of CO 2 corrosion in literatures and the autoclave simulative experiments, a predictive model of corrosion rate (r corr) in CO 2/H 2S corrosion for oil tubes has been established, in which r corr is expressed as a function of pH, temperature (T), pressure of CO 2 (P CO 2) and pressure of H 2S (P H 2S). The model has been verified by experimental data obtained on N80 steel. The improved features of the predictive model include the following aspects: (1) The influence of temperature on the protectiveness of corrosion film is taken into consideration for establishment of predictive model of the r corr in CO 2/H 2S corrosion. The Equations of scale temperature and scale factor are put forward, and they fit the experimental result very well. (2) The linear relationship still exists between ln r corr and ln P CO 2 in CO 2/H 2S corrosion (as same as that in CO 2 corrosion). Therefore, a correction factor as a function of P H 2S has been introduced into the predictive model in CO 2/H 2S corrosion. (3) The model is compatible with the main existing models.
文摘The local induction heating process and the whole induction heating process were adopted to develop the X80 Ф1219 mm × 22 mm induction bends in this paper. After the tempering of the bends, the effect of induction heating on the properties of X80 longitudinal submerged-arc welding line pipe was studied. The results show that for the X80 bend manufactured via the local induction heating, both the tensile strength and yield ratio of unquenehed straight tangents are higher than those of the quenched bend area. The toughness of straight tangents is lower than that of the bend area. The strength and toughness of straight tangents do not match pegrectly that of the bend area. The induction heating can improve effectively the toughness of weld pipe, reduce the tensile strength and yield ratio to some extent. The whole induction heating makes the match of properties between the straight tangents and the bend area reasonable, thus it is an optimum process for the manufacturing of X80 induction bend.
文摘Prospect of engineering technologies for pipelines in ChinaIn recent years,China National Petroleum Corporation (CNPC) has made remarkable achievements in the field of oil and gas transmission pipeline engineering.
文摘Technology progress of oil & gas pipelines transportation project of CNPC since the 11th Five-Year Plan period An introduction to oil & gas pipelines