The composite that can absorb the high-performance electromagnetic（EM） wave is constructed into a sandwiched structure composed of carbon black（CB）/ethylene-vinyl acetate（EVA） and Ag naowires（Ag NWs）. The Ag N...The composite that can absorb the high-performance electromagnetic（EM） wave is constructed into a sandwiched structure composed of carbon black（CB）/ethylene-vinyl acetate（EVA） and Ag naowires（Ag NWs）. The Ag NWs sandwiched between two CB/EVA layers are used to improve the absorption properties of composite. The effects of EVA-to-CB weight ratio, concentration and diameter of Ag NWs with a thickness of 0.4 mm on microwave absorption are investigated.The results indicate that for an EVA-to-CB weight ratio of 1：3, Ag NW concentration of 1.0 mg/100 m L, and average diameter of 56 nm, the reflection loss（RL） of the composite is below-10 d B in a frequency range of 9.3 Ghz–18.0 GHz, with the minimum values of-40.0 d B and-25.6 d B at 13.5 GHz and 15.3 GHz, respectively. A finite element method（FEM）is used for calculating the RL of the composite. The calculated results are in agreement with the experimental data.展开更多
基金Project partly supported by the National Natural Science Foundation of China(Grant No.61275174)
文摘The composite that can absorb the high-performance electromagnetic（EM） wave is constructed into a sandwiched structure composed of carbon black（CB）/ethylene-vinyl acetate（EVA） and Ag naowires（Ag NWs）. The Ag NWs sandwiched between two CB/EVA layers are used to improve the absorption properties of composite. The effects of EVA-to-CB weight ratio, concentration and diameter of Ag NWs with a thickness of 0.4 mm on microwave absorption are investigated.The results indicate that for an EVA-to-CB weight ratio of 1：3, Ag NW concentration of 1.0 mg/100 m L, and average diameter of 56 nm, the reflection loss（RL） of the composite is below-10 d B in a frequency range of 9.3 Ghz–18.0 GHz, with the minimum values of-40.0 d B and-25.6 d B at 13.5 GHz and 15.3 GHz, respectively. A finite element method（FEM）is used for calculating the RL of the composite. The calculated results are in agreement with the experimental data.