Based on the strength and microstructure tests,the effects of the hydantoin epoxy resin content and curing time on the mechanical properties and microstructure of copper tailings specimens were studied.The results sho...Based on the strength and microstructure tests,the effects of the hydantoin epoxy resin content and curing time on the mechanical properties and microstructure of copper tailings specimens were studied.The results showed that the strength of the solidified specimens was increased to 20.84 MPa with 30 wt.%addition of hydantoin epoxy resin.When the specimens with 10%hydantoin epoxy resin were cured for 7 and 14 d,the strengths were 6.33 and 6.67 MPa respectively,which met the requirements as foundation filler and building materials.The microscopic tests showed that the agglomeration was enhanced and the porosities of the solidified specimens were reduced with increase in the hydantoin epoxy resin content,which could greatly enhance the strength of solidified specimens.展开更多
基金financial support from the National Natural Science Foundation of China (Nos. 41972282, 41807253)the Natural Science Foundation of Hunan Province, China (No. 2021JJ30804)the Research Fund Program from Yunnan Diqing Nonferrous Metal Co., Ltd., China (No. DQYS-ZYB-09-(2021)001)
文摘Based on the strength and microstructure tests,the effects of the hydantoin epoxy resin content and curing time on the mechanical properties and microstructure of copper tailings specimens were studied.The results showed that the strength of the solidified specimens was increased to 20.84 MPa with 30 wt.%addition of hydantoin epoxy resin.When the specimens with 10%hydantoin epoxy resin were cured for 7 and 14 d,the strengths were 6.33 and 6.67 MPa respectively,which met the requirements as foundation filler and building materials.The microscopic tests showed that the agglomeration was enhanced and the porosities of the solidified specimens were reduced with increase in the hydantoin epoxy resin content,which could greatly enhance the strength of solidified specimens.