Polybutylacrylate (PBA)/poly(methyl methacrylate) (PMMA) core-shell elastic particles (CSEP), whose rubbery core diameter ranged from 0.08 μm to 1.38μm, were synthesized by using conventional emulsion polymerization...Polybutylacrylate (PBA)/poly(methyl methacrylate) (PMMA) core-shell elastic particles (CSEP), whose rubbery core diameter ranged from 0.08 μm to 1.38μm, were synthesized by using conventional emulsion polymerization, multi-step emulsion polymerization, and soapless polymerization. Allyl methacylate (ALMA) and ethylene glycol dimethacrylate (EGDMA) were selected as crosslinking reagents for core polymerization. Methacrylic acid (MAA) was used as functional co-monomer with methyl methacrylate as shell component. The content of vinyl groups in PBA rubbery core increased with the amount of crosslinking reagents. The core-shell ratio affected great on the morphology of the complex particles. Furthermore, the amounts of carboxyl on the surface of core-shell particles, copolymerized with acrylic acid, were determined by potentiometric titration. Results showed that methylacrylic acid was distributed mostly on the surface of particles.展开更多
文摘Polybutylacrylate (PBA)/poly(methyl methacrylate) (PMMA) core-shell elastic particles (CSEP), whose rubbery core diameter ranged from 0.08 μm to 1.38μm, were synthesized by using conventional emulsion polymerization, multi-step emulsion polymerization, and soapless polymerization. Allyl methacylate (ALMA) and ethylene glycol dimethacrylate (EGDMA) were selected as crosslinking reagents for core polymerization. Methacrylic acid (MAA) was used as functional co-monomer with methyl methacrylate as shell component. The content of vinyl groups in PBA rubbery core increased with the amount of crosslinking reagents. The core-shell ratio affected great on the morphology of the complex particles. Furthermore, the amounts of carboxyl on the surface of core-shell particles, copolymerized with acrylic acid, were determined by potentiometric titration. Results showed that methylacrylic acid was distributed mostly on the surface of particles.