The effects of gradient structure on the microstructure and properties of coated cemented carbides were researched with optical microscopy （OM）, scanning electron microscopy （SEM）, strength measurements, and cutti...The effects of gradient structure on the microstructure and properties of coated cemented carbides were researched with optical microscopy （OM）, scanning electron microscopy （SEM）, strength measurements, and cutting tests. It shows that vacuum sintering of WC-Ti（C, N）-TaC-Co cemented carbides results in the formation of a surface ductile zone. The ductile zone prevents crack propagation and leads to the increase of transverse rupture strength of the substrate. The impact resistance of coated gradient inserts was obviously improved on the basis of maintaining resistance to abrasion and the forming mechanism of the gradient structure was also analyzed.展开更多
Ti-X-N (X=Al,Si or Al+Si) coatings were grown onto cemented carbide substrates by cathodic arc evaporation. The hardness of the coatings was obtained by nanoindentation and the microstructure was investigated by XRD,X...Ti-X-N (X=Al,Si or Al+Si) coatings were grown onto cemented carbide substrates by cathodic arc evaporation. The hardness of the coatings was obtained by nanoindentation and the microstructure was investigated by XRD,XPS and SEM. Solid solution hardening results in a hardness increase from 24 GPa for TiN to 31.2 GPa for TiAlN. The higher hardness values of 36.7 GPa for TiSiN and 42.4 GPa for TiAlSiN are obtained by the incorporation of Si into TiN (TiAlN) coatings due to the formation of special three-dimensional net structure consisting of nanocrystalline (nc) TiN (TiAlN) encapsulated in an amorphous (a) Si3N4 matrix phase. Furthermore,the nc-TiAlN/a-Si3N4 coating shows the best machining performance.展开更多
Magnetron sputtered (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings grown on cemented carbide substrates were studied by using energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy(SEM), n...Magnetron sputtered (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings grown on cemented carbide substrates were studied by using energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy(SEM), nanoindentation, Rockwell A indentation test, strength measurements and cutting tests. The results show that the (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings perform good affinity to substrate, and the TiN/(Ti, Al)N multilayer coating exhibits higher hardness, higher toughness and better cutting performance compared with the (Ti, Al)N monolayer coating. Moreover, the strength measurement indicates that the physical vapour deposition (PVD) coating has no effect on the substrate strength.展开更多
This paper studies the influence of radial depth on vibration, chip formation and surface roughness during face milling of AISI304 austenitic stainless steel with indexable cemented carbide milling cutters. The amplit...This paper studies the influence of radial depth on vibration, chip formation and surface roughness during face milling of AISI304 austenitic stainless steel with indexable cemented carbide milling cutters. The amplitude of vibration acceleration increased with the increasing radial depth up to 80 mm. And the domain vibration frequency varied with the radial depth. In this paper, three types of chips were found: C shape, long shape and spiral shape. The minimum surface roughness value occurred when the radial depth equalled 40 mm in the experiment. Irregular changes of chip curl radius and chip thickness could be attributed to different numbers of alternately engaged teeth when the feed and speed were fixed. Surface roughness is related to forced vibration and chip formation. Radial depth with different numbers of alternately engaged teeth could significantly influence the forced vibration, chip formation, and surface roughness.展开更多
文摘The effects of gradient structure on the microstructure and properties of coated cemented carbides were researched with optical microscopy （OM）, scanning electron microscopy （SEM）, strength measurements, and cutting tests. It shows that vacuum sintering of WC-Ti（C, N）-TaC-Co cemented carbides results in the formation of a surface ductile zone. The ductile zone prevents crack propagation and leads to the increase of transverse rupture strength of the substrate. The impact resistance of coated gradient inserts was obviously improved on the basis of maintaining resistance to abrasion and the forming mechanism of the gradient structure was also analyzed.
基金Project(50721003) supported by Creative Research Group of National Natural Science Foundation of ChinaProject(2009ZX04012-021) supported by the National Major Special Science and Technology Program of China
文摘Ti-X-N (X=Al,Si or Al+Si) coatings were grown onto cemented carbide substrates by cathodic arc evaporation. The hardness of the coatings was obtained by nanoindentation and the microstructure was investigated by XRD,XPS and SEM. Solid solution hardening results in a hardness increase from 24 GPa for TiN to 31.2 GPa for TiAlN. The higher hardness values of 36.7 GPa for TiSiN and 42.4 GPa for TiAlSiN are obtained by the incorporation of Si into TiN (TiAlN) coatings due to the formation of special three-dimensional net structure consisting of nanocrystalline (nc) TiN (TiAlN) encapsulated in an amorphous (a) Si3N4 matrix phase. Furthermore,the nc-TiAlN/a-Si3N4 coating shows the best machining performance.
文摘Magnetron sputtered (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings grown on cemented carbide substrates were studied by using energy dispersive X-ray spectroscopy (EDX), scanning electron microscopy(SEM), nanoindentation, Rockwell A indentation test, strength measurements and cutting tests. The results show that the (Ti, Al)N monolayer and TiN/(Ti, Al)N multilayer coatings perform good affinity to substrate, and the TiN/(Ti, Al)N multilayer coating exhibits higher hardness, higher toughness and better cutting performance compared with the (Ti, Al)N monolayer coating. Moreover, the strength measurement indicates that the physical vapour deposition (PVD) coating has no effect on the substrate strength.
基金Project(2014ZX04012011)supported by Major National Science and Technology Projects,ChinaProject(51327902)supported by the National Natural Science Foundation of China
基金Supported by National Science and Technology Major Project of China(No.2009ZX04012-021)Major State Basic Research Development Program of China ("973" Program, No.2009CB724306)
文摘This paper studies the influence of radial depth on vibration, chip formation and surface roughness during face milling of AISI304 austenitic stainless steel with indexable cemented carbide milling cutters. The amplitude of vibration acceleration increased with the increasing radial depth up to 80 mm. And the domain vibration frequency varied with the radial depth. In this paper, three types of chips were found: C shape, long shape and spiral shape. The minimum surface roughness value occurred when the radial depth equalled 40 mm in the experiment. Irregular changes of chip curl radius and chip thickness could be attributed to different numbers of alternately engaged teeth when the feed and speed were fixed. Surface roughness is related to forced vibration and chip formation. Radial depth with different numbers of alternately engaged teeth could significantly influence the forced vibration, chip formation, and surface roughness.